Reuse of spent hydrodesulphurization (HDS) of middle petroleum fractions catalyst CoMo/γAl₂O₃ was accomplished via removal of coke and contaminants such as vanadium, Iron, Nickel, and sulfur. Three processes were adopted; extraction, leaching, decoking. Soluble and insoluble coke was removed. Leaching step used three different solvents (oxalic acid, ammonium peroxydisulfate and oxalic acid + H₂O₂) in separate in order to remove contaminant metals (V, S, Ni and Fe).

   The effect of soluble coke removal on leaching step was studied. It was found that the removal of soluble coke significantly enhances the leaching of contaminants and barely affected the removal of active metals

In this work, varying compositions of SiO₂ micro filler were added
with the Polyvinyl Chloride (PVC) and samples have been prepared
using film casting technique. The results have been analyzed and
compared for PVC samples with (1 wt%, 3 wt%, 5 wt% and 10 wt%)
SiO2 micro filler. Mechanical characteristics such as tensile strength,
elongation at break and Young`s modulus were measured for all the
samples, where the tensile strength was increased from 8.39 Mpa for
purified PVC to 16 Mpa for 3% SiO₂/PVC composite. Also, thermal
conductivity measurement values illustrated that composite materials
have a good thermal insulation at 10 wt. %, thermal conductivity was
decreased from 0.1684 W/m.

Samarium ions (Sm +3), a rare-earth element, have a significant optical emission within the visible spectrum. PMMA samples, mixed with different ratios of SmCl3.6H2O, were prepared via the casting method. The composite was tested using UV-visible, photoluminescence and thermogravimetric analysis (TGA). The FTIR spectrometry of PMMA samples showed some changes, including variation in band intensity, location, and width. Mixed with samarium decreases the intensity of the CO and CH2 stretching bands and band position. A new band appeared corresponding to ionic bonds between samarium cations with negative branches in the polymer. These variations indicate complex links between the Sm +3 ion and oxygen in the ether group. The optical absorption

In this investigation, metal matrix composites (MMC_s) were manufactured by using powder technology. Aluminum 6061 is reinforced with two different ceramics particles (SiC and B₄C) with different volume fractions as (3, 6, 9 and 12 wt. %). The most important applications of particulate reinforcement of aluminum matrix are: Pistons, Connecting rods etc. The specimens were prepared by using aluminum powder with 150 µm in particle size and SiC, B₄C powder with 200 µm in particle size. The chosen powders were mixed by using planetary mixing setup at 250 rpm for 4hr.with zinc stearate as an activator material in steel ball milling. After mixing process the powders were compacted by hydraulic

In this work, a composite material was prepared from Low-density polyethylene (LDPE) with different weight percent of grain and calcinations kaolin at temperature of (850^oC) using single screw extruder and a mixing machine operated at a temperature between (190-200^oC). Some of mechanical and physical properties such as tensile strength, tensile strength at break, Young modulus, and elongation at break, shore hardness and water absorption were determined at different weight fraction of filler (0, 2, 7, 10 and 15%). It was found that the addition of filler increases the modulus of elasticity, elongation at break, shore hardness and impact strength; on other hand, it decreases the tensile strength and tensile strength

The effect of Wood Flour addition to the gamma alumina powder used in the preparation of gamma alumina (ɤ-Al₂O₃) catalyst carrier extrudates on the pore volume and BET surface area physical properties was investigated. Two parameters which are size of wood flour particles and its quantity were studied. The sizes of wood flour particles used are 150 µm, 212 µm and 500 µm and the weight percentage added to the gamma alumina powder during the preparation of the extrudates are (1%, 3%, 5% and 10%). The results showed that the addition of wood flour to the gamma alumina powder in order to get gamma alumina extrudates used as catalyst carrier is one of the successful methods to improve the pore volume

Avery large numbers of articles are made by powder metallurgical methods using electrolytically reduced metal powders. Iron powder is one of these powders which play an important role in this field. Its preparation by electrolytic method is economic in comparison with the traditional methods (Atomization and carbonyl processes).

An electrochemical cell consisting of two electrodes (stainless steel cathode and iron anode, 99.9%) was used to study the electrolytic preparation of iron powder with particle size less than 106µm directly as powde1y form. Ferrous sulphate electrolyte was used containing sodium chloride as a stabilizing agent. The produced powder was thoroughly washed with an acidified distilled water and absolute ethan

The Cu2SiO3 composite has been prepared from the binary compounds (Cu2O, and SiO2) with high purity by solid state reaction. The Cu2SiO3 thin films were deposited at room temperature on glass and Si substrates with thickness 400 nm by pulsed laser deposition method. X-ray analysis showed that the powder of Cu2SiO3 has a polycrystalline structure with monoclinic phase and preferred orientation along (111) direction at 2θ around 38.670o which related to CuO phase. While as deposited and annealed Cu2SiO3 films have amorphous structure. The morphological study revealed that the grains have granular and elliptical shape, with average diameter of 163.63 nm. The electrical properties which represent Hall effect were investigated. Hall coeffici

The acidity of spent lubricant was treated using sodium hydroxide solution. The effect of three variables on the treatment have been studied . These are mixing time rangingfrom 5-35 minutes, NaOH to lubricant weight ratio ranging from  0.25-1.25 and weight percentage  of NaOH ranging from  2-6 % .

The experimental design of Box-Wilson method is adopted to find a useful relationship between the three controllable variables and the lowering in the acidity of the spent lubricant. Then the effective variables and interactions are identified using the statistical analysis(F-test) of  three variable fractional design. The mathematical model is well represented  by a second order polynomial.

By