In this work, MWCNT in the epoxy can be prepared at room temperature and thickness (1mm) at different concentration of CNTs powder. Optical properties of multi-walled carbon nanotubes (CNTs) reinforced epoxy have been measured in the range of (300-800)nm. The electronic transition in pure epoxy and CNT/epoxy indicated direct allowed transition. Also, it is found that the energy gap of epoxy is 4.1eV and this value decreased within range of (4.1-3.5)eV when the concentration of CNT powder increased from (0.001-0.1)% respectively.
The optical constants which include (the refractive index (n), the extinction coefficient (k), real (ε1) and imaginarily (ε2) part of dielectric constant calculated in the of (300-800)nm at different concent

In this work, a simple and very sensitive cloud point extraction (CPE) process was developed for the determination of trace amount of metoclopramide hydrochloride (MTH) in pharmaceutical dosage forms. The method is based on the extraction of the azo-dye results from the coupling reaction of diazotized MTH with p-coumaric acid (p-CA) using nonionic surfactant (Triton X114). The extracted azo-dye in the surfactant rich phase was dissolved in ethanol and detected spectrophotometrically at λmax 480 nm. The reaction was studied using both batch and CPE methods (with and without extraction) and a simple comparison between the two methods was performed. The conditions that may be affected by the extraction process and the sensitivity of m

In the present study, advanced oxidation process / heterogeneous photocatalytic process (UV/TiO₂/Fenton) system was investigated to the treatment of oily wastewater. The present study was conducted to evaluate the effect of hydrogen peroxide concentration H₂O₂, initial amount of the iron catalyst Fe⁺², pH, temperature, amount of TiO₂ and the concentration of oil in the wastewater.  The removal efficiency for the system UV/TiO₂/Fenton at optimal conditions and dosage (H₂O₂ = 400mg/L, Fe⁺² = 40mg/L, pH=5, temperature =30^oC, TiO₂=75mg/L) for 1000mg/L load was found to be 77%.

Aluminum foil cover around the re

A field trial was conducted in Experimental Station of The Field Crops Department – College Of Agriculture In Abu Ghraib, University of Baghdad to assess the effect of sulphur applications and the time after application on pH and EC of soil sample solutions ,and on the growth and yield of rape seed (Brassica napus L.)A split plot design was used with four replications , The main plot included four sulphur applications levels (0,2000,3000,4000Kg S/ha) the sub plot were the time after application (0,1,2,and 3 moths) .Sulphur application significantly decreased soil pH value ,although that decrease reached minimum parameter after two months from application date .Rather increment of sulphur application level significantly raised soil EC val

  This study included prepared samples of epoxy reinforced by the novolac , aluminum , glass powder and epoxy reinforced by aluminum , glass powder and epoxy alone .They are used as reinforced materials of volum fraction amounting 40% .  The mechanical properties inclouded ( tensile , compressive and wear) where the wear test inclouded different applied loads (5,10,15) . From the results showed the epoxy reinforced by aluminum and glass powder has higher compressive strength (56.91) Mpa and higher tensile strength (132.2) Mpa .But the epoxy alone has higher wear rate and the epoxy reinforced by aluminum and glass powder which have higher elasticity of modulus from the tensile test (315.7) Mpa

The physical, the thermal and the mechanical properties of Nano-composites, that consisted of Polyprime EP epoxy that reinforced by multi-walled carbon nanotubes (MWCNTs), have been studied. Various loading ratios, 0.1, 0.5, and 1 wt. %of MWCNT shave been infused into epoxy by a magnetic stirrer and then the hardener mixed with the mthat supplied with the epoxy. All sample shave been cutting using CNC machine. Tensile test, three-point bending, hardness tests, lee's disk, differential scanning calorimetry, water absorption and dielectric and electrical conductivity test were utilized on unfilled, MWCNT-filled epoxy to identify the loading effect on the properties of materials. Scanning electron microscopy (SEM) was used to determine the

Determining the actual amounts of active ingredients in various pharmaceutical commercial forms is still receiving a lot of attention. Two flow injection analysis (FIA) methods were suggested for determination of mesalazine (MES) in pharmaceutical forms. Normal and reverse FIA systems (nFIA and rFIA) combined with UV-Vis spectrophotometric technique were used for the analysis. The methods involved using two mods of FIA systems for measuring a colored product result from coupling of MES with 2,2'-dihydroxybiphenyl after oxidized with sodium periodate in alkaline medium. The absorbance of the red colored dye was measured at maximum wavelength of 500 nm. The calibration graphs for MES were linear in the ranges 2.5-200 and 0.5-60 µg/mL with

The present study aim at preparing frusemide in liquid form suitable for oral use. This is achieved through preparing different liquid forms of frusemide. The frusemide liquid is prepared in the following forms: oral solution, syrup and elixir with intensity of 1, 0.4 and 0.8% weight /volume respectively and in combination with potassium carbonate, polysorbate 80, alcohol and phosphate buffer solution of pH8 to dissolve the frusemide in the above mentioned forms. The different forms of the prepared medicine have been stored in glass bottles that can provide protection against light and at 40, 50, 60⁰C for four months. Besides the pH has been checked to decide the period of validity. The results show that the expiration date of

The nanocomposite on the base of synthesis Copper iodide
nanoparticles and polyvinyl alcohol (PVA/CuI) with different
concentration of CuI were obtained using casting technique.
PVA/CuI polymer composite samples have been prepared and
subjected to characterizations using FTIR spectroscopy, The FTIR
spectral analysis shows remarkable variation of the absorption peak
positions with increasing CuI concentration. The obtained results by
X-ray diffraction indicated the formation of cubic CuI particles. The
effects of CuI concentrations on the optical properties of the PVA
films were studied in the region of wavelength, (190-1100) nm.
From the derivation of Tauc's relation it was found that the direct
allowed t