Chitosan (CH) / Poly (1-vinylpyrrolidone-co-vinyl acetate) (PVP-co-VAc) blend (1:1) and nanocomposites reinforced with CaCO3 nanoparticles were prepared by solution casting method. FTIR analysis, tensile strength, Elongation, Young modulus, Thermal conductivity, water absorption and Antibacterial properties were studied for blend and nanocomposites. The tensile results show that the tensile strength and Young’s modulus of the nanocomposites were enhanced compared with polymer blend [CH/(PVP-co-VAc)] film. The mechanical properties of the polymer blend were improved by the addition of CaCO3 with significant increases in Young’s modulus (from 1787 MPa to ~7238 MPa) and tensile strength (from 47.87 MPa to 79.75 MPa). Strong interfacial

The dielectric constant of most polymers is very low; the addition of TiO2 particles into the polymers provides an attractive and promising way to reach a high dielectric constant. Polymer-based materials with a high dielectric constant show great potential for energy storage applications. Four samples were prepared, one of them was polyurethane (PU) and the other were PU with different weight percent (wt %) of TiO2 (0.1, 0.2, 0.3) powder AFM test was used to distinguish the nanoparticles. The result shows that the most shape of these nanoparticles are spherical and the roughness average is 0.798 nm. The dielectric properties were measured for all samples before and after the exposure to the UV radiation. The result illustrates that the

This study is concerned with the effect of Deep Cryogenic Treatment (DCT) at liquid nitrogen temperature (-196 o C) on the mechanical properties and performance of low carbon steel (A858). The tests specimens were divided in to two groups, the first group was subjected to the conventional heat treatment of normalizing, and the second group was also normalized then subjected to (DCT). The results have shown that after (DCT), the Hardness, Tensile properties and the impact energy absorbed were all slightly increased. However the fatigue test showed some positive improvement in fatigue limit by 20(N/mm2 ), and the volume wear rates at different loads were significantly decreased after (DCT). The changes in microstructure due to (DCT) were c

Sheets of Epoxy (EP) resin with addition of TiO2 of grain size (1.5μm, and 50nm) and weight percentage (1%, 3%, and 5%) were prepared. Discs of 20mm diameter and 3mm thickness were cut for dielectric measurements. Dielectric properties (dielectric constant, dispassion factor and electrical conductivity) over the frequency range 102 -106 Hz were measured.
Comparison was made between the effect of micro and nano particles of TiO2 on the dielectric properties of EP composites with different weight percentage. Epoxy composites with micro sized particles of TiO2 were observed to have the better values of dielectric properties.

In this work, the optical properties of Cu₂S with different thickness
(1400, 2400, 4400) Ǻ have been prepared by chemical spray pyrolys
is method onto clean glass substrate heated at 283 ^oC ±2. The effect
of thickness on the optical properties of Cu2S has been studied. It
was found that the optical properties of the electronic transitions on
fundamental absorption edge were direct allowed and the value of the
optical energy gap of Cu₂S (Eg) for direct transition decreased from
(2.4-2.1) eV with increasing of the thickness from (1400 - 4400)Ǻ
respectively. Also it was found that the absorption coefficient is
increased with increasing of thicknesses. The optical constants such<

Nanoparticles are a special group of materials with unique features and extensive applications in diverse fields. The use of nanoparticles of some metals is a viable solution to stop infectious diseases due to the antimicrobial properties of these nanoparticles. The present work demonstrates the effect of silver nanoparticles (AgNPs) on the antibacterial activity of four different antibiotics (amoxicillin, ceftriaxone, chloramphenicol, and penicillin) against eleven Gram-positive and Gram-negative isolates. Disk diffusion method was used to determine the antibacterial activity of various classes of antibiotics in the absence and presence of sub-inhibitory silver nanoparticles of concentration (80 microgram/ml). A synergistic effect was o

Films of silver oxide of different thickness have been prepared by the chemical spray paralysis. Transmission and absorption spectra have recorded in order to study the effect of increasing thickness on some optical parameter such as reflectance, refractive index , and dielectric constant in its two parts . This study reveals that all these paramters affect by increasing the thickness .

Forty eight isolates (41.02%) were obtained from 117 wound and burn samples. The isolates that showed high resistance for both antibiotic was two only that represent 4,1% from all isolates. The result of PCR product electrophoresis was referred that the gene is VIM gene. Lactose and raffinose showed double increasing in diameter of inhibition zone of imipenem with 1% that mean showed highest susceptibility that decreased with the concentration increasing, the same result were with meropenem. But no effect were detected on meropenem inhibition zone diameter. Mannose have no effect on the resistance in 1%, 3% and 7%. Results showed that only three case that increase the expression of gene, they were lactose at 1% concentration that increased

The performance of photovoltaic (PV) panel having staggered metal foam fins was examined experimentally in Baghdad, Iraq. Three staggered metal foam fin configurations attached to the backside of the PV panel were studied. The measured parameters were front and back surfaces temperature, open voltage and current circuits, maximum power, and PV efficiency. It was noted that the maximum electrical efficiency enhancement was 4.7% for staggered metal foam fins (case III) than the reference PV panel. The operating temperature of the cell was increased when the value of solar intensity was high. Thereby, the electrical efficiency was decreased. It was found that the metal foam fins decreased the PV temperature by 2-3 ^o