Iraqi bentonite is used as main material for preparing ceramic samples with the additions of alumina and magnesia. X-ray diffractions analyses were carried out for the raw material at room temperature. The sequence of mineral phase's transformations of the bentonite for temperatures 1000 ,1100 ,1200 and 1250 ºC reflects that it finally transformed in to mullite 39.18% and cristobalite 62.82%. Samples of different weight constituent were prepared. The effect of its constitutional change reveals through its heat treatments at 1000,1100,1200,1250and 1300ºC .The samples of additions less than 15% of alumina and magnesia could not stand up to 1300ºC while the samples of addition more than 15% are stable .That is shown by analy

Three hundred and fifty five patients with hepatitis were investigated in this study all cases gave negative result with HBs Ag , IgM-anti HCV , IgM-anti HEV, IgM-anti HDV and anti-HIV tests . The frequency of IgM-anti HAV was 113 and the percentage was 32 % in all ages but when these patients divided into five groups dependent on ages. The highest percentage of IgM-anti HAV was (45%) in age <10 and the percentage declined with age increase till to 9% in age >41 year.

The research was performed in order to investigate the prevalence of Eimeria spp in buffalo. Coccidiosis, is a common livestock disease include water buffaloes and nothing is known about the most pathogenic species of Eimeria. Since the highest prevalence of oocyst shedding and incidence of disease occurs in buffalo calves less than one year of age. The omnipresent occurrence and negative effects of the infection on health and buffalo growth output are taken into account. Therefore, both farmers and veterinarians should pay greater attention to infections with Eimeria spp. And there is little analysis of data reported in Iraq and the world regarding Eimeria infection in river buffalo spp.

Visceral leishmaniasis is a neglected tropical disease on the rise in different regions of Iraq, especially in areas with poor hygiene and among refugee populations. The effectiveness of existing chemotherapy for leishmaniasis is constrained by its high toxicity, cost, and the development of drug resistance. The current research examined various concentrations (ranging from 125 to 1000 μM) of lupeol to evaluate its ability to boost the generation of nitric oxide, which has anti-leishmanial properties, in an ex-vivo macrophage model. Griess assay was used to detect the nitric oxide (NO) production in Leishmania donovani infected U937 cell-line macrophages along 24 and 48 hours post treated. The nitric oxide concentration was signifi

Particulate matter (PM) emitted from diesel engine exhaust have been measured in terms of mass, using
99.98 % pure ethanol blended directly, without additives, with conventional diesel fuel (gas – oil),to
get 10 % , 15 %, 20 % ethanol emulsions . The resulting PM collected has been compared with those
from straight diesel. The engine used is a stationary single cylinder, variable compression ratio Ricardo
E6/US. This engine is fully instrumented and could run as a compression or spark ignition.
Observations showed that particulate matter (PM) emissions decrease with increasing oxygenate
content in the fuel, with some increase of fuel consumption, which is due to the lower heating value of
ethanol. The reduction in

NiO nanoparticle synthesis by chemical method and characterized by XRD with crystal size 11.72
nm and grain size 13 nm from FESEM image also NiO micro used ,two NiO as an additive to evaluate the
possibility of producing photodegradable polymers, the practical application of solid-phase photocatalytic
degradation of polyvinyl chloride (PVC- NiO composite films) was investigated. PVC has a negative impact
on the environment since its polymer degrades slowly, yet it has a wide range of industrial applications and
the amount used shows no evidence of diminishing use. Thus, a synthesis of modified PVC- NiO micro and
nano has been studied with 0, 50, 100, 150, 200, 250, and 300 (hours) as irradiation time a

This research investigates the pre- and post-cracking resistance of steel fiber-reinforced concrete specimens with Glass Fiber Reinforced Polymer (GFRP) bars subjected to flexural loading. The purpose is to modify the ductility and cracking resistance of GFRP-reinforced beams, which are prone to early cracking and excessive deflections instigated by the low modulus of elasticity of GFRP. Six self-compacting concrete specimens (1500×240×200 mm), incorporating steel fibers of two lengths (25 mm and 40 mm) with varying distribution depths, were tested to assess their structural performance. The results indicate significant enhancements in cracking resistance, stiffness, energy absorption, ductility, and flexural strength. Tested beam