Platinum (Pt) supported on sulfated zirconia (SZ) and HY-zeolite as a solid acid catalyst was synthesized successfully for isomerization reaction using precipitation and impregnation method. The physicochemical properties of the catalyst were characterized using various techniques including X-ray diffraction (XRD), Fourier transformation infra-red spectroscopy (FTIR), BET Surface area and pore volume, and Field Emission Scanning Electron Microscopy (FESEM).  The prepared composite catalyst Pt/SZ-HY consisted of high Bronsted acidic sites and Lewis acidic sites. The addition of multi-walled carbon nanotubes (MWCNTs) to SZ increased the surface area and pore volume, resulting in smaller crystal sizes and a narrower particle size dist

Worldwide attention is being focused on  nanocrystalline  zeolites  and they are replacing conventional ones due to their pronounced potential in many fields. In this study, NaY zeolite has been prepared hydrothermally using sol –gel method and modified to the proton type by ion –exchange process. Characterization is made using X-ray diffraction (XRD), thermogravimetric analysis (TGA),  Fourier transform infrared spectroscopy (FTIR),  Atomic force microscopy (AFM), Brunauer –Emmet- Teller (BET) nitrogen adsorption method, Ammonia Temperature programmed desorption (NH₃-TPD) and Scanning electron microscopy( SEM).  The effect of aging time, silica to alumina ratio is studied and the results sh

Abstract

 Nano-crystalline ZSM-5 zeolite was synthesized by hydrothermal method using chelating agent and two gel compositions:Compositionɪ:Al₂O₃:86SiO₂:5.5TPA:12.7Na₂O:3.4Trien:3320H₂O.Compositionɪɪ:Al₂O₃:68SiO₂:5.4TPA:10Na₂O:2.6Trien:2626H₂O.Study of hydrothermal reaction factors on characteristics of nano- sized zsm-5 has been carried on ,among them are crystallization temperature, crystallization time and concentration of template ( TPAOH ) solution. Synthesis was accomplished in PTFE lined autoclave ( reactor ) . The product were characterized by X-ray diffraction ( XRD ),Atomic force microsc

In the present work, zeolite Y has been synthesized successfully by sol-gel method.Zeolite was synthesized by crystallization of the final gel which consist from seeding and feed stock gels at  85 ^oC. HY zeolite was prepared by an ion exchange process with ammonium chloride solution and then loaded with different percentages of  platinum and titanium by the wet - impregnation method.

X-ray Diffraction (XRD), X-ray Florescence (XRF), Scanning Electron Microscopy (SEM), BET surface area and, Crushing strength were used to characterize the synthesized and prepared catalysts . Results showed high crystallinity  90%  with silica to alumina ratio 5 for HY, high surface area of 600 m²/g and pore

Modifying of HY/Zeolite is by loading nickel for applying catalyst in thermal catalytic cracking of furfural extract-40 from the lubricating base oil unit. The study involved the characterizing of HY-zeolite and promoted catalyst with nickel by X-ray diffraction analysis, Scanning electron microscopy (SEM), BET (Brunauer, Emmett, and Teller), and infrared ray analyses FTIR. The catalytic thermal cracking tubular reactor with a fixed bed with two type catalysts; HY/zeolite and Ni HY/zeolite, individually at a temperature of 580^oC with LHSV 5h^-1 was investigated. The results indicated that increase the conversion of catalytic cracking of furfural extract-40 also increases the yield of useful petroleum

Zeolite Y nanoparticles were synthesized by sol - gel method. Dffirent samples using two silica sources were prepared.
Sodium metasilicate (Na2SiO3) (48% silica) and silicic acid silica (H2SiO3) (75% silica) were employed as silica
source and aluminum nitrate (Al(NO3)3.9H2O) was the aluminum source with tetrapropylammonium hydroxide
(TPAOH) as templating agent.
The synihesized-samples were characterized by X-ray diffraction, showed the requirement of diffirent aging time for
complete crystallization to be achieved. Transmission Electronic Microscope (TEM) images, showed the particles were
in the same range of 30 - 75 nm. FT-IR spectroscory, showed the synthesized samples having the zeolite Y crystal
properties. The i