Ethanol as a solvent, a precursor of titanium isopropoxide and a stabilizer of either hydrochloric acid or ammonium hydroxide was used to prepare a titanium dioxide aqueous solution. The aqueous solutions with different values of pH and the morphology of the resultant reaction of the nanoparticles of titanium dioxide were investigated. The X-ray diffraction showed that at low temperatures and with acidic solutions, rutile structures are more favorable to grow on titanium dioxide synthesized, while at low and average temperatures and with base solutions, anatase phase is more pronounced. The crystalline form and the re-confirmation of the crystallite size growth were observed by the scanning electron microscopy. The atomi

In this research, a novel thin film Si-GO10 and nanopowders Si-GO30 of silica-graphene oxide (GO) composite were prepared via the sol–gel method and deposited on glass substrates using spray pyrolysis. X-ray diffraction (XRD) results showed a relatively strong peak in the graphite layer that corresponds to the (002) plane. Transmission electron microscope (TEM) images showed that SiO2 nanoparticles were randomly distributed on the surface of GO plates, and the particle size in these nanopowders was below 50 nm. Field emission scanning electron microscopy (FESEM) analysis demonstrated that silica nanoparticles on the surface of GO plates exhibited almost spherical and rod-like nanoparticle shape, which in turn confirmed the formation of Si

by in situ polymerization of aniline monomer, conducting polyaniline (PANI) nanocomposites containing various concentrations of carboxylic acid functionalized multi-walled carbon nanotubes (f-MWCNT) were synthesized. The morphological and electrical properties of pure PANI and PANI /MWCNT nanocomposites were examined by using Fourier transform- infrared spectroscopy (FTIR), X-ray diffraction (XRD) and Atomic Force Microscopy (AFM) respectively. FTIR spectra shows that the carboxylic acid groups formed at the both ends of the sidewalls of the MWCNTs. The aniline monomers were polymerized on the surface of MWCNTs, depending on the -* electron interaction between aniline monomers and MWCNTs and hydrogen bonding into interaction between t

Ethanol as a solvent, a precursor of titanium isopropoxide and a stabilizer of either hydrochloric acid or ammonium hydroxide was used to prepare a titanium dioxide aqueous solution. The aqueous solutions with different values of pH and the morphology of the resultant reaction of the nanoparticles of titanium dioxide were investigated. The X-ray diffraction showed that at low temperatures and with acidic solutions, rutile structures are more favorable to grow on titanium dioxide synthesized, while at low and average temperatures and with base solutions, anatase phase is more pronounced. The crystalline form and the re-confirmation of the crystallite size growth were observed by the scanning electron microscopy. The atomic force micr

In this research, Argon gas was used to generate atmospheric plasma in the manufacture of platinum nanomaterials, to study the resultant plasma spectrum and to calculate the cellular toxicity of those manufactured nanomaterials. This research is keen on the generation of nonthermal atmospheric pressure plasma using aqueous platinum salts (H₂PtCl₆ 6H₂O) with different concentrations and exposure of cold plasma with a different time period used to produce platinum nanoparticles, to ensure typical preparation of nanoparticles. Visible UV and X-rays were performed for this purpose, and the diameter of the system probe was (1[Formula: see text]mm) with the Argon gas flow of

Bioavailability is the objective for an optimum formulation. The target of the analysis is to maximize both the fluidity and disintegration profile of class II weakly compounds that are water-soluble. Anti-dyslipidemia drug rosuvastatin calcium (RC) (bioavailability 20%) through formulating as nanofibers (NFs) using electrospinning (ES) technology. Twenty formulas were prepared, and different polymers and polymer combinations with various concentrations were used such as polyethylene oxide (PEO) polyvinyl pyrrolidine (PVPK-30), and hydroxypropyl methylcellulose (HPMC). Three distinct groups of maximum parameters, including polymeric solution, electrospinning method, and ambient parameter, are capable of influencing the creation alon

Meloxicam is a non-steroidal anti-inflammatory drug. It is practically insoluble in water. It is associated with gastrointestinal side effects at high doses on long  term treatment. The aim of this investigation to formulate and evaluate gellified nanoemulsion of meloxicam as a topical dosage form to enhance meloxicam therapeutic activity and reduce systemic side effect.

The pseudo ternary phase diagrams were made, including  the oil mixture which is composed of almond oil and peppermint oil at a ratio (1:2), variable surfactant mixture (S mix) which are tween 80 and ethanol at ratios of (1:1, 2:1, 3:1, and 4:1) and double distilled water. Slow dripping of double distilled water to the combination  of the oil mixtu

Allopurinol derivative were prepared by reacting the (1-chloroacetyl)-2-Hydropyrazolo{3,4-d}pyrimidine-4-oneiwith 5- methoxy- 2-aminoibenzothiazoleiunder certain conditions to obtain new compound ( N- (2-aminoacetyl (5-methoxy) benzothiazole -2yl) (A4), Reaction of 5-(P-dimethyl amine benzene)-2-amino-1,3,4- oxadiazole in the presence of potassium carbonate anhydrous to yield new compound (N-(2- aminoacetyl-5-(P-dimethyl amine benzene )-1,3,4-oxadiazoles-2-yl)(A30) and Azo compound (N-(5-(Azo-2-hydroxy-5-amino benzene)-1,3-Diazol-2yl)Allopurinol(A46). The structure of prepared compounds were confirmed by (FT-IR) technique and their physical properties. The synthesized compounds were tested for cytotoxicity, Xanthine oxidase inhibiti

         Allopurinol derivative were prepared by reacting the (1-chloroacetyl)-2-Hydropyrazolo{3,4-d}pyrimidine-4-oneiwith 5- methoxy- 2-aminoibenzothiazoleiunder certain conditions to obtain new compound  ( N- (2-aminoacetyl (5-methoxy) benzothiazole -2yl) (A₄), Reaction of 5-(P-dimethyl amine benzene)-2-amino-1,3,4- oxadiazole in the presence of potassium carbonate anhydrous to yield new  compound (N-(2- aminoacetyl-5-(P-dimethyl amine benzene )-1,3,4-oxadiazoles-2-yl)(A₃₀) and Azo compound (N-(5-(Azo-2-hydroxy-5-amino benzene)-1,3-Diazol-2yl)Allopurinol(A₄₆). The structure of prepared compounds were confirmed by (FT-IR)