In this research we study the effect of UV radiation on pure PC samples and doped samples with plasticizer (DOP) for different exposure times (6, 12, 18, 24h). The study have been made on the change in the IR spectra causes by the UV radiation on both kinds of samples, besides the morphology changes were also studied by the optical microscope. From the results we conclude that the increasing of exposure causes the elaboration of CO₂ and C₂ gases.

A particulate polymer composite material was prepared by reinforcing with the Aluminum Oxide (Al₂O₃) or Aluminum (Al) metallic particles with a particle size of (30) µm to an unsaturated Polyester Resin with a weight fraction of (5%, 10%, 15%, 20%).

Tensile test results showed the maximum value of elastic modulus reached (2400MPa.)  in the case of reinforcing with (Al) particles with weight fraction (20%) and (1500 MPa.)  in the case of reinforcing with (Al₂O₃) particles of the same weight fraction.

  When the impact and the flexural strength tests were done, the results showed that flexural strength (F.S), maximum shear stress (τ_max), impact strength

This study aimed to identify the alterations of liver in the quail (Coturnix coturnix) exposed by nanosilver particles.45 quail (females) were collected from agriculture research center in Abu-Ghraib, divided into (6) groups including: T1(12 quails were exposed to 4ppm), T2 (12 quails were exposed to 8ppm) and T3 (12 quails were exposed to 12ppm) of silver nanoparticles solution for 60 days. As well as three groups for control (3 females for each). Birds were dissected to isolate livers for histological preperations after fixation with Bouin's fluid, Routine stains Hematoxyline and eosin were used. Histological study showed that the structure of liver in a control groups consist of hepatocytes arranged radially cords around the central vein

Background: This study compared in vitro the marginal adaptation of three different, low shrink, direct posterior composites Filtekâ„¢ P60 (packable composite), Filtekâ„¢ P90 (Silorane-based composite) and Sonic fillâ„¢ (nanohybrid composite) at three different composite/enamel interface regions (occlusal, proximal and gingival regions) of a standardized Class II MO cavity after thermal changes and mechanical load cycling by scanning electron microscopy. Materials and methods:Thirty six sound human maxillary first premolars of approximately comparable sizes were divided into three main groups of (12 teeth) in each according to the type of restorative material that was used: group (A) the teeth were restored with Filtekâ„¢ P6

Several  amine  liquid selective  electrodes  were prepared based on

two  active   materials,   phenol  sulfonic   acid  and   l ,2-dihydroxy-3,5- disulfonic  acid   disodium   salt   with  several   plasticizers,  di-n-butyl phthalate(ORPH),  tri-n-butyl   phosphate   (TBP)   and  a-nitro   phenyl octyl  ether   (NPOE).   Electrode   parameters   were  studied   including, concentration range,  detection  limit,  slope,  life  time,  response  time and  

During the past forty years, and due to the global climate changes, Iraq had and still suffering from the spreading and expansion of large dune fields in which many new generations have been accumulated, and older ones have expanded leading to the desertification of huge agricultural and urban areas and causing vast environmental problems that have a drastic effect on the life style of the population. To tackle such a problem, many methods have been suggested and even more are applied to fix the dunes or at least to limit their spreading so that to lessen the environmental impact. Such efforts were tried in many dune areas in Iraq, but it was in vain due to the classical nature of remedy that deals only with temporary and limited results

The aim of this study was to investigate the effect of operating variables on, the percentage of removed sludge (PSR) obtained during re-refining of 15W-40 Al-Durra spent lubricant by solvent extraction-flocculation treatment method. Binary solvents were used such as, Heavy Naphtha (H.N.): MEK (N:MEK), H.N. : n-Butanol (N:n-But), and H.N. : Iso-Butanol (N:Iso:But). The studied variables were mixing speed (300-900, rpm), mixing time (15-60, min), and operating  temperature (2540, oC). This study showed that the studied operating variables have effects where, increasing the mixing time up to 45 min for H.N.: MEK, H.N.: n-Butanol  and 30 min for H.N.: Iso-Butanol increased the PSR, after that percentage was decreased; increasing t

In this study the melting point and hardness of the paraffin wax was improved by mixing it with 1:1 ratio of micro crystalline wax then adding weight percentage wt% of locally produced nano particles (CuO,ZnO,AI2O3 and bentonite ) for each addition to the wax mixture. The results showed an increase in the melting point and hardness values of the prepared samples by increasing the weight percentage of each nano particles additives. . It was found that the addition of nano bentonite to the wax mixture gave high melting point values (122.5°C)and hardness (81.2)followed by melting point value (97°C)and hardness(68.2)resulting from the addition of CuO nano particles to the wax mixture compared to other used nano particles.