The modified Hummers method was applied to prepare graphene oxide (GO) from the graphite powder. Tin oxide nanoparticles with different loading (10-20 wt.%) supported on reduced graphene oxide were synthesized to evaluate the oxidative desulfurization efficiency. The catalyst was synthesized by the incipient wetness impregnation (IWI) technique. Different analysis methods like FT-IR, XRD, FESEM, AFM, and Brunauer-Emmett-Teller (BET) were utilized to characterize graphene oxide and catalysts. The XRD analysis showed that the average crystal size of graphene oxide was 6.05 nm. In addition, the FESEM results showed high metal oxide dispersions on the rGO. The EDX analysis shows the weight ratio of Sn is close to its theoretical weight.

Multi-walled carbon nanotubes (MWCNTs) were synthesized by chemical vapor deposition (CVD) using ferrocene as the carbon and iron-catalyst precursor and were evaluated for antibacterial activity against Escherichia coli ATCC 25,922. The as-grown material was characterized by X-ray diffraction (XRD), Raman spectroscopy, field-emission scanning electron microscopy (FE-SEM), and energy-dispersive X-ray spectroscopy (EDX). The characterization results confirmed the formation of graphitized multi-walled nanotube structures and the presence of iron-containing residues derived from the ferrocene precursor. Antibacterial activity was assessed by agar well diffusion, broth microdilution, and viable-count plating. A concentration-dependent reduction

In this work pyrazolin derivatives were prepared from the diazonium chloride salt of 4-aminobenzoic acid. Azo compounds were prepared from the reaction of an ethanolic solution of sodium acetate and calculated amount of active methylene compound namely, acetyl acetone to obtain the corresponding hydrazono derivative (1). Cyclocondensation reaction of compounds (1) with hydrazine hydrate and phenyl hydrazine in boiling ethanol affording the corresponding pyrazoline-5-one derivatives of 4-aminobenzoic acid (2,3). Then compound (3) was reacted with thionyl chloride to give the corresponding acid chloride derivative(4), followed by conversion into the corresponding acid hydrazide derivative (5) carboxylic acid thiosemicarbazide (11), esters

Alloys from AgSb(SxSe1-x)2 with different compositions were prepared using quenching from the melt . This was done by put the appropriate amount of Ag, Sb,S and Se in an evaluated quartz ampoule , sealed and left at oven in temperature 1273 for 5 hours. Thin films with different composition were deposited by pulsed deposition technique PLD onto glass substrates at ambient temperature . This paper concerned on the investigate effect of composition on structural morphology, and electrical properties. The structure and morphology of the prepoared thin films were checked using X–ray diffraction and atomic force microscope. The D.C conductivity of the AgSb(SxSe1-x)2thin films with various x content was measured

نحو تعزيز المشاركة السياسية للطالبات الجامعيات الفلسطينيات

This work studies developing ultrafiltration (UF) membranes using organic and inorganic additives to remove organic dyes at UF conditions with high effectiveness. Flat sheet (18 wt%) polyvinylidene fluoride (PVDF) membranes were prepared via phase inversion and then developed by adding 6 wt% polyethylene glycol (PEG) as a pore former. Furthermore, the PVDF/PEG membranes were developed by embedding tin oxide nanoparticles (SnO2 NPs) with different contents of 0.3, 0.6, and 0.9 wt%. The prepared membranes were examined for their performance in the dye removal before being characterized using the field emission scanning electron microscope, atomic force microscopy, contact angle, Fourier-transform infrared spectroscopy, surface charge,