In this study porcelain was prepared by using composition consisting of raw materials with in following fractions , 50% kaolin , 25% feldspar, and 25% silica( SiO2) tested by XRay diffraction (XRD) method .Study the effect additives at different concentration from zirconia (ZrO2) (2,5,10,15,20) Wt% on some physical properties of porcelain, the sample is prepared by the conventional manufacturing method , It is found that some physical properties of porcelain changes considerably with the substituent sample, It was found that the increase of zrconia (ZrO2) additive of all our sample produce. Increasing in dielectric constant and bulk density and decreasing with open porosity and dielectric loss tangent

In this research study Hardness (shore D), Water absorption,
Flexural, Impact Test, and Fracture Toughness of polymer nano
composites. The polymer nano composites based on unsaturated
polyester resin reinforced with Kevlar fibers (K.F). The samples are
attended by hand lay – up method according to (Rule mixture) for
various volume fractions of unsaturated polyester resin, fiber and
carbon nanotube. The polyester resin was matrix strengthened with
3% volume fraction from Kevlar fiber and (0.5%, 1%, 1.5%, 2%)
volume fractions of carbon nanotube. The water absorption, hardness
(shore D), flexural test, impact test and toughness fracture properties
were studied. Results showed that the water absorption increas

Soil defilement with "raw petroleum" is a standout amongst the most across the board and genuine ecological issues going up against both the industrialized and oil country like Iraq. Along these lines, the impact of "raw petroleum" on soil contamination is one of most critical subjects that review these days. The present examination expects to research "unrefined oil"effectson the mechanical and physical properties of clayey soils. The dirt examples were acquired from Al-Doura area in Baghdad city and arranged by the "Brought together Soil Grouping Framework (USCS)" as silty mud of low pliancy (CL). Research center tests were done on contaminated and unpolluted soil tests with same thickness. The dirtied tests are set up by blending

NH₃ gas sensor was fabricated based on deposited of Functionalized Multi-Walled Carbon Nanotubes (MWCNTs-OH) suspension on filter paper substrates using suspension filtration method. The structural, morphological and optical properties of the MWCNTs film were characterized by XRD, AFM and FTIR techniques. XRD measurement confirmed that the structure of MWCNTs is not affected by the preparation method. The AFM images reflected highly ordered network in the form of a mat. The functional groups and types of bonding have appeared in the FTIR spectra. The fingerprint (C-C stretch) of MWCNTs appears in 1365 cm^-1, and the backbone of CNTs observed at 1645 cm^-1. A homemade sensi

The aim of this work is to study the effect of mud compositions on it’s rheological behavior under high temperature conditions. Seventeen samples of five types of water base mud in which (fresh water bentonite mud. Lignosulphonate mud, gypsum mud, polymer mud, and salt saturated mud) were tested with different temperatures using the fann viscometer model 50-c. All the tested samples, except the fresh water bentonite mud, have the same trend reduction in both plastic viscosity and yield point with increasing temperature. Six rheological models has been adapted: Bingham plastic, power law, Casson model represent the laboratory data accurately  

The study concern with the preparation of three type of mixtures; which are prepared from different percentage of polyvenil Butyral, Di-n-butyl phathalate and paraffin wax pastillated. The solvent used is Xylolzul analyses. After washing, Drying and milling the kaolin Dukhla, as a matrix in this study, and by using sieving Tech. The range of particle size used is less than and less than as a mesh batch. The added percentage from prepared mixture were 5% and 10% to 95% and 90% of the matrix respectively. Then disk samples were prepared by using a compaction pressure with heating. After cooling and drying the samples were undergo heat treatment in the range of (1250 – 1350) oC. The measurement of shrinkage and Dielectric properties sho