In this research ,Undoped Nio and 1%Li doped Nio thin films were deposited utilizing chemical spray pyrolysis on the glass substrates heated (450C). The effects of non-thermal plasma on the structural and optical properties were studied. XRD measurement shows that Nio and Nio:1%Li films were found to be polycrystalline and have cubic structure with a preferred orientation (111). Decreased crystal size after exposure especially at (7) sec. AFM data indicate that the surface roughness average and (RMS) values of the prepared doped films are increasing after exposure to plasma, the transmittance increases after doped samples exposure to plasma, it was found that the energy gap value decreased when doped samples exposure to plasma, also, thickn

Preparation of superposed thin film (CdTe)1-xSex / ZnS) with concentration of (x= 0.1, 0.3, 0.5) at a temperature of substrate (Ts= 80 0C) by using Thermal Vacuum Evaporation System. The measurement of X-ray diffraction shows that the compounds CdTe, ZnS, (CdTe)1-xSex and (CdTe)1-xSex / ZnS have a polycrystalline structure, the C-V characteristic shows that the capacitance degrease by increasing the concentration (x) in reverse bias, while the I-V characteristic shows the current dark (Id) increase in forward and reverse bias by increasing (x) and the photocurrent (Iph) increase in reverse bias by increasing the concentration (x), the values of photocurrent are greater than from the values of the dark current for all concentrations

The research work was conducted to investigate the effect of oral administration of aqueous extract of turmeric at doses of (5, 10) mg/kg body weight for two weeks daily by determining the genotoxic effect (mitotic index), evaluation of immunological effect (IgG, IgM, IgA, C3, C4) and measuring fertility hormones (follicles stimulation hormone/FSH, lutenising hormone/LH) levels with histological examinations of female albino swiss mice ovaries in comparison with control (normal saline). A clear effect in increasing mitotic activity was reveled for both doses in comparison with control. Results also showed a significant increase in the value of all immunological parameters at both doses, in comparison with control. Also, obvious rais

The research work was conducted to investigate the effect of oral administration of aqueous extract of turmeric at doses of (5, 10) mg/kg body weight for two weeks daily by determining the genotoxic effect (mitotic index), evaluation of immunological effect (IgG, IgM, IgA, C3, C4) and measuring fertility hormones (follicles stimulation hormone/FSH, lutenising hormone/LH) levels with histological examinations of female albino swiss mice ovaries in comparison with control (normal saline). A clear effect in increasing mitotic activity was reveled for both doses in comparison with control. Results also showed a significant increase in the value of all immunological parameters at both doses, in comparison with control. Also, obvious raise was se

      Spray pyrolysis technique was subjected to synthesized (SnO₂)_1-x (TiO₂: CuO) _x Thin films on different substrates like glass and single crystal silicon using. The structure of the deposited films was studied using x-ray diffraction. A more pronounced diffraction peaks of SnO₂ while no peaks of (CuO , TiO₂ ) phase appear in the X-ray profiles by increasing of the content of (TiO₂ , CuO) in the sprayed films. Mixing concentration (TiO₂ , CuO) influences on the size of the crystallites of the SnO₂ films ,the size of crystallites of the spray paralyzed oxide films change in regular manner by increasing of (TiO

High temperature superconductors materials with composition Bi1.6-xSbxPb0.4Sr2Ca2-yCdyCu3OZ (x = 0, 0.1, 0.2 and 0.3) and (y = 0.01 and 0.02), were prepared by using the chemical reaction in solid-state ways, and test influence of partial replacement of Bi and Ca with Sb and Cd respectively on the superconducting properties, all samples were sintered at the same temperature (850 oC) and for the same time (195 h). The structural analysis of the prepared samples was carried out using X-ray diffraction (XRD) measurements performed at room temperature, scanning electron microscope (SEM) and dc electrical resistivity was measured as a function of temperature. It was found that the sample prepared by partial substitution of Sb at ratio (x= 0.2