In this work, varying compositions of SiO₂ micro filler were added
with the Polyvinyl Chloride (PVC) and samples have been prepared
using film casting technique. The results have been analyzed and
compared for PVC samples with (1 wt%, 3 wt%, 5 wt% and 10 wt%)
SiO2 micro filler. Mechanical characteristics such as tensile strength,
elongation at break and Young`s modulus were measured for all the
samples, where the tensile strength was increased from 8.39 Mpa for
purified PVC to 16 Mpa for 3% SiO₂/PVC composite. Also, thermal
conductivity measurement values illustrated that composite materials
have a good thermal insulation at 10 wt. %, thermal conductivity was
decreased from 0.1684 W/m.

In a world of limited space, the owners are always surrounded by others next to them, and, consequently, there is hardly any activity which the owner may exercise on his land which would not affect the other owners. If he builds a building, that building may block the sun's rays or the air from the buildings next to it and owned by other people. And if he runs a business, the lands adjacent to that business may be overburdened with the accompanying noise or traffic. If oil is prospected in a land, the neighboring lands may be deprived of oil or their owners may be exposed to toxic fumes. Hence the importance of researching the intention of harming others, as it is one of the most important forms of abuse in the use of the right (especially

In this research, the X-ray diffraction pattern was used, which was obtained experimentally after preparation of barium oxide powder. A program was used to analyze the X-ray diffraction lines of barium oxide nanoparticles, and then the particle size was calculated by using the Williamson-Hall method, where it was found that the value of the particle size is 25.356 nm. Also, the dislocation density was calculated, which is equal to1.555 x1015 (lines/nm2), and the value of the unit cell number was also calculated, as it is equal to 23831.

This research sheds light on those discrepancies in the use of ornaments, adornment and perfumes, as well as the art of cosmetics, in two important civilizations, namely, the Mesopotamian civilization as the earlier civilization, and the civilization of Yemen, which represents the first Arab civilization. Through the foregoing, our research includes two topics, the first topic included the history of the use of decorations, ornaments and perfumes in the civilization of Mesopotamia, while the second topic included the study of ornaments, adornment and cosmetic art in the ancient civilization of Yemen. And then the research came out with a number of conclusions that the researcher considers very important to highlight the differences and f

Intellectual and material displacement is one of the design strategies through many mechanisms and means, and depends on the idea of changing the shape within the internal spaces at times and has concepts related to the transformation at other times. And represented by the boxes for travelers, the research problem emerged through the following question: (What is the effectiveness of displacement in the formal structures in the interior design of historical sites), and the aim of the study is to reveal the reality of the use of historical internal spaces and to determine the formal displacement that occurs as a result of change and transformation, and it included two topics, the first topic Transformation and the effectiveness of formal d

This work deals with preparation of zeolite 5A from Dewekhala kaolin clay in Al-Anbar region for drying and desulphurization of liquefied petroleum gas. The preparation of zeolite 5A includes treating kaolin clay with dilute hydrochloric acid 1N, treating metakaolin with NaOH solution to prepare 4A zeolite, ion exchange, and formation. For preparation of zeolite 4A, metakaolin treated at different temperatures (40, 60, 80, 90, and 100 °C) with different concentrations of sodium hydroxide solution (1, 2, 3, and 4 N) for 2 hours. The zeolite samples give the best relative crystallinity of zeolite prepared at 80 °C with NaOH concentration 3N (199%), and at 90 and 100°C with NaOH concentration solution 2N (184% and 189%, respectively). Ze

            In this study, pure SnO₂ Nanoparticles doped with Cu were synthesized by a chemical precipitation method. Using SnCl₂.2H₂O, CuCl₂.2H₂O as raw materials, the materials were annealed at 550°C for 3 hours in order to improve crystallization. The XRD results showed that the samples crystallized in the tetragonal rutile type SnO₂ stage. As the average SnO₂ crystal size is pure 9nm and varies with the change of Cu doping (0.5%, 1%, 1.5%, 2%, 2.5%, 3%),( 8.35, 8.36, 8.67, 9 ,7, 8.86)nm respectively an increase in crystal size to 2.5% decreases at this rate and that the crystal of SnO₂ does not change with the introduction of Cu, and S

KE Sharquie, JR Al-Rawi, AA Noaimi, MM Jabir, Iraqi Postgraduate Medical Journal, 2009