The study included adding antimony oxide to mixtures of coating metal surfaces (Enameling), after it was selected ceramic materials used in the coating metal pieces of the type of steel and cast iron in two layers. The first is called a ground coat and the second is a cover coat.
Ceramic materials layer for ground coat have been melted down in
platinum crucible at a temperature of 1200oC to prepare the glass
mixture (Frit). It was coated on metals at a temperature of 780oC for
two minutes, while the second layer was prepared glass mixture
(Frit) at a temperature of 1200oC, but was coated at a temperature of
760oC for two minutes.
Underwent tests crystalline state of powders (Frits) and enameled samples using X-ray di

The technique of plant tissue culture has been used to In vitro micropropagation of Spilanthes acmella (L.) Murr. It is an ornamental and medicinal plant not cultivated in Iraq. Seeds were sterilized and cultuared on full strength Murashige and Skoog medium(1962)(MS). Naphthalene acetic acid (NAA), 6- furfuryl aminopurine (Kin.) growth regulators were used at the Initiation stage.The combination between IAA and Kin. was used in multiplication stage. IAA was used for rooting the shoots. Results showed that 1.5% sodium hypochlorite for 15 min was very effective for disinfecting and survival. Nodes exhibited relatively highest response as compared with apical meristems and leaflets culture. Supplying the culture medium with 1 mg/L.

Background: The aim of this in vitro study was to evaluate and compare the effect of preheating microleakage among three different filler size composites which include Filtek^tm Z250 micro hybrid, Z250^xt Nano hybrid and nanocomposite Z350^xt.  in Class II cavity preparation .

Materials and methods: sixty maxillary first premolars were prepared with class II cavities. Samples were divided into three groups according to material used    group A (FiltekZ250 micro hybrid). Group B(Z250^xt Nano hybrid). Group C (nanocomposite Z350^xt)and each group divided into two subgroups of ten teeth according to temperature of  composite:

t-Self-Compacting Concrete (SCC) reduces environmental noise and has more workability. This research presents an investigation of the behavior of SCC under mechanical loading (impact loading). Two types of cement have been used to produce SCC mixtures, Ordinary Portland Cement (OPC) and Portland Limestone Cement (PLC), which reduces the emission of carbon dioxide during the manufacturing process. The mixes were reinforced with Carbon Fiber Reinforced Polymer (CFRP) which is usually used to improve the seismic performance of masonry walls, to replace lost steel reinforcements, or to increase column strength and ductility. Workability tests were carried out for fresh SCC. Prepared concrete slabs of 500×500×50mm were tested for lo

Background: Decalcification of surface enamel adjacent to fixed orthodontic appliances, in the form of white spot lesions, is a wide spread and familiar well-known side effect of orthodontic treatment. The present study was carried out to evaluate the effect of enamel protective agent (Clinpro white varnish) on shear and tensile bond strength of Dentaurum orthodontic stainless steel brackets by using 3M Unitek and Ormco as orthodontic adhesive agents. Materials and methods: Sixty-four extracted human upper first premolar teeth were selected and randomly divided into two groups with 32 teeth each, representing the shear and tensile bond strength testing groups. Then according to the type of bonding adhesive and the addition of Clinpro before

Background: One of the drawbacks of vital teeth bleaching is color stability. The aim of the present study was to evaluate the effects of tea and tomato sauce on the color stability of bleached enamel in association with the application of MI Paste Plus (CPP-ACPF). Materials and Methods: Sixty enamel samples were bleached with 10% carbamide peroxide for two weeks then divided into three groups (A, B and C) of 20 samples each. After bleaching, the samples of each group were subdivided into two subgroups (n=10). While subgroups A1, B1 and C1 were kept in distilled water, A2, B2, and C2 were treated with MI Paste Plus. Then, the samples were immersed in different solutions as follow: A1 and A2 in distilled water (control); B1 and B2 in black

Background: This study was formulated to compare the effect of 5%hydrofluoric acid in comparison to 37%phosphoric acid with and without the application of silane on bond strength of composite to porcelain. Materials and Methods: Specimen preparation was divided in to two phases, metal-disks fabrication (8mm-diameter and 4mm-thickness) and ceramic veneering. Thirty two specimens were prepared, sandblasted with 50 μm aluminum oxide, and divided into four groups of eight samples. Groups I and III were etched with 37%phosphoric acid while groups II and IV were etched with 5%hydrofluoric acid; and groups I and II were silaneted while groups III and IV were not. Heliobond, and resin composite were applied to each specimen using a plastic transpa

Background: The mechanical properties of 3D-printed denture base resins are crucial factors for determining the quality and performance of dentures inside a patient’s mouth. Tensile strength and diametral compressive strength are two properties that could play significant roles in assessing the suitability of a material. Although they measure different aspects of material behavior, a conceptual link exists between them in terms of overall material strength and resilience. Aim: This study aims to investigate the correlation between tensile strength and diametral compressive strength after incorporating 2% ZrO2 nanoparticles (NPs) by weight into 3D-printed denture base resin. Methods: A total of 40 specimens (20 dumbbell-shaped and

Background: Calcium hydroxide and calcium-silicate materials used as direct pulp capping materials. The aims of this in vitro study is to compare among these materials in, the calcium ion release and pH change in soaking water after immersion of materials’ specimens in deionized water. Also Solubility and water sorption of materials’ specimens measured after soaking time. Calcium-silicate materials used were Biodentine, TheraCal and MTA Plus. Materials and methods: Four materials used in this study; Urbical lining (as control group), Biodentine, TheraCal and MTA Plus. Ten discs fabricated from each tested material, by using plastic moulds of 9 mm diameter and 1 mm thickness. Each specimen was immersed in 10 ml of d