Iron-Epoxy composite samples were prepared by added
different weight percentages (0, 5, 10, 15, and 20 wt %) from Iron
particles in the range of (30-40μm) as a particle size. The contents
were mixed carefully, and placed a circular dies with a diameter of
2.5 cm. Different mechanical tests (Shore D Hardness, Tensile
strength, and Impact strength ) were carried out for all samples. The
samples were immersed in water for ten weeks, and after two weeks
the samples were take-out and drying to conducting all mechanical
tests were repeated for all samples. The hardness values increased
when the Iron particle concentration increased while the Impact
strength is not affected by the increasing of Iron particles
c

In this study, two types of mixes were adopted by using two grading of coarse aggregate. The practical side of this study was to produce no-fine aggregate concrete by using crushed clay brick aggregates. The durability of the produced concrete and internal sulfate attack was studied.      For durability assessment, it is found that the no-fine concrete made with crushed brick aggregate lost about (15-25) % of its compressive strength after being subjected to 60 cycles of wetting and drying with age 120 days. The curing condition showed that the water curing improved the compressive strength with a rate higher than that when sealed or air dry curing were used. The crushed brick no-fine concrete de

Implementation of Warm Mix Asphalt concrete (WMA) is getting global acceptance due to the restrictions for protecting the environment and the requirements to reduce fuel consumption. In this investigation, two WMA mixtures have been prepared in the laboratory using medium curing cutback (MC-30) and Cationic emulsion asphalt. Hot Mix Asphalt (HMA) was also prepared for comparison. The cylinder specimens (63.5mm) in height and (101.6mm) in diameter were constructed from the mixtures and subjected to indirect tensile strength test to determine the Tensile Strength Ratio (TSR). The cylinder specimens of (101.6mm) in height and (101.6mm) in diameter were also constructed from those mixtures and subjected to static compressive

Corrosion inhibiting admixtures are unique among other methods to protect reinforced concrete from corrosion damage. In this study, the effect of furfural on the fresh and hardened properties of concrete mixes of 35 and 45 MPa compressive strengths as well as the corrosion inhibition of furfural was evaluated. Furfural was added at different dosages (1, 2 and 3% by weight of cement) with and without superplasticizer (HRWR). Different electrochemical measurements were performed (Half-cell potential, Tafel plot and linear polarization resistance). Electrochemical measurements confirmed that furfural dramatically reduces the rate of corrosion; the inhibition efficiencies were 62.7 and 63.8 % due to 3% furfural addition to 35 and 45MPa-concr

The Iraqi houses flattening the roof by a concrete panel, and because of the panels on the top directly exposed to the solar radiation become unbearably hot and cold during the summer and winter. The traditional concrete panel components are cement, sand, and aggregate, which have a poor thermal property. The usage of materials with low thermal conductivity with no negative reflects on its mechanical properties gives good improvements to the thermal properties of the concrete panel. The practical part of this work was built on a multi-stage mixing plan. In the first stage the mixing ratio based on the ratios of the sand to cement. The second stage mixing ratios based on replacing the coarse aggregate quantities with the

We described herein the synthesized and characterized of new bent and liner core compounds containing thiazolidin-4-one ring[XI-XIII] and [XIV-XVI] respectively. These compounds synthesized by sequence reactions starting from reaction resorcinol or hydroquinone with chloracetyl chloride to yield compounds [I] and [II] ,then the later compounds reactant with 4-hydroxybenzylaldehyde to product dialdehyde compounds [III] and [IV] .The Schiff bases compounds[V-VII] and [VIII-X] synthesized from reaction the compound [III] or [IV] with different aromatic amines, while the bent and liner core mesogens containing thiazolidin-4-one ring [XI-XIII] and [XIV-XVI] synthesized from reaction Schiff bases compounds[V-VII] or [VIII-X] with thioglycolic aci

  We described herein the synthesized and characterized of new bent and liner core compounds containing thiazolidin-4-one ring[XI-XIII] and [XIV-XVI] respectively. These compounds synthesized by sequence reactions starting from reaction resorcinol or hydroquinone with chloracetyl chloride to yield compounds [I] and [II] ,then the later compounds reactant with 4-hydroxybenzylaldehyde to product dialdehyde compounds [III] and [IV] .The Schiff bases compounds[V-VII] and [VIII-X] synthesized from reaction the compound [III] or [IV] with different aromatic  amines, while the bent and liner core mesogens containing thiazolidin-4-one ring [XI-XIII] and [XIV-XVI] synthesized from reaction Schiff bases compounds[V-VII] or  [VIII-X]