Mechanical Properties Enhancement of Conventional Glass Ionomer Cement by Adding Zirconium Oxide Micro and Nanoparticles
...Show More Authors

The aim of this work is to enhance the mechanical properties of the glass ionomer cement GIC (dental materials) by adding Zirconium Oxide ZrO2 in both micro and nano particles. GIC were mixed with (3, 5 and 7) wt% of both ZrO2 micro and nanoparticles separately. Compressive strength (CS), biaxial flexural strength (BFS), Vickers Microhardness (VH) and wear rate losses (WR) were investigated. The maximum compression strength was 122.31 MPa with 5 wt. % ZrO2 micro particle, while 3wt% nanoparticles give highest Microhardness and biaxial flexural strength of 88.8 VHN and 35.79 MPa respectively. The minimum wear rate losses were 3.776µg/m with 7 wt. % ZrO2 nanoparticle. GIC-containing ZrO2 micro and nanoparticles is a promising restorative material with improved mechanical properties expect wear rate losses.

 

Crossref
View Publication Preview PDF
Quick Preview PDF
Publication Date
Wed Mar 20 2019
Journal Name
Al-khwarizmi Engineering Journal
Improvement of Mechanical and Fatigue Properties for Aluminum Alloy 7049 By Using Nano Composites Technique
...Show More Authors

The aim of present work is to improve mechanical and fatigue properties for Aluminum alloy7049 by using Nano composites technique. The ZrO2 with an average grain diameter of 30-40 nm, was selected as Nano particles, to reinforce Aluminum alloy7049 with different percentage as, 2, 4, 6 and 7 %. The Stir casting method was used to fabricate the Nano composites materials due to economical route for improvement and processing of metal matrix composites. The experimental results were shown that the adding of zirconium oxide (ZrO2) as reinforced material leads to improve mechanical properties. The best percentage of improvement of mechanical properties of 7049 AA was with 4% wt. of ZrO2 about (7.76% ) for ultim

... Show More
View Publication Preview PDF
Crossref (3)
Crossref
Publication Date
Fri Jul 01 2016
Journal Name
Journal Of Engineering And Sustainable Development
EVALUATION OF MECHANICAL PROPERTIES OF HIGH PERFORMANCE SELF-CONSOLIDATED CONCRETE ENHANCED BY DISCRETE STEEL AND POLYPROPYLENE FIBERS
...Show More Authors

High performance self-consolidating concrete HP-SCC is one of the most complex types of concrete which have the capacity to consolidated under its own weight, have excellent homogeneity and high durability. This study aims to focus on the possibility of using industrial by-products like Silica fumes SF in the preparation of HP-SCC enhanced with discrete steel fibers (DSF) and monofilament polypropylene fibers (PPF). From experimental results, it was found that using DSF with volume fraction of 0.50 %; a highly improvements were gained in the mechanical properties of HP-SCC. The compressive strength, splitting tensile strength, flexural strength and elastic modulus improved about 65.7 %, 70.5 %, 41.7 % and 80.3 % at 28 days age, respectively

... Show More
View Publication Preview PDF
Publication Date
Mon Dec 25 2000
Journal Name
Journal Of Advanced Research In Fluid Mechanics And Thermal Sciences
Enhancement of nanofluid heat transfer in elliptical pipe and helical micro tube heat exchanger
...Show More Authors

Publication Date
Sun Jul 09 2023
Journal Name
Journal Of Engineering
Assessment of Modified - Asphalt Cement Properties
...Show More Authors

The Asphalt cement is produced as a by-product from the oil industry; the asphalt must practice further processing to control the percentage of its different ingredients so that it will be suitable for paving process. The objective of this work is to prepare different types of modified Asphalt cement using locally available additives, and subjecting the prepared modified Asphalt cement to testing procedures usually adopted for Asphalt cement, and compare the test results with the specification requirements for the modified Asphalt cement to fulfill the paving process requirements. An attempt was made to prepare the modified Asphalt cement for pavement construction in the laboratory by digesting each of the two penetration grade Asphalt c

