The study of surface hardness, wear resistance, adhesion strength, electrochemical corrosion resistance and thermal conductivity of coatings composed from sodium silicate was prepared using graphite micro-size particles and carbon nano particles as fillers respectively of concentration of (1-5%), for the purpose of covering and protecting the oil distillation towers. The results showed that the sodium silicate coating reinforced with carbon nano-powder has higher resistance to stitches, mechanical wear, adhesive and thermal conductivity than graphite/sodium silicate composite especially when the ratio 5% and 1%, the electrochemical corrosion test confirmed that the coating process of stainless steel 304 lead to increasin

 Powder of silver nanoparticles was prepared by Sol - Gel method successfully using silver nitrate , (AgNO3) gesture is added to sodium citrate (C6H5O7Na3) as a reducing agent and by using  Magnetic Stirrer to mix the solutions and heated then using centrifuge machine to separate the silver nanoparticles from solution .It is then dried in an oven at a temperature 40oC for 24 hours.     Structure characteristics was studied , the synthetic silver powder was prepared through the use of an (XRD). Results showed the composition of silver nanoparticles is a (fcc) and a constant lattice (4.086 ± 0.006 Ã…) by comparing it with standard tables (JCPDS) which is found perfectly matched to file with a number 04-0783, which

Abstract

Personality is one of the most important elements that should be developed in university student. Thus, we have to develop the positive traits and neutralize the negative traits of students as well as we have to pay attention to the level of student achievement at the same time, the researcher designed a scale to measure the traits of study sample. The research come out with a number of recommendations and proposals, the most important of which Enhancing the positive characteristics of university students in order to reach them to the level of mature personality with mental health. Enhancing the positive role of the high level of achievement by motivating the stude

Experimental results on harmonic distortions in 13.56 MHz RF Argon glow discharge using different grounded electrodes areas and electrodes spacing are presented. The experiment is carried out at four pressure values. RF power values used are between 20 and 90 watts. The results indicate significant increase in distortions at two specific values of the cone angle enclosing the two electrodes within its geometrical volume. The computation of the cone head angle gave the symmetry discharge or asymmetry as well as when the angle is small the condition is near symmetry discharge associated with decrease in the nonlinearity.

      The current study involves an experimental investigation of plasma main parameters of a DC discharge with a hollow cathode (HCD) geometry in air using apertures of different diameters from the hollow cathode (1, 1.5, 2, and 2.5 cm). A tiny Langmuir probe is used to investigate the plasma properties. The HCD was operated at constant power of 12.4 W and gas pressures ranging between 0.1 to 0.8 torr. It was observed that the operational conditions strongly affect the electron temperature and density, while the hollow cathode diameter has not much influence. The main important observation was that at relatively high air pressure (>0.4 torr) two electron temperatures were obtained, while at relatively low pressure (<0.4 torr)

Low-pressure capacitively coupled RF discharge Ar plasma has been studied using Langmuir probe. The electron temperature, electron density and Debay length were calculated under different pressures and electrode gap. In this work the RF Langmuir probe is designed using 4MHz filter as compensation circuit and I-V probe characteristic have been investigated. The pressure varied from 0.07 mbar to 0.1 mbar while electrode gap varied from 2-5 cm. The plasma was generated using power supply at 4MHz frequency with power 300 W. The flowmeter is used to control Argon gas flow in the range of 600 standard cubic centimeters per minute (sccm). The electron temperature drops slowly with pressure and it's gradually decreased when expanding the electro