The research aims to identify the digital repository of the University of Baghdad, explain its features, how to register, explaining the mechanism for adding and retrieving research. In addition to identifying the number of people registered in and the number of intellectual outputs stored in it. The descriptive approach and survey methods were adopted by visiting the repository's website and the websites of the University of Baghdad's formations during the period (1-6/4/2024). The theoretical framework included an explanation of the concept of the digital repository, the importance of repositories, their features, and types, with reference to models of Iraqi, Arab, and foreign university digital repositories. The practical framework of the

Photocatalytic degradation of methylene blue was studied using CdS and ZnS as catalyst. The photocatalytic activity of the specimen was studied by exposing to UV-radiation. The result shows that the degradation efficiency of the dye for CdS micro-particles was 92% after 7 hours and for ZnS micro-particles was 88.29% for the same time interval.

The derivatives formed after the successive acetylation, esterification and nitration reactions to cholic, deoxycholic, and taurocholic acids were identified to be of the following general strucure: Colt, Where RI=NO3, OH, 0=, or CH3COO. R2=H, NO3, OH, 0-=, or CH3COO. R3=H, NO3,01-1, 0=, or CH3COO. R4=OH, NH(CH2)2S03Na, NH(CH2)2S03H, or OMe. By using U.V-visible and I.R spectrophotometry . The number of hydroxyl groups was determined, purity was checked from T.L.C, Most of these derivatives will find pharmaceutical application.

Compounds were prepared from In2O3 doped SnO2 with different doping ratio by mixing and sintering at 1000oC. Pulsed Laser Deposition PLD was used to deposit thin films of different doping ratio In2O3: SnO2 (0, 1, 3, 5, 7 and 9 % wt.) on glass and p-type wafer Si(111) substrates at ambient temperature under vacuum of 10-3 bar thickness of ~100nm. X-ray diffraction and atomic force microscopy were used to examine the structural type, grain size and morphology of the prepared thin films. The results show the structures of thin films was also polycrystalline, and the predominate peaks are identical with standard cards ITO. On the other side the prepared thin films declared a reduction of degree of crystallinity with the increase of doping ra

ABSTRACT The antibacterial and antbiofilm activities of water extract of Calendula officinalis flowers against some of enteropathogenic bacteria was studied, also phytochemical screening and determination of antioxidant activity of the extract has been investigated. The results showed that the water extract of C. officinalis exhibited a good antibacterial activity against all pathogenic bacterial isolates (Salmonella, Shigella dysenteriae, Shigella flexneri, Shigella sonnei and E. coli) especially at concentration 100 µg/ml in contrast with the control cefotan antibiotic. S. sonnei was more sensitive to extract than other bacteria with highest inhibition zone (23 mm). The preliminary phytochemical tests results indicated the presence

current research aims to build an intellectual framework for concept of organizational forgetting, which is considered one of the most important topics in contemporary management thought, which is gain the consideration of most scholars and researchers in field of organizational behavior, which is to be a loss of intentional or unintentional knowledge of any organizational level. It turned out that just as organizations should learn and acquire knowledge, they must also forget, especially knowledge obsolete and worn out. And represented the research problem in the absence of Arab research dealing with organizational forgetting, and highlights the supporting infrastructure core, and show a close relationship with organizational le

A new spontaneous mutation (dh) is described for Culex quinquefasciatus Say. This
phenotype was observed in the second generation to cause complete coloration of the head
capsule and the siphon of the larvae. This character is mainly detectable in the larval stage
and slightly in the adult stage.
The reciprocal mass matting between mutants from F2 generation and normal wild type
sibs, revealed that the mode of inheritance can be controlled by an autosomal recessive
gene(s). This happened for both sexes with slightly variability in their expression. No
significant larval mortalities were found in all crosses.

Reflection cracking in asphalt concrete (AC) overlays is a common form of pavement deterioration that occurs when underlying cracks and joints in the pavement structure propagate through an overlay due to thermal and traffic-induced movement, ultimately degrading the pavement’s lifespan and performance. This study aims to determine how alterations in overlay thickness and temperature conditions, the incorporation of chopped fibers, and the use of geotextiles influence the overlay’s capacity to postpone the occurrence of reflection cracking. To achieve the above objective, a total of 36 prism specimens were prepared and tested using an overlay testing machine (OTM). The variables considered in this study were the thickness of the