The influence of fiber orientation and water absorption on fatigue crack growth resistance for cold cure acrylic (PMMA) reinforced by chopped and woven -glass-fibers were investigated. A weight of 2 g for chopped fibers and the same weight for woven -glass-fibers (one layer) were used to prepare samples. Some of these samples would storage in dry condition; the others were immersed in water for 15 days. Fatigue test was carried out. The results shows that, for PMMA, the initial bending stress for dry specimen was 3.392 N/cm2 and the number of cycles were 1364, the initial bending stress for wet samples was 4.20 N/cm2, and the number of cycles was 2411. The samples would cut in two pieces because of the cracks would propagated fast during

Three N-(hydroxylphenyl) dimethylmaleimides were directly prepared in good yields (81-86)% from the reaction of dimethylmaleic anhydride with amino phenols. The prepared imides were esterified to the corresponding benzoates, methacrylates and cinnamates via their reaction with different acid chlorides in the presence of triethylamine. The prepared esters were tested as plasticizers for PVC via preparing of thirty six samples of PVC with the prepared esters in certain weight ratio followed by recording their softening points. Comparison the results with the universal plasticizers for PVC (DOP) and (DBP) indicated that the prepared esters in general have high plasticizing efficiency.

Probiotic bacteria using in commercially produced foods are at most members of the genera Lactobacillus and Bifidobacterium. This research was aimed to study the antimicrobial effect of lactobacillus bacteria as probiotic against some pathogenic bacteria, strains of lactobacillus bacteria were isolated from two types of yoghurt in Baquba city, Iraq . Total of 60 yoghurt samples from 2 origins (30 locally and 30 commercial produced yoghurt) were used to isolate probiotic bacteria which were identified phenotypically and biochemically. 30 (100%) of locally produced yoghurt samples include with probiotic bacteria while 12 (40%) commercially types of yoghurt samples were contained with probiotic, the method of modi

The molluscicidal effects of herbicide 2, 4-D were studied against tow species of freshwater snail Bulinus truncatus and Melanopsis nodosa by short term experiments. Calculated values of lethal concentrations (LC50 and LC100) were maid to two spices for different period of time 24hr, 48hr, 72hr and 96hr. The study had showed that the herbicide 2, 4-D was toxic against the tow species. The toxicity of the herbicide was low or unknown in low concentrations in the first period of exposure 24and 48hr to two spices but it increase gradually with increase period of exposure. The spice of B.truncatus was more tolerant than the M.nodosa. All the individual of M nodosa was death while in B.truncatus the complete death was not appear until finish the

In the present study, an attempt has been made to experimentally investigate the flexural performance of ten simply supported reinforced concrete gable roof beams, including solid control specimen (i.e., without openings) and nine beams with web openings of different dimensions and configurations. The nine beams with openings have identical reinforcement details. All beams were monotonically loaded to failure under mid-span loading. The main variables were the number of the created openings, the total area of the created openings, and the inclination angle of the posts between openings. Of interest is the load-carrying capacity, cracking resistance and propagation, deformability, failure mode, and strain development that represent the behav

Soil movement resulting due unsupported excavation nearby axially loaded piles imposes significant structural troubles on geotechnical engineers especially for piles that are not designed to account for loss of lateral confinement. In this study the field excavation works of 7.0 m deep open tunnel was continuously followed up by the authors. The work is related to the project of developing the Army canal in the east of Baghdad city in Iraq. A number of selected points around the field excavation are installed on the ground surface at different horizontal distance. The elevation and coordinates of points are recorded during 23 days with excavation progress period. The field excavation process was numerically simulated by using the finite

Background: This study was performed to compare the marginal fit changes and facture resistance of metal ceramic crowns constructed from Ceramill Sintron metal coping veneered with three different porcelain veneering materials (Vita Master Koromikos VMK, Willi Geller Creation CC and GC initial MC), also to evaluate the influence of thermocycling on load at fracture. Materials and Methods: Master brass die was scanned ,then metal coping was designed and milled from Ceramill Sintron blank to get 60 metal copings, then divided randomly into three groups(20 sample), then veneered with porcelain: VITA, Creation or GC. The marginal gaps were measured before and after porcelain veneering then marginal fit changes was calculated. Fracture resist

    The complexes of para-chloranil as electron acceptor and the anions of amide, azide and cyanide as electron donors in aqueous ethanol as a solvent, were studied spectrophotometrically .     The reactions lead to the formation of charge transfer complexes. The CT complexes were stable in excess acceptor concentration, while they were underwent another transformations in excess donors concentrations.   Stoichiometries were determined, the molecular ratio was determined by continuous variation method (Job method) and is was  1:1 (donor: acceptor).   The maximum wavelength (λ max.), the energy (hÏ…CT), ionization potential (Ip) and activation energy (w ) of excited state f

Acetophenone sulfamethoxazole and 3-Nitrobenzophenone sulfamethoxazole were prepared from the reaction of sulfamethoxazole with two ketones. The prepared ligands were identified by (C.H.N) analysis and UV-VIS, FT-IR spectroscopic techniques. Metal complexes of the two ligands were prepared in an aqueous alcohol with Zn (II), Mn (II) and Cu (II) ions with a molar ratio1:1. The proposed general formula for the resulting complexes was [ML.CL2.H2O]H2O .The complexes were characterized by (C.H.N) technique , spectroscopic methods ,conductivity, atomic absorption ,magnetic susceptibility measurements and melting point. According to the results obtained, the suggested geometry is to be octahedral for all the complexes.