The purpose of my thesis is to prepare four new ligands (L1-L4) that have been used to prepare a series of metal complexes by reacting them with metal ions: M=(Mn(II), Co(II), Ni(II), Cu(II), Zn(II), Cd(II), Hg(II) Where succinyl chloride was used as a raw material for the preparation of bi-dented ligands (L1-L4) by reacting it with potassium thiocyanate as a first step and then reacting with (2-aminobenzothiazole, Benzylamine, 4-aminoantipyrine, Sulfamethoxazole) respectively as a second step with the use of dry acetone as a solvent, the chemical formula of the four ligands prepared in succession: N1,N4-bis(benzo[d]thiazol-2-ylcarbamothioyl)succinamide (L1) N1,N4-bis(benzylcarbamothioyl)succinamide (L2) N1,N4-bis((1,5-dimethyl-3-oxo-2-phenyl-2,3-dihydro-1H-pyrazol-4-yl) carbamothioyl)succinamide (L3) N1,N4-bis((4-(N-(5-methylisoxazol-3-yl)sulfamoyl) phenyl) carbamo thioyl) succinamide (L4) The new ligands were identified using spectroscopic measurements that included (FT-IR spectra, UV-Vis spectra, and nuclear magnetic resonance (1H, 13CNMR) spectra, mass spectra, elemental analysis (C.H.N.S), and thermal analysis (TGA&DSC), as the results of the measurements proved to be identical to the proposed molecular formula for these ligands. A series of metal complexes for ligands was also prepared, which included seven complexes for each ligand, by adding each of the metal ions to the four ligands prepared in succession to produce the following molecular formulas: - [M2(L)Cl4] , L= L1, L2, L3, L4 (M= Mn(II), Co(II), Ni(II), Cu(II), Zn(II), Cd(II), Hg(II)) The prepared complexes were diagnosed by several techniques, including the study of the infrared spectra of the prepared complexes, and when comparing those spectra with the spectra of each of the four ligands prepared in the free form, these gave clear changes, including the emergence of a new band within the fingerprint area. It was not originally present in the spectra of ligands in their free form, and this is due to the occurrence of coordination between the metal ions under study and the donor atoms, which are the oxygen atom of the (C=O) group, and the sulfur atom of the (C=S) group in the ligands. (L1-L4), while other distinct bands were obtained with clear changes in shape, intensity, and location, and this is an indication of the occurrence of a coordination process between the metal ions under study and the four prepared ligands. The percentage of metal ions in the prepared complexes was determined by flame atomic absorption spectrometry, where it was shown from the careful analysis of the elements the great agreement between the percentages calculated theoretically and obtained practically. The magnetic sensitivity results showed that some of the prepared metallic complexes have paramagnetic properties. The measurements of the molar conductivity of the prepared complexes dissolved in DMSO at a concentration of 1×10-3 M and at the laboratory temperature showed that they are of a non-electrolytic nature. The prepared complexes were also studied through solubility, melting point, and ultraviolet-visible techniques, and through the data of all the aforementioned techniques, structural formulas were proposed for the prepared complexes, through which it was found that the prepared ligands are bivalve chelating ligands that lead to their participation as ligand into complexes with a tetrahedral geometric shape for all metallic complexes under study. The research included a study evaluating the antioxidant activity of some selected metal complexes by studying the amount of radical scavenging of DPPH* compared to ascorbic acid as an antioxidant reference agent. The zinc complex showed higher activity than the nickel complex compared to standard ascorbic acid. The [Cu2(L1)Cl4] and [Co2(L1)Cl4] complexes were also tested as antibodies to inhibit the breast cancer cell line (MCF-7) and compared with the normal cell line (HdFn), where the copper complex showed the ability to inhibit the cancerous cell line compared with the cobalt complex. The molecular binding of ligands (L3) and (L4) was also studied, and their possibility of using them as drugs in the treatment of some diseases, where the ligand L3 showed better association with the active site of the enzyme than the ligand L4, and is expected to highest antimicrobial effect. Finally, the biological effect of the prepared ligands and some of their complexes on the growth of two types of bacteria, Escherichia coli and Staphylococcus aureus, was studied using DMSO solvent, where the complexes showed greater activity than the ligands against the selected types of bacteria.
