Background: Dental implants provide a unique treatment modality for the replacement of a lost dentition .This is accomplished by the insertion of relatively an inert material (a biomaterial) into the soft and hard tissue of the jaws, there by providing support and retention for dental prostheses. Low level laser therapy (LLLT) is an effective tool used to prompt bone repair and remodeling, this has referred to the biostimulation effect of LLLT. The Aim of this study was to evaluate the effects of inflammatory cells on osseointegration of CpTi implant irradiated by low level laser. Materials and Methods: thirty two adult New Zealand white rabbits, received titanium implants were inserted in the tibia. The right side is considered as experime

Mixed Kirkuk and Sharki-Baghdad crude oils were distilled into narrow fractions. The range of these narrow fractions were 10oC, starting from IBP to 350oC. The total distillates from mixed Kirkuk and Sharki-Baghdad crude oils were 58.25 vol % and 44.65 vol %, respectively.The hydrocarbons compositions (paraffin, naphthene, aromatic) in light fractions starting from IBP to 250oC were determined by using PONA analysis method. The results show that the paraffin content decreases with increasing mid percent boiling point of the fraction, while the naphthene, and aromatic increase with the increase of mid percent boiling point of mixed Kirkuk and Sharki-Baghdad crude oils. Three groups of empirical equations were developed for the prediction

Abstract

 In this work, pure Polypyrrole (PPy) and Polypyrrole (PPy)/Graphene (GN) was synthesized by in-situ polymerization in different weight percentages (0.1, 0.3, 0.5, 1, 3 and 5 wt.% (g)) of GN nano particles using chemical oxidation method at room temperature. The FTIR, SEM and electrical properties were studies for the nano composites. The result show that when concentration of GN Nano particle increase, the electrical conductivity increased and the graphene sheets were merging to form a continuous area of the GN through the polypyrrole base material. The FTIR spectra shows that the characteristics absorption peaks of polypyrrole that is, 1546.80, 1463.87 and 3400.27 cm^-1(stretching vibration in the pyrrol

In this work, spinel ferrites (NiCoFe₂O₄) were prepared as thin films by dc reactive dual-magnetron co-sputtering technique. Effects of some operation parameters, such as inter-electrode distance, and preparation conditions such as mixing ratio of argon and oxygen in the gas mixture, on the structural and spectroscopic characteristics of the prepared samples were studied. For samples prepared at inter-electrode distance of 5 cm, only one functional group of OH^- was observed in the FTIR spectra as all bands belonging to the metal-oxygen vibration were observed. Similarly, the XRD results showed that decreasing the pressure of oxygen in the gas mixture lead to grow more crystal planes in the samples prepare

The DC electrical conductivity properties of Ge60Se40-xTex alloy with x = 0, 5, 10, 15 and 20). The samples were formed in the form of discs with the thickness of 0.25–0.30 cm and the diameter of 1.5 cm. Samples were pressed under a pressure of 6 tons per cm2 , using a ton hydraulic press. They were prepared after being pressed using a ton hydraulic press using a hydraulic press. Melting point technology use to preper the samples. Continuous electrical conductivity properties were recorded from room temperature to 475 K. Experimental data indicates that glass containing 15% Te has the highest electrical conductivity allowing maximum current through the sample compared to Lu with other samples. Therefore, it is found that the DC co

A significant influence of temperature width found on the vanadium oxide properties, it plays a major role in highlighting the thermal limits of the three phases (metallic, semiconductor, and dielectric). Two values of the temperature width , and , had taken and studied their effect on both the dielectric constant and its two parts; refractive index, and extinction coefficient, and. It found that: as the temperature width is greater, the more the properties of the three phases for . In addition to increasing the thermal range for phases which can be reached to when , while it's at . Our results have achieved great compatibility with the published results globally. In addition to the effect of both ultraviolet, visible, and infrared

Background: The most common reason for re-making a maxillofacial prosthesis is the degradation of the mechanical properties of the silicone. Aim of this study: To assess some mechanical properties of VST-50F maxillofacial silicone reinforced with a composite of silicon dioxide nanoparticle and polyamide-6 microparticle before and after artificial aging. Material and Method: Preparing 240 samples tested for tear strength, tensile strength and elongation percentage, hardness, and roughness before and after aging. The Silicon dioxide was added in concentrations of 1% by weight and Polyamide-6 in the concentration of 0.25% and 0.5% by weight to the VST-50F RTV maxillofacial silicone. The one-way ANOVA and post hoc tests were used for inferentia

This work describes, selenium (Se) films were deposited on clean glass substrates by dc planar magnetron sputtering technique.The dependence of sputtering deposition rate of Se film deposited on pressure and DC power has been studied. The optimum argon pressure has range (4x10-1 -8x10-2 )mbar. The optical properties such as absorption coefficient (α) was determined using the absorbance and transmission measurement from UnicoUV-2102 PC spectrophotometer, at normal incidence of light in the wavelength range of 200-850 nm. And also we calculated optical constants(refractive index (n), dielectric constant (εi,r), and Extinction coefficient (κ) for selenium films.