New Schiff bases derivatives [IV]a-e is prepared via condensation of Derythroascorbic acid with p-substituted aldehydes in dry benzene. To obtain these derivatives, the 5,6-O-isopropylidene-L-ascorbic acid[I] was chosen as starting material, compound prepared from the reaction of L-ascorbic acid as starting material. Compound[I] was prepared from the reaction of L-ascorbic acid with dry acetone in the presence of hydrogen chloride. The esterification of hydroxyl groups at C-2 and C-3 positions with excess ofethyl α –chloroacetate in the presence of sodium acetate produce acorresebonding ester [II] , which was condensed with hydrazine hydrate to give new hydrazide [III] . The new Schiff bases [IV]a-e were synthesized by reaction of acid h

An aromatic ester containing two azo groups namely p-nitro phenyl azo-β-naphthyl-(4'-azobenzoic acid)-4-benzoate was synthesized by esterfiaction of 4,4'-azo dibenzoic acid with p-nitro phenyl azo-β-naphthol. Synthesized ester was characterized by CHN-Elemental analysis, FTIR, 1H NMR and 13C NMR. A modified PVA polymer was obtained by grafting 10 g of PVA-polymer via partial esterification with (2, 3, 4 g) p-nitro phenyl azo-1-naphthyl-4-azobenzoic acid)-4-azo benzoate. Grafting PVA-polymer behaviours was studied, by physical measurements (solubility, swelling), thermal properties (DSC) and tensile.

Thermal and catalytic pyrolysis of waste plastics in an inert atmosphere has been regarded as a creative method, since pyrolysis can convert plastics waste into hydrocarbons that can be used either as fuels or as a source of chemicals.

Natural Iraqi kaolin clay was used to synthesis the NaX nano- zeolite by hydrothermal conditions with average particle size equal to 77.63nm.Thermal decomposition kinetics of high-density polyethylene (HDPE) in the absence and presence of catalysts nano NaX Zeolite was investigated. Thermal and catalytic degradation of HDPE was performed using a thermogravimetric analyzer in nitrogen atmosphere under non-isothermal conditions 4, 7 and 10 °C/min heating rates were employed in thermogravimetric anal

Adsorption techniques are widely used to remove certain classes of pollutants from wastewater. Phenolic compounds represent one of the problematic groups. Na-Y zeolite has been synthesized from locally available Iraqi kaolin clay. Characterization of the prepared zeolite was made by XRD and surface area measurement using N2 adsorption. Both synthetic Na-Y zeolite and kaolin clay have been tested for adsorption of 4-Nitro-phenol in batch mode experiments. Maximum removal efficiencies of 90% and 80% were obtained using the prepared zeolite and kaolin clay, respectively. Kinetics and equilibrium adsorption isotherms were investigated. Investigations showed that both Langmuir and Freundlich isotherms fit the experimental data quite well. On the

Esterification considers the most important reaction in biodiesel production. In this study, oleic acid was used as a suggested feedstock in order to study and simulate production of biodiesel. The batch esterification reaction of oleic acid was carried out at various operating conditions; temperature from 40 to 70 °C, ethanol to oleic acid molar ratio from 3/1 and 6/1 and a reaction time up to 180 min.
The catalyst used was prepared NaY zeolite, which is added to the reaction mixture as 2, 5 and 10 wt.% of oleic acid.
The results show that the optimum conditions, gives 0.81 conversion of oleic acid, were 6/1 molar ratio of ethanol/oleic acid, 5 wt.% NaY relative to initial oleic acid, 70°C and 60 minutes. The activation energy o

Effect of nano and micro SiO2 particles with different weight percent (2,4,6,8 and 10) %wt on the Interlaminar fracture toughness (GIc) of 16-plies of woven roving glass fiber /epoxy composites prepared by hand lay – up technique were investigated. The specimens were tested using DCB test (mode I).
Area method was used to compute the interlaminar fracture toughness. The results show that, GIc would increase with the increasing in the filler content, the main failure in microcomposites and nanocomposites was delamination in the layers, the delamination reduced with increasing in the filler content.

The Eurasia Proceedings of Science Technology Engineering and Mathematics | Volume: 6

 In this work, the ligand was obtained from the reaction of diazonium salt of naphthyl amine with 1-amino-2-naphtol-4-sulfonic acid. The bidentate ligand  type (NO) donar atoms was reacted with 1,10-phenanthroline and matel salt in a 1:1:1 mole ratio to give the complexes, using NaOH as a base. Physical-chemical teqnichas were used to characteriz the prepared compounds FT-IR,U.V-Vis, fluorescence and 1HNMR spectroscopy, atomic absorption , chloride content along with conductivity and melting point measurements .Finally, thermal analysis was used to confirm the presence of coordination H2O molecule in the complexes structure. According to memtioned characterization methods, the general formula proposed for CoII ZnII, CdII and Hg