... Show More
View Publication Preview PDF
Crossref
Publication Date
Mon Oct 28 2019
Journal Name
Periodicals Of Engineering And Natural Sciences (pen)
Kinetic profile of silver and zinc oxide nanoparticles by intraperitoneal injection in mice , a comparative study
...Show More Authors

View Publication
Scopus (3)
Scopus Crossref
Publication Date
Mon Apr 01 2019
Journal Name
Journal Of Engineering
Improving the Physical and Mechanical Properties of Fireclay Refractory Bricks by Added Bauxite
...Show More Authors

In this study, the investigation of Local natural Iraqi rocks kaolin with the addition of different proportions of bauxite and its effect on the physical and mechanical properties of the produced refractories was conducted. Kaolin/bauxite mixture was milled and classified into various size fractions, the kaolin (less than 105 μm) and the bauxite (less than 70μm). The specimens were mixed from kaolin and bauxite in ranges B1 (95+5)%, B2 (90+10)%, B3(85+15)%, and B4 (80+20)%  respectively. The green specimens were shaped by the semi-dry method using a hydraulic press and a molding pressure of 7 MPa with the addition of (9-12) %wt. of PVA ratio. After molding and drying, the specimens were fired at (1100, 1200 and 13

... Show More
View Publication Preview PDF
Crossref (2)
Crossref
Publication Date
Fri Mar 15 2019
Journal Name
Al-khwarizmi Engineering Journal
Studying the effect of Different wt % AL2O3 Nanoparticles of 2024Al Alloy / AL2O3 Composites on Mechanical Properties
...Show More Authors

 

The nanocompsite of alumina (Al2O3) produced a number of beneficial effects in alloys. There is increasing in resistance of materials to surface related failures , such as the mechanical properties , fatigue and stress corrosion cracking .The experimental results observed that the adding of reinforced  nanomaterials  type Al2O3  enhanced the   HB hardness, UTS, 0.2 YS and ductility of 2014 Al/Al2O3 nano composites . the analysis of experiments, indicated that The maximum enhancement was observed at 0.4 wt.% Al2O3. The ultimate improvement percentage were 15.78% HB hardness, 18.1% (UTS), 12.86% (

... Show More
View Publication Preview PDF
Crossref (5)
Crossref
Publication Date
Mon Dec 25 2017
Journal Name
Biomedical And Pharmacology Journal
Effect of the Addition of Polyamide (Nylon 6) Micro-Particles on Some Mechanical Properties of RTV Maxillofacial Silicone Elastomer Before and After Artificial Aging
...Show More Authors

View Publication
Crossref (7)
Crossref
Publication Date
Sat Sep 23 2017
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Dielectric Properties of High Alumina Glass
...Show More Authors

High   Alumina   Glasses   "Alumina   Silicate   Glasses"   was prepared by utilizing powder technology technique. The starting materials are wasted soda-lime glass from an industrial site, Iraqi­ Duekhla raw kaolin and small amounts of potassium carbonates.

X-ray Diffraction and FTIR analysis show complete vitreous glasses are obtained. Increasing Alumina content plays an obvious role in improving physical and mechanical properties of the prepared high  alumina  glass.   In  addition,  the   increased  alumina  content enhanced the dielectric constant and reduced dielectric loss. These results may be interpreted as du

... Show More
View Publication Preview PDF
Publication Date
Tue Jun 30 2015
Journal Name
Al-khwarizmi Engineering Journal
Morphology and Mechanical Properties of (Epoxy/PVC) Blend
...Show More Authors

Abstract

     In this research, the morphology and mechanical properties of (Epoxy/PVC) blend were investigated.  (EP/PVC) blend was prepared by manual mixing of epoxy resin with different weight ratios of (Poly vinyl chloride (PVC) after dissolving it in cyclohexanon). Five sheets of polymer blends in wt% included (0%, 5%, 10%, 15% and 20%) of PVC were prepared at room temperature. Tests were carried out to study some mechanical properties for these blends and compared with the properties of pure epoxy. The morphology of the prepared materials was examined to study the compatibility nature between the two polymers under work. It was found that the best ratio of addition is (20%) of PVC.

... Show More
View Publication Preview PDF