Electrical and Structural Properties of CuBa2LaCa2Cu4O11+δ Superconducting System
...Show More Authors

In this work, the superconducting CuBa2LaCa2Cu4O11+δ compound was prepared by citrate precursor method and the electrical and structural properties were studied. The electrical resistivity has been measured using four probe test to find the critical temperature Tc(offset) and Tc(onset). It was found that Tc (offset) at zero resistivity has 101 K and Tc (onset) has 116 K. The X-ray diffraction (XRD) analysis exhibited that a prepared compound has a tetragonal structure. The crystal size and microscopic strain due to lattice deformation of CuBa2LaCa2Cu4O11+δ were estimated by four methods, namely Scherer(S), Halder-Wagner(H-W), size-strain plot (SSP) and Williamson-Hall, (W-H) methods. Results of crystal sizes obtained by these methods were compared with each other. In all these methods, the values of βhkl (full-width half-maximum (FWHM) for diffraction peaks) and miler indices (hkl) are determined from the results obtained from Fullprof, Mach, Origin and VESTA software. The lattice parameters a, b and c, lattice shape, d and degree of crystallization were calculated. It was found that the crystal size which are calculating by S, W-H, SSP and H-W were (174.8472, 171.1776, 173.1009 and 175.4386) A0 respectively while the lattice strain values were (none, 0.0025, 0.004 and 0.003464), respectively.

Scopus Crossref
View Publication
Publication Date
Mon Mar 08 2021
Journal Name
Baghdad Science Journal
Structural and mechanical properties of dental amalgam record locally
...Show More Authors

The dental amalgam of radioactive materials in the restoration of teeth because of its readily adaptable to existing materials in the oral cavity in addition to mechanical properties such as hardness mechanical resistance Alndgat and others in this study were prepared Almlagm used Guy dental restoration of silver alloy tin plus some elements to improve the characteristicsmechanical such as copper, zinc or indium in addition to mercury

View Publication Preview PDF
Publication Date
Sun Apr 23 2017
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Preparation And Study Of Some Electrical Properties Of Mn-Ni Fe2O4
...Show More Authors

 In this study, Mn-Ni Ferrite was prepared by using two composites of manganese ferrite ( MnFe2o4 )  and Nicle Ferrite ( NiFe2O4) tested by X-Ray diffraction (XRD) method. The dielectric constant (𝜀̅) and the dielectric loss tangent (𝑡𝑎𝑛 𝛿) were studied for the ferrite system prepared at different frequencies (100, 200… and 5000 kHz). It was found that the values of (𝜀̅) and (𝑡𝑎𝑛 𝛿) decrease with the  increase of frequencies.

View Publication Preview PDF
Publication Date
Thu Jun 01 2017
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
D.C. Electrical Properties of MgCl2–Filled PEO Films
...Show More Authors

The D.C. electrical properties of poly (ethylene oxide)/MgCl2 composites were investigated as a function of different MgCl2 filler concentrations (0, 5, 10, 15 and 20 wt.%) and different temperatures in the range (276–333)o K at three different polarizing fields. Resistivity: and dc Conductivity: σ dc were measured, and the activation energy: Ea of the thermal rate-process of the electrical conduction was investigated. It was found that the current-voltage measurement results exhibited Ohmic resistance behavior, the composites exhibit negative temperature reliance of resistivity and enhancement in the D.C. electrical conductivity with both temperature and MgCl2 concentration. The determined activation energy was found to

... Show More
View Publication Preview PDF
Publication Date
Sun Feb 24 2019
Journal Name
Iraqi Journal Of Physics
Morphology, chemical and electrical properties of CdO Nanoparticles on porous silicon
...Show More Authors

In this paper, CdO nanoparticles prepared by pulsed laser deposition techniqueonto a porous silicon (PS) surface prepared by electrochemical etching of p-type silicon wafer with resistivity (1.5-4Ω.cm) in hydrofluoric (HF) acid of 20% concentration. Current density (15 mA/cm2) and etching times (20min). The films were characterized by the measurement of AFM, FTIR spectroscopy and electrical properties.

  Atomic Force microscopy confirms the nanometric size.Chemical components during the electrochemical etching show on surface of PSchanges take place in the spectrum of CdO deposited PS when compared to as-anodized PS.

