Examining how PMMA and polyamide denture base materials' physical characteristics are affected by electrolyzed water used as a denture cleaner
...Show More Authors

Denture cleansing is an essential step that can stop cross‑contamination and adds to the health of the patient, denture durability, and the general quality of life. A disinfection technique must be practical and devoid of damaging effects on the material's properties used to construct the denture base. The main aim of this study is to evaluate the effect of three concentrations of electrolyzed water denture cleanser on heat cure acrylic and polyamide after immersion in electrolyzed water. The evaluation is based on their efficacy on surface hardness, wettability, and color stability compared with one submerged in distilled water as a control group. The method consists of eighty samples of heat-cured acrylic and polyamide material. The samples were immersed in electrolyzed water at a concentration of (100-200ppm) and in distilled water for 5 minutes, 30 times, and daily for 12 days to simulate a one-year interval. The tests showed that the surface hardness and color stability were maintained, with no significant difference between the control and experimental groups. In comparison, the result of wettability showed a statistically significant difference between the control and experimental groups. Thus, electrolyzed water does not affect the surface hardness and color stability of heat-cure acrylic and polyamide denture base materials. However, the wettability of these materials was significantly increased. Keywords: Electrolyzed water; Heat cure acrylic; Polyamide material

Scopus Crossref
View Publication Preview PDF
Quick Preview PDF
Publication Date
Sun Nov 01 2020
Journal Name
Iop Conference Series: Materials Science And Engineering
Assessment of some mechanical properties of PMMA/silica/zirconia nanocomposite as a denture base material
...Show More Authors
Abstract<p>In this research, nanocomposites of poly(methyl methacrylate) (PMMA) and a mixture of nano silica (SiO<sub>2</sub>) and nano zirconia (ZrO<sub>2</sub>) were prepared in different weight percentages of the nano fillers to improve some of the properties of PMMA resin to be used as a denture base material. The nano filles were surface modified with a coupling agent and added to the PMMA in different amounts. Impact strength, transverse strength, hardness and roughness were tested for both control and experimental groups. The results indicate that PMMA/silica/zirconia nanocomposites, prepared with 5% by weight of both types of fillers, had a slight increase in impact s</p> ... Show More
View Publication
Scopus (23)
Crossref (12)
Scopus Crossref
Publication Date
Wed Mar 12 2025
Journal Name
Journal Of Baghdad College Of Dentistry
Evaluation of shear bond strength between thermosens as relining material and different denture base materials
...Show More Authors

Background: Denture relining is the process of resurfacing of the tissue side of the ill fitting denture, the bond strength at the relining-denture base interface is most important for denture durability.The aim of present study was to evaluate the shear bond strength between the thermosens as relining material and different denture base materials that bonded by thermo fusing liquid. As this corrective procedureis the common chair side procedure in the dental clinic. Material and method: Sixty samples were prepared and divided into three main groups according to the type of denture base materials.Group (A) referred to the heat cure acrylic samples which consisted of 20 samples. Group (B) referred to the high impact acrylic samples which con

... Show More
View Publication Preview PDF
Publication Date
Tue Sep 04 2018
Journal Name
Al-khwarizmi Engineering Journal
Studying the Mechanical Properties of Denture Base Materials Fabricated from Polymer Composite Materials
...Show More Authors

In this research, the effect of adding two different types of reinforcing particles was investigated, which included: nano-zirconia (nano-ZrO2) particles and micro-lignin particles that were added with different volume fractions of 0.5%, 1%, 1.5% and 2% on the mechanical properties of polymer composite materials. They were prepared in this research, as a complete prosthesis and partial denture base materials was prepared, by using cold cure poly methyl methacrylate (PMMA) resin matrix. The composite specimens in this research consist of two groups according to the types of reinforced particles, were prepared by using casting methods, type (Hand Lay-Up) method. The first group consists of PMMA resin reinforced by (nano-ZrO

... Show More
View Publication Preview PDF
Crossref (8)
Crossref
Publication Date
Fri Jul 22 2022
Journal Name
Journal Of Biomimetics, Biomaterials And Biomedical Engineering
Influence of Bioactive and Bio Inert Ceramic Powders on Tribology Properties of PMMA Composite Denture Base
...Show More Authors

Polymer matrix composites are suitable materials for medical applications, such as denture base resin polymethyl methacrylate (PMMA). This includes light weight and high strength. This paper describes the effect of selected weight fractions (1, 2, 3, 4 & 5) % wt of nano(Alumina AL2O3, Zirconia ZrO2, Hydroxyapatite HA and Halloysite nanoClay) reinforcements on the biopolymer matrix (PMMA). Some tribology tests were used to evaluate the prepared system (impact strength, hardness surface, and wear rate) tests. The samples were fabricated by (Hand Lay-Up) with different particle reinforcement percentages. All tests were accomplished at room temperature, and samples were developed according to the ASTM standard. The weight fraction o

... Show More
View Publication
Scopus (1)
Crossref (2)
Scopus Clarivate Crossref
Publication Date
Fri Jul 01 2022
Journal Name
Journal Of Biomimetics, Biomaterials And Biomedical Engineering
Influence of Bioactive and Bio Inert Ceramic Powders on Tribology Properties of PMMA Composite Denture Base
...Show More Authors

