This contribution provides an atomistic understanding into the impact of W, Nb, and Mo co-substitution at Hf-site of cubic HfO2 lattice to produce Hf1−xTMxO2 system at x = 25%. The calculations have been performed under the framework of density functional theory supported by Habbured parameter (DFT+U). Structural analysis demonstrates that the recorded lattice constants is in good coherence with the previously published results. For the lattice parameters, contraction by 1.33% comparing with the host system has been reported. Furthermore, the doping effect of TM on the band gap leads to its reduction in the resulting Hf0.75TM0.25O2 configurations. The partial density of states (PDOS) indicate that hybridization through localized electroni

This contribution provides an atomistic understanding into the impact of W, Nb, and Mo co-substitution at Hf-site of cubic HfO2 lattice to produce Hf1−xTMxO2 system at x = 25%. The calculations have been performed under the framework of density functional theory supported by Habbured parameter (DFT+U). Structural analysis demonstrates that the recorded lattice constants is in good coherence with the previously published results. For the lattice parameters, contraction by 1.33% comparing with the host system has been reported. Furthermore, the doping effect of TM on the band gap leads to its reduction in the resulting Hf0.75TM0.25O2 configurations. The partial density of states (PDOS) indicate that hybridization through localized electroni

The limitations of conventional cement mortar as a widely used construction material include low tensile capacity, high permeability, and susceptibility to chemical degradation. The increasing demand for durable and sustainable construction materials has led to increased attention in modifying cementitious materials through nanotechnology. This study investigates the influence of nano-silica (NS) and nano-alumina (NA) on the physical, strength-related, and durability characteristics of cement mortar to determine the optimum nanomaterial type and dosage for performance enhancement. Six mortar mixes, in addition to a reference mix, were designed and prepared by adding 1%, 1.5%, and 2% of the cement weight with NS and NA separately, an

Coblatcomplex has been prepared by reaction between C16H19N3O3S (L) as ligand and metal salt (II). The prepared complex were characterized by infrared spectra, electromic spectra, magnetic susceptibility, molar conductivity measurement and metal analysis by atomic absorption and (C.H.N) analysis. From these studies tetrahedral geometry structure for the complex was suggested. The photodegredation of complex were study using photoreaction cell and preparednanoTiO2 catalyst in different conditions (concentration, temperatures, pH).The results show that the recation is of a first order with activation energy equal to (6.6512 kJ /mol).

Coblatcomplex has been prepared by reaction between C16H19N3O3S (L) as ligand and metal salt (II). The prepared complex were characterized by infrared spectra, electromic spectra, magnetic susceptibility, molar conductivity measurement and metal analysis by atomic absorption and (C.H.N) analysis. From these studies tetrahedral geometry structure for the complex was suggested. The photodegredation of complex were study using photoreaction cell and preparednanoTiO2 catalyst in different conditions (concentration, temperatures, pH).The results show that the recation is of a first order with activation energy equal to (6.6512 kJ /mol).

 In this work, nanostructure aluminum oxide thin films were deposited on glass substrates using a direct current (DC) magnetic reactive sputtering (MRS) technique. A gaseous mixture of argon and oxygen at different mixing ratios was used to synthesize Al2O3 nanoparticles. After extracting Al2O3 powder from the glass substrate, X-ray diffraction (XRD), field-emission scanning electron microscopy (FE-SEM), and energy-dispersive spectroscopy (EDS) were used to analyze the structural and morphological properties of the synthesized thin films. The effect of deposition time on the spectral properties, as well as on the size of the nanoparticles, was determined.

Polyaniline films were successfully synthesized in this study using an oxidative polymerization method at temperatures ranging from 0 to 4 ° C. Polyaniline films were deposited using a single step of chemical oxidative polymerization rather than electrochemical polymerization. The polyaniline was examined using FTIR, XRD, SEM, AFM, and Four Point Probe. This result demonstrates that polyaniline synthesized using this method has a uniform morphology, small size (17 to 40) nm, high crystallinity, and high conductivity (9.42 s/cm).

A particulate polymer composite material was prepared by reinforcing with the Aluminum Oxide (Al₂O₃) or Aluminum (Al) metallic particles with a particle size of (30) µm to an unsaturated Polyester Resin with a weight fraction of (5%, 10%, 15%, 20%).

Tensile test results showed the maximum value of elastic modulus reached (2400MPa.)  in the case of reinforcing with (Al) particles with weight fraction (20%) and (1500 MPa.)  in the case of reinforcing with (Al₂O₃) particles of the same weight fraction.

  When the impact and the flexural strength tests were done, the results showed that flexural strength (F.S), maximum shear stress (τ_max), impact strength