Na⁺/K⁺-ATPase is a prevalent enzyme that maintains the Na⁺ and K⁺ gradients across the cell membrane by transporting three Na⁺ out and two K⁺ into the cell, the aim of this study  is to provide detailed mechanistic insights, potentially with important effects on physiological regulation of active Na and K transport in tissues of Aerobic Thyroid Patient. Thyroid tissues were obtained from a 35 year old patients, the operation was carried out at the Al-Hadi Specialist Hospital in Samarra city, the sample was stored at -20^ºC until used. The purification protocol included Salt Precipitation, Ion Exchange Chromatography, Gel Filtration and E

The marshes form large areas in southern Iraq, which are large water bodies, covered by reeds and papyrus plants. The marshes are characterized by distinctive physical elements, which have given them a unique and unique identity that can be clearly distinguished by the physical pattern. The physical environment derives its identity through a group Of inputs that interact with each other and represent both cultural and social inputs of the most important inputs that affect the formation of identity, and in the physical environment of the Marshlands many of the symbols that are associated with the collective memory of individuals, these symbols have value in the community Thus, the preservation of these symbols and inherited from one gener

This study examined the adsorption behavior of anionic dye (orange G) from aqueous solution onto the raw and activated a mixture of illite, kaolinite and chlorite clays from area of Zorbatiya (east of Iraq).The chemical treatment involved alkali and acid activation. The alkali activation obtained by treated the raw clay (RC) with 5M NaOH (ACSO) and the acid activation founded by treated it with 0.25M HCl (ACH) and 0.25M  (ACS). The thermal treatment carried out by calcination the produce activated clay at 750^oC for acid activation and 105^oC for alkali activation. Batch

Iron-Epoxy composite samples were prepared by added
different weight percentages (0, 5, 10, 15, and 20 wt %) from Iron
particles in the range of (30-40μm) as a particle size. The contents
were mixed carefully, and placed a circular dies with a diameter of
2.5 cm. Different mechanical tests (Shore D Hardness, Tensile
strength, and Impact strength ) were carried out for all samples. The
samples were immersed in water for ten weeks, and after two weeks
the samples were take-out and drying to conducting all mechanical
tests were repeated for all samples. The hardness values increased
when the Iron particle concentration increased while the Impact
strength is not affected by the increasing of Iron particles
c

Thin films of CdS:Cu were deposited onto glass substrate temperature 400 °c. The optieal properties have been studied for Cds doped with (1,3, 8) wt% of Cu before and after Gamma irradiation. It was found that the irradiation caused an ( Frenkel defects) where the atom is displaced from its original site leaving vacancy and forming on interstitial atom. It was found the irradiation caused an absorption edge shifting towards long wavelength as a result of the increasing of Cu concentration.

In this paper we have studied the optical properties of CuBr thin

films.  Different  sample  thicknesses  have  been  prepared  by  using thermal evaporation  technique with 14.4 runlsec as the average deposition rate and 1 00°C as the substrate temperature.

The composites were manufactured and study the effect of addition of filler (nanoparticles SiO2 treated with silane) at different weight ratios (1, 2, 3, 4 and 5) %, on electrical, mechanical and thermal properties. Materials were mixed with each other using an ultrasound, and then pour the mixture into the molds to suit all measurements. The electrical characteristics were studied within a range of frequencies (50-1M) Hz at room temperature, where the best results were shown at the fill ratio (1%), and thermal properties at (X=3 %), the mechanical properties at the filler ratio (2%).