This research studies the effect of adding micro, nano and hybrid by ratio (1:1) of (Al2O3,TiO2) to epoxy resin on thermal conductivity before and after immersion in HCl acid for (14 day) with normality (0.3 N) at weight fraction (0.02, 0.04, 0.06, 0.08) and thickness (6mm). The results of thermal conductivity reveled that epoxy reinforced by (Al2O3) and mixture (TiO2+Al2O3) increases with increasing the weight fraction, but the thermal conductivity (k) a values for micro and Nano (TiO2) decrease with increasing the weight fraction of reinforced, while the immersion in acidic solution (HCl) that the (k) values after immersion more than the value in before immersion.

Thermal conductivity for epoxy composites filled with Al2O3 and Fe2O3 are
calculated, it found that increasing the weight ratio of Al2O3 and Fe2O3 lead to
increase in the values of thermal conductivity, but the epoxy composite filled with
Fe2O3, have values of thermal conductivity less than for epoxy composite filled with
Al2O3, for the same weight ratio. Also thermal conductivity calculated for epoxy
composites by contact to every two specimens (like sandwich) content same weight
ratio of alumina-oxide and ferrite-oxide, its found that the value of thermal
conductivity lays between the values of epoxy filled Al2O3 and of epoxy filled Fe2O3

In present work examined the oxidation desulfurization in batch system for model fuels with 2250 ppm sulfur content using air as the oxidant and ZnO/AC composite prepared by thermal co-precipitation method. Different factors were studied such as composite loading 1, 1.5 and 2.5 g, temperature 25 ^oC, 30 ^oC and 40 ^oC and reaction time 30, 45 and 60 minutes. The optimum condition is obtained by using Tauguchi experiential design for oxidation desulfurization of model fuel. the highest percent sulfur removal is about 33 at optimum conditions. The kinetic and effect of internal mass transfer were studied for oxidation desulfurization of model fuel, also an empirical kinetic model was calculated for model fuels

In this study, crop residues from rice husks were used to enhance the properties of the prepared
wood-plastic composites (W.P.C) are made from epoxy (EP) and unsaturated polyester (UPE) at
a ratio of (50:50) and reinforced with scales in different proportions, both types are fine
(300μm≤) and coarse (300μm>). These blends were undergoing (wear, impact, hardness,
differential scanning calorimetry (DSC), and thermal conductivity) tests and the results showed
the best weight fraction. is the fine particle weight fraction at 25% and coarse at 15%, depending
on the studied tribological characteristics. The results showed by thermal properties of glass
transition temperatures (Tg). For each of the (EP,

       In this study, an industrial source) E-Glass fiber) and a natural source (chestnut filler) were combined to improve the properties of polyesters. Hand-layup technique was applied in this work. Polyester (UPE) were reinforced with E-glass fibers, then reinforced with nano chestnut particles. All composites were prepared with (10% wt.) of E-glass for all prepared sheet and this ratio applied for Nano chestnut composite to preparing nano hybrid composites, Nano chestnut particles were used to reinforce E-glass/UPE composites with weight ratio (3%, 6% and 9% wt.). The evaluated mechanical performances for E-glass/NCSP polyester composite were tensile strength, impact strength and hardness. The higher ultimate tensile strength, Y

In this research study theory to find the stress and emotion gases in the glass as a result of exposure to pulses of the laser beam has been the study using vehicles three major on-system axes cylindrical (r, 0, z), where I took three models of glass silica glass soda glass fused and shedtwo types of lasers where the study showed that the thermal stresses and emotions ...

The aim of this study is to determine the flexural properties of steel fiber as a metal fiber and polyester resin as a matrix. The steel fibers were added to polyester resin at the various fiber volume fractions of 5, 10, and 15% steel fiber, and with different fiber orientations such as woven steel fiber type (0-45) ° and woven steel fiber type (0-90) ° indicate. Hand layup processes in these experiments were used to produce specimens test with the curing time of 24 hr. for the composite at room temperature. The results show that the flexural strength and flexural modulus values for 15 % vol.of woven steel fiber composite type (0-90) ° are (210MPa) and (2.29GPa( respectively. The results above indicate that the woven steel fiber (0-9

In this work, two groups of nanocomposite material, was prepared from unsaturated polyester resin (UPE), they were prepared by hand lay-up method. The first group was consisting of (UPE) reinforced with individually (ZrO2) nanoparticles with particle size (47.23nm). The second group consists of (UPE) reinforced with hybrid nanoparticles consisting of zirconium oxide and yttrium oxide (70% ZrO2 + 30% Y2O3) with particles size (83.98nm). This study includes the effect of selected volume fraction (0.5%, 1%, 1.5%, 2%, 2.5%, 3%) for both reinforcement nano materials. Experimental investigation was carried out by analyzing the thermo-physical properties like thermal conductivity, thermal diffusivity and specific heat for the polymeric composit

In this research prepared Epoxy – Talc powder composites with weight ratio of Talc powder (0,5,10,15,20,25)% . The value of thermal conductivity increase with increasing ratio of talc powder and water absorption increase with increasing ratio of talc powder because the structure from magnesium silicate hydroxide and hydrophilic nature .Ethanol absorption decrease with increasing percentage talc powder compared with epoxy pure