This study was aimed to study the effect of adding transglutaminase (TGase) on the mechanical and reservation properties of the edible films manufactured from soybean meal protein isolate (SPI) and whey protein isolate(WPI). The results showed an improvement in the properties with increase in the WPI ratios. Thickness of the SPI films amounted 0.097 mm decreased to 0.096 mm for the WPI: SPI films at a ratio of 2:1, when TGase was added decreased to 0.075 mm. While the tensile strength increased from 7.64 MPa for SPI films to eight MPa for the WPI: SPI films at a ratio of 2:1, when TGase was added increased to 11.04 MPa. Also, the elongation of the WPI: SPI films at a ratio of 2:1 presence of the TGase decreased to 40.6% compared wit

The problem of the damage caused by terrorist acts has raised many difficulties in many countries, including Iraq, which requires the existence of a law that sets out sufficient rules for compensating the victims of terrorist acts, in order to compensate them for the harm they have not suffered. It may be difficult or impossible for them to identify causing damage, and therefore unable to obtain compensation by applying the traditional rules of liability that require proof of fault and identify the culprit. The security funds come as an appropriate alternative that pays compensation in such cases for victims to reparation for the damage they suffered. Therefore, this problem remains one of the most problems that Iraq suffers from it, which

So far synthesis of Gonadotropin Releasing Hormone (GnRH) analogues reported in the literature has clarified some aspects of structural activity of the naturally released GnRH. As a part of continuing efforts for further understanding of this relationship, the present investigation was undertaken which involved synthesis and biological evaluation of two GnRH analogues, firstly, by replacement of the amino acid L-Argenine in the 8^th position at the backbone structure of the natural hormone by the amino acid D-Alanine; and secondly, by replacement of the amino acid L-Glycine in the 10^th position by D-Alanine also at the backbone structure of the nature hormone, to obtain the following analogues respectively:

P

Objective Advantageous properties of silicone elastomer made it one of the favorable materials in maxillofacial prosthesis construction, but these properties may change after months of usage or after pigments addition. This study aimed to define the optimum concentration for a mixture of two types of intrinsic pigments that added to VST-50 maxillofacial silicone material and study their effects on mechanical properties before and after artificial aging. Methods After the pilot study was conducted, 0.1% by weight of rayon flocking and 0. 2% by weight of burnt sienna intrinsic pigment concentration was selected because of improvement in tested mechanical properties of VST-50 maxillofacial silicone. A total of one hundred and eighty samples we

An experiment was conducted in the plastic house of the Botanical Garden in the Department of Biology, College of Education for Pure Sciences (Ibn Al-Haitham), University of Baghdad during one growth season. The experiment included the study of the effect of three concentrations of citric acid (0, 75, 150) mg. L-1 and four concentrations of malic acid (0, 50, 100, 150) mg. L-1 and their interaction in some of the growth and yield parameters of the broad bean plant, plant height, dry weight, number of leaves, total chlorophyll content, the number of flowers and pods and the weight of the pod. The experiment was carried out in full random design (4× 3) and with three duplicates, the results showed a significant effect of citric and malic aci

This work deals with preparation of zeolite 5A from Dewekhala kaolin clay in Al-Anbar region for drying and desulphurization of liquefied petroleum gas. The preparation of zeolite 5A includes treating kaolin clay with dilute hydrochloric acid 1N, treating metakaolin with NaOH solution to prepare 4A zeolite, ion exchange, and formation. For preparation of zeolite 4A, metakaolin treated at different temperatures (40, 60, 80, 90, and 100 °C) with different concentrations of sodium hydroxide solution (1, 2, 3, and 4 N) for 2 hours. The zeolite samples give the best relative crystallinity of zeolite prepared at 80 °C with NaOH concentration 3N (199%), and at 90 and 100°C with NaOH concentration solution 2N (184% and 189%, respectively). Ze

In this work, The effect of annealing treatment at different temperatures (373, 423 and 473) K and chemical treatment with talwen at different immersion time (40, 60 and 80) min on structural and optical properties of the bulk heterojunction (BHJ) blend copper phthalocyanine tetrasulfonic acid tetrasodium salt/poly dioxyethylenethienylene doped with polystyrenesulphonic acid (CuPcTs/PEDOT:PSS) thin films were investigated. The films were fabricated using spin coating technique. X-ray diffraction (XRD) measurements displayed only one peak at 2θ =4.5o corresponding to (001) direction which has dhkl larger than for standard CuPcTs. The dhkl increase then decrease with increasing annealing temperature and
the time of chemical treatment w