Twenty nine core samples were taken from Ratawi 7 Oil well according to the presence of oil in formation and availability of core samples. This well is located in the province of Basra/southern Iraq. The samples were collected from Yamama Formation. The core samples are taken from the well at different depths, ranging between (3663m-3676m). The range of Vp for these core samples is (668-4017 m/sec) and its average is (1779 m/sec), While the range of Vs is (291-1854 m/sec) and its average is (796 m/sec). In the current study the ultrasonic method is conducted to measure Vp, Vs as well as some petrophysical properties for core samples and some elastic moduli such as (Young's modulus, Bulk modulus, Shear modulus, Poisson's ratio and Lame's

This study involved the treatment of textile wastewater contaminated with direct blue 15 dye (DB15) using a heterogeneous photo-Fenton-like process. Bimetallic iron/copper nanoparticles loaded on bentonite clay were used as heterogeneous catalysts and prepared via liquid-phase reduction method using eucalyptus leaves extract (E-Fe/Cu@BNPs). Characterization methods were applied to resultant particles (NPs), including SEM, BET, and FTIR techniques. The prepared NPs were found with porous and spherical shapes with a specific surface area of particles was 28.589 m2/g. The effect of main parameters on the photo-Fenton-like degradation of DB15 was investigated through batch and continuous fixed-bed systems. In batch mode, pH, H2O2 dosage, DB15 c

The research included the preparation of cyclic compounds from thiazoles, imidazoles and oxazepines from the reaction of cyclization starting material that acts Schiff bases, which is a raw material in the formation of cyclic compounds from Schiff's(B1) by reaction of 4- aminobenzenesulfonylamide with 4-hydroxyacetophenone which can used to synthesized two lines. The first introducing the preparation of pyrazoles [B4, B5] from ester [B2], which derived to acid hydrazide[B3] with hydrazine hydrate and final pyrazoles obtained by the reaction with diethylmalonate and acetylacetone. The second including prepared the new 1,3-oxazepine1,5-dione derivatives[B6,B7,B8] from adding different anhydrides to the base[B1] as a seven membered ring ; te

Hybrid architecture of ZnO nanorods/graphene oxide ZnO-NRs@GO synthesized by electrostatic self-assembly methods. The morphological, optical and luminescence characteristics of ZnO-NRs@GO and ZnO-NRs thin films have been described by FESEM, TEM, HRTEM, and AFM, which refers to graphene oxide have been coated ZnO-NRs with five layers. Here we synthesis ZnO-NRs@GO by simple, cheap and environmentally friendly method, which made it favorable for huge -scale preparation in many applications such as photocatalyst. ZnO-NRs@GO was applied as a photocatalyst Rodamin 6 G (R6G) dye from water using 532 nm diode laser-induced photocatalytic process. Overall degradation of R6G/ ZnO-NRs@GO was achieved after 90 minutes of laser irradiation while it ne

In this manuscript, the effect of substituting strontium with barium on the structural properties of Tl_0.8Ni_0.2Sr_2-xBr_xCa₂Cu₃O_9-δcompound with x= 0, 0.2, 0.4, have been studied. Samples were prepared using solid state reaction technique, suitable oxides alternatives of Pb₂O₃, CaO, BaO and CuO with 99.99% purity as raw materials and then mixed. They were prepared in the form of discs with a diameter of 1.5 cm and a thickness of (0.2-0.3) cm under pressures 7 tons / cm², and the samples were sintered at a constant temperature o

A thin film of SnSe were deposited by thermal evaporation technique on 400 ±20 nm thick glass substrates of these films were annealed at different temperatures (100,150,200 ⁰C), The effect of annealing on the characteristics of the nano crystalline SnSe thin films was investigated using XRD, UV-VIS absorption spectroscopy, Atomic Force Microscope (AFM), and Hall effect measurements. The results of X-ray displayed that all the thin films have polycrystalline and orthorhombic structure in nature, while UV-VIS study showed that the SnSe has direct band gap of nano crystalline and it is changed from 60.12 to 94.70 nm with increasing annealing temperature. Hall effect measurements showed that all the films have a positive Hall coeffic