Different polymers were prepared by condensation polymerization of sebacic anhydride and adipic anhydride with ethylene glycol and poly(ethylene glycol). Their number average molecular weights were determined by end group analysis. Then, they were grafted on the prepared phthalocyaninatocopper(II) compounds with the general formula (NH2)4PcCu(II) having amino groups of 3,3',3'',3'''- or 4,4',4'',4'''- positions. All prepared polymers, compounds, and phthalocyaninatocopper(II)-grafted polymers were characterized by FTIR. The sizing measurements were carried out in 3,3',3'',3'''- (NH2)4PcCu(II) and 4,4',4'',4'''- (NH2)4PcCu(II) compounds with and without grafting polymers. The results showed that the grafting process led to decreasing in par
... Show More
The present work aims to validate the experimental results of a new test rig built from scratch to evaluate the thermal behavior of the brake system with the numerical results of the transient thermal problem. The work was divided into two parts; in the first part, a three-dimensional finite-element solution of the transient thermal problem using a new developed 3D model of the brake system for the selected vehicle is SAIPA 131, while in the second part, the experimental test rig was built to achieve the necessary tests to find the temperature distribution during the braking process of the brake system. We obtained high agreement between the results of the new test rig with the numerical results based on the developed model of the brake
... Show More
(4)
(2)
(58)
(55)
to evaluate their suitability for industrial applications. Structural, mechanical, thermal, and surface analyses were performed to determine the influence of blend composition. The results showed that the 60/40 (HDPE/LDPE) blend exhibited superior mechanical performance, including tensile strength, impact resistance, and hardness, while the 80/20 blend demonstrated higher thermal stability and morphological uniformity. The results obtained demonstrate the potential for using HDPE/LDPE blends in many areas, including packaging, insulation, and engineering products that require a balance between durability and thermal stability. They also suggest their potential future application in agricultural irrigation pipes, which require highly reliabl
... Show More
(1)
A field experiment was carried out at the research station of the College of Agriculture - Wasit University / Kut, during the fall season 2021 in soil with texture (sandy mixture) using the RCBD design in the arrangement of splintered plates and with three replications, to study the effect of spraying different combinations of organic emulsion (Appetizer) and NPK nano fertilizer with urea fertilizer on the growth of synthetic cultivars of yellow corn. The main panels included three synthetic varieties of yellow corn (Fajr1, Sumer and Baghdad3), which symbolized by (V1,V2,V3) in sequence, while the secondary panels included five fertilization treatments in which mineral fertilizer (urea) was used 46% nitrogen with the full recomme
... Show MoreIn this study, polymeric coating was developed by incorporating nano graphene in the polymer blend with applications to oil storage tanks. The oil storage tanks samples were brought from the oil Pipeline Company / Doura refinery in Baghdad. The coating polymer was formed with a blend (epoxy resin and repcoat ZR). The proportion of mixing the mixture was 3:1:1 epoxy resin 21.06 gm: repcoat ZR 10.53 gm: hardener 10.53 gm. The blend/graphene was prepared using in stui-polymerization method with different weight percentage 1, 3, 5, and 7 wt % added to blend. The resulting solution was put in a glass tube on a magnetic stirrer for one hour at a temperature of 40 °C. The result of contact angle and water absorption the best ratio of 3wt
... Show More
(2)
Coupling reaction of 2-amino benzoic acid with the 8-hydroxy quinoline gave the azo ligand (H2L): 5-(2-benzoic acid azo )-8-hydroxy quinoline.Treatment of this ligand with some metal ions (CoII, NiII and CuII ) in ethanolic medium with a (1:2) (M:L) ratio yielded a series of neutral complexes with general Formula[M(HL)2],where: M=Co(II), Ni(II) and Cu(II), HL=anion azo ligand (-1).The prepared complexes were characterized using flame atomic absorption,FT-IR and UV-Vis spectroscopic methods as well as magnetic susceptibility and conductivity measurements.
New Schiff base ligand 2-((4-amino-5-(3, 4, 5-trimethoxybenzyl) pyrimidin- 2-ylimino) (phenyl)methyl)benzoic acid] = [HL] was synthesized using microwave irradiation trimethoprim and 2-benzoyl benzoic acid. Mixed ligand complexes of Mn((ІІ), Co(ІІ), Ni(ІІ), Cu(ІІ), Zn(ІІ) and Cd(ІІ) are reacted in ethanol with Schiff base ligand [HL] and 8-hydroxyquinoline [HQ] then reacted with metal salts in ethanol as a solvent in (1:1:1) ratio. The ligand [HL] is characterized by FTIR, UV-Vis, melting point, elemental microanalysis (C.H.N), 1H-NMR, 13C-NMR, and mass spectra. The mixed ligand complexes are characterized by infrared spectra, electronic spectra, (C.H.N), melting point, atomic absorption, molar conductance and magnetic moment me