Coblatcomplex has been prepared by reaction between C16H19N3O3S (L) as ligand and metal salt (II). The prepared complex were characterized by infrared spectra, electromic spectra, magnetic susceptibility, molar conductivity measurement and metal analysis by atomic absorption and (C.H.N) analysis. From these studies tetrahedral geometry structure for the complex was suggested. The photodegredation of complex were study using photoreaction cell and preparednanoTiO2 catalyst in different conditions (concentration, temperatures, pH).The results show that the recation is of a first order with activation energy equal to (6.6512 kJ /mol).

Supra nanoparticles (submicron) of Chicken bones fibers were used (before and after treated with citric acid solution) as additives  to dental composite with the weight ratios (1%, 2% and 4%). The main mechanical tests represented by hardness, wear resistance and compression strength was carried out on the improvement dental composites.

The addition of treated supra nanoparticles Chicken thigh bones with particles size (300 nm) by weight ratio (1%) to ordinary dental composite resin , significantly improves all of its mechanical properties, in addition to the increase the value of the its  glass transition temperature from  43^oC  to 45.4 ^oC. The techniques X-ray diffraction (XRD), Energy Dispersive Spectr

Coblatcomplex has been prepared by reaction between C16H19N3O3S (L) as ligand and metal salt (II). The prepared complex were characterized by infrared spectra, electromic spectra, magnetic susceptibility, molar conductivity measurement and metal analysis by atomic absorption and (C.H.N) analysis. From these studies tetrahedral geometry structure for the complex was suggested. The photodegredation of complex were study using photoreaction cell and preparednanoTiO2 catalyst in different conditions (concentration, temperatures, pH).The results show that the recation is of a first order with activation energy equal to (6.6512 kJ /mol).

The presence of construction wastes such as clay bricks, glass, wood, plastic, and others in large quantities causes serious environmental problems in the world. Where these wastes can be used to preserve the natural resources used in construction and reduce the impact of this problem on the environment, it also works to reduce the problem of high loads of concrete blocks. Clay bricks aggregate (AB) can be recycled as coarse aggregate and replaced with volumetric proportions of coarse aggregate by ( 5% and 10%), as well as the use of clay brick powder (PB) by replacing its weight of cement (5% and 10%) and reduced in the manufacture of concrete blocks (blocks). Four mixtures will be prepared and tested to learn how to re

16S rRNA gene sequence examination is an effective instrument for characterization of new pathogens in clinical specimens. Akey component of colonization, biofilm formation, and protection of the pragmatic human pathogen Pseudomonasaeruginosais the biosynthesis of the exopolysaccharide Psl.Extracellular polysaccharides,biofilm, are secreted by microorganisms into the neighboring environment and are significant for surface attachment and keeping structural safety within biofilms.Biofilm production is an important technique for the survival of P. aeruginosa,and its association with antimicrobial resistance represents a defy for patient therapeutics. The aim of the current research is to assess the antibiotic resistance manner and distribution

High   Alumina   Glasses   "Alumina   Silicate   Glasses"   was prepared by utilizing powder technology technique. The starting materials are wasted soda-lime glass from an industrial site, Iraqi­ Duekhla raw kaolin and small amounts of potassium carbonates.

X-ray Diffraction and FTIR analysis show complete vitreous glasses are obtained. Increasing Alumina content plays an obvious role in improving physical and mechanical properties of the prepared high  alumina  glass.   In  addition,  the   increased  alumina  content enhanced the dielectric constant and reduced dielectric loss. These results may be interpreted as du

The reinforced fiberglass in cement slurry reflects the effect on its properties compared to usual additives. Fiberglass is typically used in cement slurry design for one or another of the following goals: (Earth earthquake, bearing storage, and with differential stresses, to enhance cement durability and increase its compressive strength). The main goal is to use glass fiber and ground fiberglass to improve the tensile strength and moderate compressive strength significantly. On the other hand, the use of glass fibers led to a slight increase in the value of thickening time, which is a desirable effect. Eleven glass fiber samples and milled glass fiber were used to show these materials' effect on Iraqi cement with (0.125, 0.25, 0.5

In this work, Soda Lime Glass (S.L.G.) powder was used ,as
fluxe in traditional porcelain instead of feldspar. Two ceramics
porcelain were compared; commercial or traditional porcelain that
content of 50wt % kaolin, 25wt % quartz, and 25wt % feldspar.
Feldspar mass was substituted by scraps soda lime glass yielding a
new porcelain composition, to determine the softening points and
then the effect of glass addition on porcelain firing process.
Eight samples, for each patch, were prepared and 8wt % water
was added. The resulting composite blends were then die pressed at
2N, to produce disk specimens with diameter of 1.5 cm, and then
they were sintered at (1000, 1100, 1200, 1250,1300,1350,1400 and
1450) ˚C,

In this work, the effect of different particle size on the nonlinear optical properties of silver nanoparticles in de-ionized water was studied. The experimental observation of the far field diffraction patterns by CCD camera in two and three dimensions. The maximum change of nonlinear refractive index and the relative phase shift were calculated. The self-defocusing technique was used with a continuous-wave radiation from DPSS Blue laser .The wavelength is 473 nm with an output power of 270 mW. All the Ag colloids samples containing the sizes 15, 30, 50, and 70 nm of silver nanoparticles used in the study were chemically prepared. It was found that the nonlinear refractive index is a particle size dependent and of the order of 10-7 cm2/