Effect of Sb2O3 and/or CdO nanoparticle substitution on the properties of high-TC superconducting Bi1.6-x SbxPb0.4Sr2Ca2-yCdyCu3OZ material
...Show More Authors

High temperature superconductors materials with composition Bi1.6-xSbxPb0.4Sr2Ca2-yCdyCu3OZ (x = 0, 0.1, 0.2 and 0.3) and (y = 0.01 and 0.02), were prepared by using the chemical reaction in solid-state ways, and test influence of partial replacement of Bi and Ca with Sb and Cd respectively on the superconducting properties, all samples were sintered at the same temperature (850 oC) and for the same time (195 h). The structural analysis of the prepared samples was carried out using X-ray diffraction (XRD) measurements performed at room temperature, scanning electron microscope (SEM) and dc electrical resistivity was measured as a function of temperature. It was found that the sample prepared by partial substitution of Sb at ratio (x= 0.2) and Cd with ratio (y=0.01), has the maximum value of zero resistance temperature, where was the TC(onset) and TC(0) values for this sample are (140 K) and (123 K) respectively, and XRD results reveal that this sample has the highest percentage of Bi- 2223 phase, as well as the analysis of XRD patterns of the prepared materials showed polycrystalline structure and signalize that all samples had an orthorhombic crystalline structure. It was concluded that Sb2O3 nanoparticles it may be acts as a flux agent in the matrix to lower the partial melting temperature of the samples and that leads to the promotion of the high-TC phase.

Crossref
View Publication Preview PDF
Quick Preview PDF
Publication Date
Tue Jan 01 2019
Journal Name
Aip Conference Proceedings
Studying the partial substitution of barium with cadmium oxide and its effect on the electrical and structural properties of HgBa2Ca2Cu3O8+δ superconducting compound
...Show More Authors

View Publication
Scopus (24)
Crossref (20)
Scopus Clarivate Crossref
Publication Date
Tue Jan 01 2019
Journal Name
Energy Procedia
Improvement the Superconducting properties of TlBa2 Ca2 Cu3xNix O 9-δ superconducting compound by partial substitution of copper with nickel oxide on the
...Show More Authors

View Publication
Scopus (21)
Crossref (24)
Scopus Clarivate Crossref
Publication Date
Sun Jun 12 2011
Journal Name
Baghdad Science Journal
Superconducting Properties of the (Bi0.8Pb0.2)2(Sr0.9Ba0.1)2 Ca2Cu3-x Nix O10+? System.
...Show More Authors

The effect of substitution of Ni on Cu in (Bi0.8Pb0.2)2(Sr0.9Ba0.1)2 Ca2Cu3-x Nix O10+? for (x=0,0.1….1,2,3) superconductor system and sintering time has been investigated .The samples were prepared by solid-state reaction methods. The results show that the optimum sintering temperature is equal to 850 ºC, and the sintering time is equal to 140 h. The highest transition temperature (Tc) obtained for (Bi0.8Pb0.2)2(Sr0.9Ba0.1)2 Ca2Cu3-x NixO10+? composition was 113 with x=0.8 Phase analyses of the samples by X-ray diffraction (XRD) analysis showed an orthorhombic structure with a high Tc phases (2223) as a dominant phase and low Tc phase (2212) in addition to some impurity phases.

View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Tue Jan 01 2019
Journal Name
Aip Conference Proceedings
Physical properties of HgX Sb1-X Ba2Ca2Cu3O8+δ superconducting compound: Effect of fast neutrons irradiation
...Show More Authors

Applications of superconductor compounds were considered as modern and important topics, especially these which are exposures to one of the nuclear radiation kinds. So, we gone to investigate the influence of fast neutrons irradiation on electrical and structural characteristics of HgxSb1-xBa2Ca2Cu3O8+δ superconducting compound at (x = 0.7) in ratio. The superconducting specimens were synthesized using solid state technique. Specimens were exposure to the nuclear radiation using fast neutrons with doses (0, 9.06 x1010, 15.3 x 1010 and 18.17 x 1010) n/cm2 respectively. Electrical and X-ray diffraction properties of superconductor specimens before and after irradiation were investigated under standard conditions. Results of X-ray diffraction

... Show More
View Publication Preview PDF
Scopus (1)
Crossref (2)
Scopus Clarivate Crossref
Publication Date
Tue Jan 01 2019
Journal Name
Energy Procedia
Improved thermal and mechanical properties of CdBa2-x SrxCa2Cu3O8+δ superconducting compounds
...Show More Authors

View Publication
Scopus Clarivate Crossref
Publication Date
Tue Jan 08 2019
Journal Name
Iraqi Journal Of Physics
Effect of concentrations ratios of NiO on the efficiency of solar cell for (CdO)1-x(NiO)x thin films
...Show More Authors

CdO:NiO/Si solar cell film was fabricated via deposition of CdO:NiO in different concentrations 1%, 3%, and 5% for NiO thin films in R.T and 723K, on n-type silicon substrate with approximately 200 nm thickness using pulse laser deposition. CdO:NiO/n-Si solar cell photovoltaic properties were examined under 60 mW/cm2 intensity illumination. The highest efficiency of the solar cell is 2.4% when the NiO concentration is 0.05 at 723K.

View Publication Preview PDF
Crossref
Publication Date
Mon Jan 01 2018
Journal Name
Aip Conference Proceedings
Effect of gamma irradiation on the TlBa2Ca2Cu3O9-δ superconducting properties
...Show More Authors

View Publication
Scopus (10)
Crossref (10)
Scopus Clarivate Crossref
Publication Date
Tue Feb 01 2022
Journal Name
Journal Of Physics: Conference Series
Study the effect of gamma Irradiation on the Superconducting Properties of HgBaSrCa2Cu3O8+δ
...Show More Authors

Publication Date
Tue Feb 01 2022
Journal Name
Journal Of Ovonic Research
Effect of copper on physical properties of CdO thin films and n-CdO: Cu / p-Si heterojunction
...Show More Authors

Scopus (14)
Scopus
Publication Date
Tue Feb 01 2022
Journal Name
Journal Of Ovonic Research
Effect of copper on physical properties of CdO thin films and n-CdO: Cu / p-Si heterojunction
...Show More Authors