Photonic Crystal Fiber Interferometers (PCFIs) are widely used for sensing applications. This work presents the fabrication and the characterization of a relative humidity sensor based on a polymer-coated photonic crystal fiber that operates in a Mach- Zehnder Interferometer (MZI) transmission mode. The fabrication of the sensor involved splicing a short (1 cm) length of Photonic Crystal Fiber (PCF) between two single-mode fibers (SMF). It was then coated with a layer of agarose solution. Experimental results showed that a high humidity sensitivity of 29.37 pm/%RH was achieved within a measurement range of 27–95%RH. The sensor also showed good repeatability, small size, measurement accuracy and wide humidity range. The RH sensitivity o

   The modified Hummers method was applied to prepare graphene oxide (GO) from the graphite powder. Tin oxide nanoparticles with different loading (10-20 wt.%) supported on reduced graphene oxide were synthesized to evaluate the oxidative desulfurization efficiency. The catalyst was synthesized by the incipient wetness impregnation (IWI) technique. Different analysis methods like FT-IR, XRD, FESEM, AFM, and Brunauer-Emmett-Teller (BET) were utilized to characterize graphene oxide and catalysts. The XRD analysis showed that the average crystal size of graphene oxide was 6.05 nm. In addition, the FESEM results showed high metal oxide dispersions on the rGO. The EDX analysis shows the weight ratio of Sn is close to its theoretical weight.

Graphite coated electrodes (GCE) based on molecularly imprinted polymers were fabricated for the selective potentiometric determination of Glibenclamide (Glb). The molecularly imprinted (MIP) and nonimprinted (NIP) polymers were synthesized by radical bulk polymerization using (Glb.) as a template, acrylic acid (AA) and acrylamide (AAm) as monomers, ethylene glycol dimethacrylate (EGDMA) as a cross-linker and benzoyl peroxide (BPO) as an initiator. The imprinted membranes and the non-imprinted membranes were prepared using dioctyl phthalate (DOP) and Dibutylphthalate (DBP) as plasticizers in PVC matrix. The membranes were coated on graphite electrodes. The MIP electrodes using (AA) and (AAm) showed a near nernstian response with slopes o

The current research aims to find out the extent to which students of the Faculty of Education for Pure Sciences\/Ibn al-Haitham have owned laboratory academic skills, the researcher adopted a descriptive research approach to conform to the goal of the research, the research sample the consisted of 140 students from the Department of Chemistry Phase II, The research tool, which consisted of a measure of laboratory academic skills, which consisted of seven skills and consisted of 28 paragraphs (four paragraphs per field), was prepared and the pent-up scale was chosen because the selected sample were university students, and the results showed the ownership of students' skills of laboratory academic skills other than skill The use of the libr

This paper investigated the fatigue life behavior of two composite materials subjected to different times of shot peening (2, 4 and 6 min).The first material prepared from unsaturated polyester with E-glass reinforcement by 33% volume fraction. While, the second one was prepared from unsaturated polyester with aluminum powder by2.5% volume fraction. The experimental results showed that the improvement in endurance limit was obtained (for the first material) at 2, 4 and 6 min shot peening times where the percentage of maximum improvement was 25% at shot peening time of 6 min. While, the endurance limit of the second material decreased at shot peening times of 2, 4 and 6 min where the percentage of maximum reduction was 29 % at shot peenin

 Glay pots experiments were carried out in the botanical garden of Biology Department/  College of Education for Pure Science Ibn AL-Haitham / Baghdad University for the growing season 2014-2015 , to evaluate the effect of foliar spraying of hydrogen peroxide ( H2O2) and glutamic acid and their interaction on some growth parameters and yield components of black cumin plant . The experiment included the following factors :- 1- Four concentrations of hydrogen peroxide (0 , 5 , 10 , 20 ) mM.L-1 . 2- Three concentrations of glutamic acid ( 0 , 50 , 100 ) mg.L-1 .      The experiment was designed according to completely randomized design (CRD) with three replications ,        Results revealed that

The complexity and partially defined nature of jet grouting make it hard to predict the performance of grouted piles. So the trials of cement injection at a location with similar soil properties as the erecting site are necessary to assess the performance of the grouted piles. Nevertheless, instead of executing trial-injected piles at the pilot site, which wastes money, time, and effort, the laboratory cement injection devices are essential alternatives for evaluating soil injection ability. This study assesses the performance of a low-pressure laboratory grouting device by improving loose sandy soil injected using binders formed of Silica Fume (SF) as a chemical admixture (10% of Ordinary Portland Cement OPC mass) to di