The electrical properties of prepared PS; namely current density-voltage charact

... Show More
View Publication Preview PDF
Crossref
Publication Date
Sat Jun 01 2013
Journal Name
International Journal Of Advanced Research In Engineering And Technology (ijaret)
MORPHOLOGICAL AND ELECTRICAL PROPERTIES OF SP DEPOSITED CADMIUM SULPHIDE THIN FILMS
...Show More Authors

ABSTRACT: Thin film of CdS has been deposited onto clean glass substrate by using Spray pyrolysis technique. Results of Morphological (AFM) studied; electrical properties and optical conductivity studied are analysis. AFM results show a crystalline nature of the films. From the conductivity measurement at different temperatures, the activation energy of the films was calculated and found to be between 0.188 - 0.124 eV for low temperature regions, and between 1.67-1.19eV for high temperature regions. Hall measurements of electrical properties at room temperature show that the resistivity and mobility of CdS polycrystalline films deposited at 400 C0, were 3.878x103 . cm and 1.302x104cm2/ (V.s), respectively. The electrical conductivity of th

... Show More
Preview PDF
Publication Date
Mon Oct 01 2012
Journal Name
Iraqi Journal Of Physics
Synthesis and study the electrical properties of carbon nanotubes- polyvinylchloride composites
...Show More Authors

The aim of this paper, study the effect of carbon nanotubes on the electrical properties of polyvinylchloride. Samples of polyvinylchloride carbon nanotubes composite prepared by using hot press technique. The weight percentages of carbon nanotubes are 0,5,10 and 20wt.%. Results showed that the D.C electrical conductivity increases with increasing of the weight percentages of carbon nanotubes. Also, the D.C electrical conductivity changed with increase temperature for different concentrations of carbon nanotubes. The activation energy of D.C electrical conductivity is decreased with increasing of carbon nanotubes concentration.

View Publication Preview PDF
Publication Date
Sat Jan 01 2022
Journal Name
3rd International Scientific Conference Of Alkafeel University (iscku 2021)
Simulation and investigation of the ICP plasma torch’s electrical and thermal properties
...Show More Authors

View Publication
Scopus Crossref
Publication Date
Mon Oct 01 2018
Journal Name
Iraqi Journal Of Physics
Effect of Sb2O3 and/or CdO nanoparticle substitution on the properties of high-TC superconducting Bi1.6-x SbxPb0.4Sr2Ca2-yCdyCu3OZ material
...Show More Authors

High temperature superconductors materials with composition Bi1.6-xSbxPb0.4Sr2Ca2-yCdyCu3OZ (x = 0, 0.1, 0.2 and 0.3) and (y = 0.01 and 0.02), were prepared by using the chemical reaction in solid-state ways, and test influence of partial replacement of Bi and Ca with Sb and Cd respectively on the superconducting properties, all samples were sintered at the same temperature (850 oC) and for the same time (195 h). The structural analysis of the prepared samples was carried out using X-ray diffraction (XRD) measurements performed at room temperature, scanning electron microscope (SEM) and dc electrical resistivity was measured as a function of temperature. It was found that the sample prepared by partial substitution of Sb at ratio (x= 0.2

... Show More
View Publication Preview PDF
Crossref
Publication Date
Sat Jul 01 2023
Journal Name
Chemical Methodologies
Acid Activation of Iraqi Bentonite Clay and Studying its Structural, Dielectric and Electrical Behavior at Various Temperatures
...Show More Authors

Iraqi calcium bentonite was activated via acidification to study its structural and electrical properties. The elemental analysis of treated bentonite was determined by using X-ray fluorescence while the unit crystal structure was studied through X-ray diffraction showing disappearance of some fundamental reflections due to the treatment processes. The surface morphology, on the other hand, was studied thoroughly by Scanning Electron microscopy SEM and Atomic Force Microscope AFM showing some fragments of montmorillonite sheets. Furthermore, the electrical properties of bentonite were studied including: The dielectric permittivity, conductivity, tangent loss factor, and impedance with range of frequency (0.1-1000 KHz) at different temperatu

... Show More
Publication Date
Mon Dec 01 2014
Journal Name
Aip Advances
Ab initio structural and vibrational properties of GaAs diamondoids and nanocrystals
...Show More Authors

Gallium arsenide diamondoids structural and vibrational properties are investigated using density functional theory at the PBE/6-31(d) level and basis including polarization functions. Variation of energy gap as these diamondoids increase in size is seen to follow confinement theory for diamondoids having nearly equiaxed dimensions. Density of energy states transforms from nearly single levels to band structure as we reach larger diamondoids. Bonds of surface hydrogen with As atoms are relatively localized and shorter than that bonded to Ga atoms. Ga-As bonds have a distribution range of values due to surface reconstruction and effect of bonding to hydrogen atoms. Experimental bulk Ga-As bond length (2.45 Å) is within this distribu

... Show More
View Publication
Scopus (10)
Crossref (9)
Scopus Clarivate Crossref