The present work studies the mechanical properties of SiO2 μPs, and NPs in St/PVA blends. The samples were prepared by casting method as PVA, St/PVA blends at different concentrations (30, 40, 50, and 60 %). DSC and TGA tests were carried out to the samples evolved. The result showed a single glass transition temperature (Tg) for all St /PVA blends that was attributed to the good miscibility of the blends involved. It was found that (Tg) decrease with starch ratio increase. It was seen that (PVA) of (Tg=105 oC); The glass transition temperature which was decrease with starch ratio that was attributed to glass transition relaxation process due to micro-Brownian motion of the main chain back bond. The endothermic peak at 200 oC was attrib

The research aims to identify: 1-Designing a test to measure the movement compatibility of the eye and the leg for the students of the Faculty of Physical Education and Sports Sciences, Samarra University. 2-Codification (setting scores and standard levels) for the results of the motor compatibility test for the eye and the leg for students of the Faculty of Physical Education and Sports Sciences, Samarra University. The researchers reached the some following conclusions: 1-A test to measure the movement compatibility of the eye and the leg for the students of the Faculty of Physical Education and Sports Sciences. 2-There is a discrepancy in the standard levels of the research sample.

م. د. ولاء طارق حميد, Al. Qadisiya journal for the Sciences of Physical Education, 2017

Thyroid hormones, triiodothyronine (T3) and thyroxin (T4) play an important role in growth, development, and physiology of the kidney. The kidney has a central role in metabolism and clearance of these hormones as well as thyroid – stimulating hormone (TSH). Chronic renal failure (CRF) is a state of irreversible deceleration in renal function results in alterations in internal milieu, which affects the synthesis and secretory rate of hormones. To evaluate the thyroid hormone levels in non-dialyzed patients with chronic renal failure (CRF); 24 patients with CRF aged 30-70 years, mean±S.d. (48.458 ± 13.569) and 48 healthy volunteers who served as controls aged 30-70 years (43.104 ± 12.387) were studied for their thyroid function status u

the shear strength parameters of the treated and untreated gypsum soil under the effect of four soaking and drying cycles has studied in this paper, moreover examined the effect of wetting and drying cycles on the collapse potential of the soil and comparing between the behavior of the treated and untreated gypsum soil under the effect of the two conditions. Gypsum soil sample brought from Sawa lake in Al Muthana governorate with the content of gypsum 65.5%, the polyurethane polymer (PP) was used with different percentages 3, 6, and 10% to enhance the mechanical properties of gypsum soil, model was prepared to achieve four soaking and drying cycle to the samples before testing, this model consists of an Aluminum plate base with dimensions 7

Expansive soil spreads in Iraq and some countries of the world. But there are many problems can be occurred to the structures that built on, so we must study the characteristics of these soils due to the  problems that may be caused to these structures which built on these kinds of soil and then study the methods of treatment. The present study focuses on improving  the geotechnical properties of expansive soils by treating it Metakaolin(M). Metakaolin (M) has never been used before as an improvement material  for stabilizing the expansive soil . Metakaolin  is a pozzolanic material. It’s obtained by calcination of kaolinite clay at temperatures from 700°C to 800°C. Kaolin chemical composition is

Iron-Epoxy composite samples were prepared by added
different weight percentages (0, 5, 10, 15, and 20 wt %) from Iron
particles in the range of (30-40μm) as a particle size. The contents
were mixed carefully, and placed a circular dies with a diameter of
2.5 cm. Different mechanical tests (Shore D Hardness, Tensile
strength, and Impact strength ) were carried out for all samples. The
samples were immersed in water for ten weeks, and after two weeks
the samples were take-out and drying to conducting all mechanical
tests were repeated for all samples. The hardness values increased
when the Iron particle concentration increased while the Impact
strength is not affected by the increasing of Iron particles
c

Physical adsorption by nitrogen gas was studied on seven commercial platinum reforming catalysts (RG-402, RG-412, RG-432, RG-451, RG 422,RG-482, PS-10), four prepared platinum catalysts (0.1%Pt/alumina, 0.2 %Pt/alumina, 0.45 %Pt/alumina and 0.55% Pt/alumina), and -alumina support. Physical adsorption was carried out by using Accelerated Surface Area and Porosimetry (ASAP 2400 device) at 77 K . The results indicate that the surface area in genaral decreases with increasing platinum percentage, high platinum loaded (0.45% and 0.55%) it was found that the percent increasing in surface area was lower than those obtained for low platinum loaded catalysts , and at very higher platinum loading 0.6 %Pt , some reduction in surface area was

تعد الرماية واحدة من الألعاب التي يقاس مستوى الانجاز فيها بالأرقام إذ ارتفعت الأرقام المسجلة بالنسبة لسلاح المسدس الهوائي حتى وصلت عند بعض الأبطال العالميين إلى الانجاز النهائي ، وقد لجأ المدربون إلى مختلف الطرق التدريبية, وان ضعف الثبات والتركيز هما اللذان يقودان إلى هبوط مستوى الانجاز في الرماية ، ولتحقيق التركيز والثبات المطلوبين أثناء الرمي يجب التدريب على مطاولة حمل السلاح التي تعد من أصعب تدريبات الر