Polymer matrix composites are suitable materials for medical applications, such as denture base resin polymethyl methacrylate (PMMA). This includes light weight and high strength. This paper describes the effect of selected weight fractions (1, 2, 3, 4 & 5) % wt of nano(Alumina AL2O3, Zirconia ZrO2, Hydroxyapatite HA and Halloysite nanoClay) reinforcements on the biopolymer matrix (PMMA). Some tribology tests were used to evaluate the prepared system (impact strength, hardness surface, and wear rate) tests. The samples were fabricated by (Hand Lay-Up) with different particle reinforcement percentages. All tests were accomplished at room temperature, and samples were developed according to the ASTM standard. The weight fraction of (4% for AL

... Show More
Scopus (1)
Scopus
Publication Date
Wed Mar 12 2025
Journal Name
Journal Of Baghdad College Of Dentistry
The Effect of Zirconium Silicate Nanopowder Reinforcement on Some Mechanical and Physical Properties of Heat Cured Poly (Methyl Methacrylate) Denture Base Materials
...Show More Authors

Background: Polymethylmethacrylate (PMMA) has relatively unsatisfactory mechanical properties such as low flexural strength and impact strength also dimensional instability. Material and method: Zirconium silicate nanoparticles were coated with a layer of trimethoxysilylpropylmethacrylate (TMSPM) before sonication in monomer (MMA) with the percentages 1% and 1.5% by weight then mixed with powder using conventional procedure, (150) samples were prepared and divided into three groups, each group consisted of (50) samples, the first group prepared from PMMA without addition (control), another group with the addition of 1% wt Zrsio4 nanoparticles (experimental) and the third one with 1.5% wt Zrsio4 nanoparticles (experimental). Each group

... Show More
View Publication Preview PDF
Publication Date
Wed Nov 07 2018
Journal Name
Iraqi National Journal Of Nursing Specialties
The Effect of Different Types of Separating Medium On Some Physical Properties of Processing Acrylic Denture-base with Two Investment Materials: A comparative Study
...Show More Authors

Objective(s): In the present study, glycerin is used as a substitute for tin-foil and cold mold seal (Alginate mould seal)
in the process of curing heat and cold-cure acrylic resin denture base against stone and plaster.
Methodology: 60 specimens were prepared from heat-cure acrylic resin and cold-cure acrylic resin denture base. The
study includes 12 groups of specimens depending on the type of processing, investment material and type of
separating medium that are used in curing process. Each group of them contains 5 specimens for each test.
Some of physical properties of the processed acrylic denture base that (water sorption and solubility) have been
compared with those processed using tin-foil and tin-foil substitut

... Show More
View Publication Preview PDF
Publication Date
Thu Dec 01 2011
Journal Name
Iraqi Journal Of Physics
Influence of water absorption on fatigue behavior for chopped and woven-glass-fibers-reinforced PMMA denture
...Show More Authors

The influence of fiber orientation and water absorption on fatigue crack growth resistance for cold cure acrylic (PMMA) reinforced by chopped and woven -glass-fibers were investigated. A weight of 2 g for chopped fibers and the same weight for woven -glass-fibers (one layer) were used to prepare samples. Some of these samples would storage in dry condition; the others were immersed in water for 15 days. Fatigue test was carried out. The results shows that, for PMMA, the initial bending stress for dry specimen was 3.392 N/cm2 and the number of cycles were 1364, the initial bending stress for wet samples was 4.20 N/cm2, and the number of cycles was 2411. The samples would cut in two pieces because of the cracks would propagated fast during

... Show More
View Publication Preview PDF
Publication Date
Wed Mar 12 2025
Journal Name
Journal Of Baghdad College Of Dentistry
The effect of the addition of silanized Nano titania fillers on some physical and mechanical properties of heat cured acrylic denture base materials
...Show More Authors

Background: Polymethyl methacrylate (PMMA) is the most commonly used material in denture fabrication. The material is far from ideal in fulfilling the mechanical requirement. The purpose of this study was to evaluate the effect of addition of 3% wt of treated (silanized) Titanium oxide Nano filler on some physical and mechanical properties of heat cured acrylic denture base material. Materials and methods: 100 specimens were constructed, 50 specimens were prepared from heat cure PMMA without additives (control) and 50 specimens were prepared from heat cure PMMA with the addition of TiO2 Nano fillers. Each group was divided into 5 sub groups according to the test performed which was mixed by probe ultra-sonication machine. Results: A highly

... Show More
View Publication Preview PDF
Publication Date
Wed Mar 12 2025
Journal Name
Journal Of Baghdad College Of Dentistry
The Effect of Plasma Treatment on Shear Bond Strength of High Impact Acrylic Resin Denture Base Lined with Two Types of Soft Lining Materials after Immersion in Distilled Water and Denture Cleanser
...Show More Authors

Background: In dentistry, dentist takes the advantages of soft lining materials due to the viscoelastic properties. The major problem is the adhesion of the soft liner with the denture base material. Materials and Methods: Heat cured of high impact acrylic resin specimens prepared with dimensions 75x13x13mm for shear bond strength test, soft lining material (Refit and Mollosil) with a 3-mm thickness and used to join each two acrylic blocks. Also four specimens with the same previous dimensions utilized for chemical and physical surface analysis. The specimens grouped as control (without plasma) and experiment (with oxygen plasma) treated high impact acrylic specimens. Results: Plasma treatment increased the shear bond strength for both Refi

... Show More
View Publication Preview PDF