Alloys from AgSb(SxSe1-x)2 with different compositions were prepared using quenching from the melt . This was done by put the appropriate amount of Ag, Sb,S and Se in an evaluated quartz ampoule , sealed and left at oven in temperature 1273 for 5 hours. Thin films with different composition were deposited by pulsed deposition technique PLD onto glass substrates at ambient temperature . This paper concerned on the investigate effect of composition on structural morphology, and electrical properties. The structure and morphology of the prepoared thin films were checked using X–ray diffraction and atomic force microscope. The D.C conductivity of the AgSb(SxSe1-x)2thin films with various x content was measured

The purpose of the current work was to evaluate the effect of Radiation of Gamma on the superconducting characteristics of the compound PbBr2Ca1.9Sb0.1Cu3O8+δ utilizing a 137Cs source at doses of 10, 15, and 20MRad. Solid state reaction technology was used to prepare the samples. Before and after irradiation, X-ray diffraction (XRD) and superconductor properties were examined. Results indicated that the tetragonal structure of our chemical corresponds to the Pb-1223 phase with an increase in the ratio c/a as a result of gamma irradiation. (Tc (onset) ) and on set temperature Tc (offset)) were also dropping from 113 to the 85.6 K and 129.5 to 97 K, respectively, for a transition temperatu