The petroleum industry faces a significant problem in enhanced oil recovery (EOR) from carbonate reservoirs because of their mostly oil-wet character, which restricts hydrocarbon extraction. To better understand how surfactant-polymer techniques can enhance oil recovery, this study investigates the effectiveness of polyvinyl alcohol (PVA) as a stand-alone agent and the function of ionically modified smart water on carbonate properties. The study focuses on its effect on critical parameters essential for effective oil displacement and recovery, such as wettability alteration, interfacial tension, and surface tension (ST) using different brines (smart water). The ability of the polymer PVA to lower interfacial and surface tensi

When a vehicle is left parked in the sun for an extended period, the gathered heat causes damage to several interiors within the cabin and causes discomfort for people and animals left inside the car. In the present work, the effect of the orientation of a parked white minibus on temperature distribution and cooling load calculation is studied experimentally in an open environment. Two different cases were studied facing south and facing east. For several hours, the temperature inside the car cabin had been monitored and measured at five separate locations. The cooling load calculations are carried out based on the experimental measurements. The results show that the overheating of parked cars always happens as a result

The study is concern on determine the effect of different temperatures (25, 28, 30 and 370C), and different pH values (4.5, 5.5, 6 and 8) on the radial growth (mm) of 15 dermatophyte isolates (Microsporum canis 7, Trichophyton rubrum 5, Trichophyton mentagropyhtes 3). The specimens for the current study were collected from nail infections in patients with different type of leukemia whom admitted at Baghdad Educational Hospital, 7th floor. The result revels that the optimum temperature for radial growth was 300C then 280C for all isolates, while the optimum pH for all isolates was 6.

The CdSe pure films and doping with Cu (0.5, 1.5, 2.5, 4.0wt%) of thickness 0.9μm have been prepared by thermal evaporation technique on glass substrate. Annealing for all the prepared films have been achieved at 523K in vacuum to get good properties of the films. The effect of Cu concentration on some of the electrical properties such as D.C conductivity and Hall effect has been studied.
It has been found that the increase in Cu concentration caused increase in d.c conductivity for pure CdSe 3.75×10-4(Ω.cm)-1 at room temperatures to maximum value of 0.769(Ω.cm)-1 for 4wt%Cu.All films have shown two activation energies, where these value decreases with increasing doping ratio. The maximum value of activation energy was (0.319)eV f

Films of CdSe have been prepared by evaporation technique with thickness 1µm. Doping with Cu was achieved using annealing under argon atmosphere . The Structure properties of these films are investigated by X-ray diffraction analysis. The effect of Cu doping on the orientation , relative intensity, grain size and the lattice constant has been studied. The pure CdSe films have been found consist of amorphous structure with very small peak at (002) plane. The films were polycrystalline for doped CdSe with (1&2wt%) Cu contents and with lattice constant (a=3.741,c=7.096)A°, and it has better crystallinty as the Cu contents increased to (3&5wt%) Cu. The reflections from [(002), (102). (110), (112), and (201)]planes are more prominen