The study was carried out by reinforcing the resin matrix material

which was (Epoxy- Ep828) by useing Kevlar fibers and glass fibers type (E-gl ass) both or them in the form of woven roving and poly propylene tlbcrs  in  the form chopped  strand  mats.  wi th (30%)  volume  fraction. Some mechan i cal  properties of the were prepared composite specimens U ltraviolet   radiation  were  stuied   after   being  subjected  to  different weathering conditi ons i ncluded. Compression and hardness testing were carried out using Briel! method so as to compare between composite behavior i n the environments previously mentioned .

 <

Ultrasonic pulse echo measurements on porous alumina as ceramic

material with porosities ranging from (20-40)% showed effect of volume

fraction of porosity on both thermal and elastic properties. A quadratic relationships, by using a least squares method, is deduced for the dependence of the shear velocity, longitudinal velocity, shear modulus, Young's modulus,  bulk  modulus, Poisson 's ratio, Debye temperature, specific heat, and thermal conductivity on the total  porosity. By these relationships,  the  thermal  and  elastic  properties  results  of  pore-free alumina  were  calculated.  The  elastic  properties  results  of  

A Copper- Mullet walled Carbon Nanotube Cu/MWCNT composite coatings prepared by direct and pulse electrodeposition with various contents of MWCNT particles, using electrodeposition method from acidic sulfate bath. The effect of the current density, pulse frequency and  particle loading (PL) of MWCNT particle in the electrolyte on the morphology and volume fraction Vol% of MWCNT in deposit were investigate. The experimental results indicated that the depositing condition affect on the microstructure of deposited copper and MWCNT Vol% in deposit. Also, the Vol% of MWCNT increases in deposit with particle loading (PL) increasing in the bath and increased with increased current density. Increasing MWCNTs in electrolyte produced increase

   This study included preparation for the unsaturated polyester samples before and after reinforced by the Alumina oxide powder of different volume fraction amounting (2%,4%,6%).    And this research included the study of some of mechanical properties such as (Hardness,compressive,wear).     The results showed that the increase of the hardness and compressive strength after the reinforced and the increase with the volume fraction increase.   As the wear test shows that the wear rate increases with applied load increase(5,10,15) from  (10.6-18.6) gm/cm befor reninforced and from(5.4-15.2)gm/cm,(4.7-12.9)gm/cm,(48.1)gm/cm,after reinforced from the different volume fraction, and t

Porcelain is one of the most important ceramic materials with a wide range of traditional and technical applications. Since most mixtures of porcelain have a high sintering temperature, bentonite has been added in this research to improve the characteristics of sintering and burning. The porcelain mixture consisted of the following Iraqi raw materials: 30% wt kaolin, 30 wt% non-plastic clay (grog), 10% wt sodium feldspar, 10 wt% potassium feldspar and 20 wt% flint. After the mechanical mixing process and transfer the powder mixture to the slurry by adding distilled water, then different weight percentage of the sodium bentonite(0, 2.5, 5, 7.5 and 10) wt% was added. The specimens were prepared by using the solid casting m