The present work aimed to study effect of (N749 & N3) dyes on TiO2 optical and electrical properties for optoelectronic application. The TiO2 paste prepared by using a doctor blade method. The samples were UV-VIS specterophometricall analyzes of TiO2 before and after immersed in dyes (N749 & N3). The results showed absorption spectra shift toward the visible region due to the adsorption of dye molecules on the surface of oxide nanoparticles. It is seen that the Eg determined to give a value of 3.3eV for TiO2 before immersing in dyes, and immersing in dyes (N749 & N3) are (1.4 &1.6 eV) respectively. The structural properties (XRD), (FTIR) and (SEM) for the sample prepared were investigated and (J-V) characteristics was stu

A number of disorders characterized by aberrant cell proliferation are referred to as cancers. Cancer is a complicated group of mutagenic diseases that can move or infiltrate to other parts of the body. It develops through a multi-step process. The need for new therapeutic strategies is driven by malignancies resistance to conventional therapies. Use of the Newcastle disease virus as an oncolytic agent has advanced and expanded in immunocompetent carcinoma tumor models by utilizing reverse genetics techniques. Preclinical investigations have shown that recombinant NDV (rNDV-GFP), which expresses foreign genes, is proven to be effective in cancer treatment. Green fluorescent protein gene is usually used as an expression reporter for certa

Silver nanoparticles (Ag-NPs) have been prepared using the electro-chemical
method. The experimental setup of this technique consist of two electrodes of pure
silver (99.2 %), the applied voltage on the electrodes is 20 V and the current through
the colloidal was about 0.4 Amp. The silver nanoparticles crystallization has been
studied; the crystalline structure appears Face center Cubic. The optical properties of
silver nanoparticles are strongly affected by the Local Surface Plasmon Resonance
(LSPR). The wavelength of maximum absorption band for an Ag NPs have a range
(~350nm-550nm).

In this study, In2O3 was prepared by Solvothermal technique in autoclave device, which is a simple and inexpensive technique to indicate the best condition. The reaction took place between indium chloride and urea. In(OH)3 as-prepared annealing at 100°C and convert to In2O3 at annealing temperatures 300, 500, 700 °C for 90 min .The physical properties of nanoparticles were characterized by XRD, SEM, AFM, UV/Visible and FTIR spectroscopy measurements. The examination results of XRD for In2O3 powder annealed at different temperature showed the formation of a cubic phase of nanoparticles with high intensity of plane (222). The lattice constant decreases with the increase of annealing temperature (from 10.07 to 10.04 Ǻ). AFM indicated an

This study proposed to synthesize iron oxide by biological method nanoparticles. The E.coli is used to reduce Ferric chloride salt into iron particles. The formation of iron oxide nanoparticle was initially monitored by visual observation and then characterized with the help of various characterization techniques such as Uv-vis spectroscopy, (AFM) and (FTIR) analysis, which revealed that the biosynthesized iron oxide nanoparticles were spherical within size 27.7 nm. Optimization of iron oxide nanoparticle biosynthesis by E.coli was performed for parameters (temperature and pH) and the results revealed that temperature 37°C and pH 5 were the optimum conditions for iron oxide nanoparticales biosynthesis by E.coli.<

This study was conducted to investigate the antibacterial activity of green synthesized copper oxide nanoparticles (CuO NPs) using Aloe vera. Initially, bacteria were collected from clinical samples of patients having otitis media infection and the isolates were identified at the species level following biochemical tests. Copper oxide nanoparticles were prepared by green synthesis using Aloe vera leaves and characterized using UV- visible spectroscopy at 260 nm peak. The shape and size were determined by using transmission electron microscopy (TEM) and the dimensions of the particles were more precisely determined by using scanning electron microscopy (SEM) and x-ray diffraction (XRD). Different concentrations of nanopa

Nanofluids (dispersion of nanoparticles in a base fluid) have been suggested as promising agents in subsurface industries including enhanced oil recovery. Nanoparticles can easily pass through small pore throats in reservoirs formations; however, physicochemical interactions between nanoparticles and between nanoparticles and rocks can cause a significant retention of nanoparticles. This study investigated the transport, attach, and retention of silica nanoparticles in core plugs. The hydrophilic silica nanoparticles were injected into limestone core as nanofluid of different nanoparticles size (5 nm, and 20 nm), concentration (0.005 – 0.1 wt% SiO2), and base fluid salinity (0 – 3 wt% NaCl) at different temperatures (23, and 50 °C). D

Background. Nanocoating of biomedical materials may be considered the most essential developing field recently, primarily directed at improving their tribological behaviors that enhance their performance and durability. In orthodontics, as in many medical fields, friction reduction (by nanocoatings) among different orthodontic components is considered a substantial milestone in the development of biomedical technology that reduces orthodontic treatment time. The objective of the current research was to explore the tribological behavior, namely, friction of nanocoated thin layer by tantalum (Ta), niobium (Nb), and vanadium (V) manufactured using plasma sputtering at 1, 2, and 3 hours on substrates made of 316L stainless steel (SS),

In this work gold nanoparticles (AuNPs), were prepared. Chemical method (Seed-Growth) was used to prepare it, then doping AuNPs with porous silicon (PS), used silicon wafer p-type to produce (PS) the processes doping achieved by electrochemical etching, the solution etching consist of HF, ethanol and AuNPs suspension, the result UV-visible absorption for AuNPs suspension showed the single peak located at ~(530 – 521) nm that related to SPR, the single peak is confirmed that the NPs present in the suspension is spherical shape and non-aggregated. X-ray diffraction analysis indicated growth AuNPs with PS. compare the PS layer without AuNPs and with AuNPs doped for electrical properties and sensitivity properties we found AuNPs:PS is more