In this research Epoxy resin was reinforced by nano alumina (AL2O3) particles in grain size(25-30 nm) with two weight ratios (2,4)% then compared with pure Epoxy. Four mechanical tests were performed on these materials include Hardness, flexural, impact & compression strengths before and after immersion in tap water and chemical solutions (CH3COOH) acid, (KOH) base at (0.5N) ,The diffusivity coefficients of all prepared samples were calculate after immersion in water and chemical solutions mentioned above , the results were showed that the Flexural, Impact & Hardness increase after addition the ceramic particles (AL2O3) while the immersion process results showed illustrated different values from sample to other.

This work study the effect of laser surface heat treatment on physical properties (green density, density after sintering, theoretical density and porosity)of a composite material of an Al powder as a matrix with different percentage of B4C powder as additive material. This work was done by two stages: First stage: Production the maincomposite material which is contain Al powder with grain size 24μm as a matrix and B4C powder with grain size 50μm as additive with different weight percentage (5%,10%,15%,20%,25%,30%), and the powders Maxined for suitable time 15min, after that the mixture compacted with 2ton and sintered at 550C0. Second stage: Laser surface treatment was done for the productive composite material after sintering by usin

Gallbladder disease is relatively common and its complications are seen every now and then. One of the rare complications is gallbladder perforation. In our case we were faced with a picture similar to perforation of the gallbladder upon surgical exploration, with empyema of gallbladder and pericholecystic abscess and a stonelocated between the gallbladder and the liver bed (inside the abscess) and no perforation in the gallbladder or fistula with the biliary tree could be discerned.

In this research, the effect of each of the concentrations ( Nd⁺³) was studied (N) the thickness of the thin disk (d) the number of times that the pumping beam passes through the effective medium of this laser (M_p) the reflectivity of the laser output mirror (R ₂₎ The losses of the effective medium (L) and the pumping power used in achieving the reverse qualification (P_P) on each of the pumping threshold capacities (P_p.th) and the output power of the laser (P_out) and the efficiency (ŋ) in Nd³⁺ thin-disk lasers (TDLs) pumping quasi-three-level With continuous operation (cw), at room temperature, and in the Gaussian mode (TEM00),

We found under these opera

This investigation was conducted to examine some physical and chemical properties of sand dunes collected from Basrah (1 '2 and 3) 'Nassiriya (4 and 5) and Amara (6) provinces that situated in lower Mesopotamia plain.

The results indicate clearly that the dominant particles in the samples were sand that were ranging from (81) % to (97) %, however the aggregated size of (0.1 - 0.25) mm were predominates in the investigated sand dunes of the region . Also the study shows that the content of the organic matter and potassium ions were very low (0.1- 0.4% '0.02 -0.22 meq I 100 gm soil. Further more the current result shows high a percentage of calcium carbonate (20.3 - 42.5%). In addition, the study has found a

RESRAD is a computer model designed to estimate risks and radiation doses from residual radioactive materials in soil. Thirty seven soil samples were collected from the area around the berms of Al-Tuwaitha site and two samples as background taken from an area about 3 km north of the site. The samples were measured by gamma-ray spectrometry system using high purity germanium (HPGe) detector. The results of samples measurements showed that three contaminated area with 238U and 235U found in the study area. Two scenarios were applied for each contaminated area to estimate the dose using RESRAD (onsite) version 7.0 code. The total dose of resident farmer scenario for area A, B and C are 0.854, 0.033 and 2.15×10-3 mSv.yr-1, respectively. Whi

Silver selenide telluride Semiconducting (Ag2Se0.8Te0.2) thin films were by thermal evaporation at RT with thickness350 nm at annealing temperatures (300, 348, 398, and 448) °K for 1 hour on glass substrates .using X-ray diffraction, the structural characteristics were calculated as a function of annealing temperatures with no preferential orientation along any plane. Atomic force microscopy (AFM) and X-ray techniques are used to analyze the Ag2SeTe thin films' physical makeup and properties. AFM techniques were used to analyze the surface morphology of the Ag2SeTe films, and the results showed that the values for average diameter, surface roughness, and grain size mutation increased with annealing temperature (116.36-171.02) nm The transm