Thin films of the blended solution of (NiPc/C60) on glass substrates were prepared by spin-coated method for three different ratios (100/1, 100/10 and 100/100). The effects of annealing temperature and C60 concentration on the optical properties of the samples were studied using the UV-Vis absorption spectroscopy and FTIR spectra. The optical absorption spectrum consists of two main bands, Q and B band, with maxima at about (602-632) nm and (700-730) nm for Q1 and Q2 respectively, and (340-375) nm for B band. The optical energy gap were determined from optical absorption spectra, The variation of optical energy gap with annealing temperature was nonsystematic and this may be due to the improvement in crystal structure for thin films. Whi

Abstract

               The main problem of the study lies in the lack of a clear perception among the study sample about the impact of digital marketing tools on legal liquidity. Legal) of the International Development Bank for Investment and Finance and to achieve the objectives of the research, the method of observation and survey was used in measuring the dimensions of digital marketing. As for banking liquidity, the reports and financial statements of the bank were used as the research sample, as well as the use of the statistical analysis program SPSS in the statement of the relationship The study concluded, in summary, the following: Mar

Background: Lack of durability of the bond of the dental adhesive systems to tooth structure is one of the most important problems in tooth colored restorative work. This in vitro study was performed to evaluate the effect of 2% chlorhexidine gluconate(CHX) on dentin bond strength by using total etch adhesive system at twenty-four hours and three months of water storage. Material and methods:A flat dentin surface was prepared for forty sound human maxillary premolar teeth which were acid etched with 36% phosphoric acid gel after being divided randomly into four groups of ten teeth each according to storage time and CHX application, theCHX was applied for 60 seconds before adhesive application for groups I and III which were tested after twe

         Melatonin is a potent scavenger of reactive oxygen species or free radicals like superoxide and hydroxyl radicals. The oxidation of hemoglobin to methemoglobin (meth-Hb) by oxidizing compounds has been widely studied. The present work was designed to evaluate the ability of different concentrations of melatonin to inhibit nitrite–induced oxidation of hemoglobin. Blood samples were obtained from apparently healthy individuals from which erythrocyte hemolysate was prepared. Different concentrations of melatonin (10^-9-1.0 mg/ml) were incubated for 10 min with the hemolysate, then to the resultant mixture 1 ml of sodium nitrite (final concentration 0.6 mM) was added, and the

The first aim of this paper was to evaluate the push-out bond strength of the gutta-percha coating of Thermafil and GuttaCore and compare it with that of gutta-percha used to coat an experimental hydroxyapatite/polyethylene (HA/PE) obturator. The second aim was to assess the thickness of gutta-percha around the carriers of GuttaCore and HA/PE obturators using microcomputed tomography (μCT). Ten (size 30) 1 mm thick samples of each group (Thermafil, GuttaCore, and HA/PE) were prepared. An orthodontic wire with a diameter of 0.5 mm was attached to the plunger of an Instron machine in order to allow the push-out testing of the gutta-percha coating. Five samples of (GuttaCore and HA/PE) were scanned using