The combination of carbon nanotubes (CNT) and conducting polymers offers an attractive route for the production of novel compounds that can be used in a variety of applications such as sensors, actuators, and molecular scale electronic devices. In this work, functionalized multiwall carbon nanotubes (f-MWCNTs) were added in different load ratios (3 wt%, 5 wt% and 10 wt%) to thiophen (PTh) polymer to procedure PTh/CNTs nanocomposite and deposited on porous silicon substrate by electropolarization. Photoconductive detectors were fabricated using PTh/f-MWCNTs matrix to work in the near region and middle IR regions. These detectors were illuminated by semiconductor laser diode wavelength of 808(nm) and Nd-YAG laser of wavelength 1064 (n

Sheets of Epoxy (EP) resin with addition of TiO2 of grain size (1.5μm, and 50nm) and weight percentage (1%, 3%, and 5%) were prepared. Discs of 20mm diameter and 3mm thickness were cut for dielectric measurements. Dielectric properties (dielectric constant, dispassion factor and electrical conductivity) over the frequency range 102 -106 Hz were measured.
Comparison was made between the effect of micro and nano particles of TiO2 on the dielectric properties of EP composites with different weight percentage. Epoxy composites with micro sized particles of TiO2 were observed to have the better values of dielectric properties.

Background: Marginal adaptation is critical for long – term success of crown and bridge restoration. Computer aided design / computer aided manufacture (CAD/ CAM) system is gaining more importance in the fabrication of dental restoration. Objective: The aim of this study is to evaluate the effect of crystallization firing on the vertical marginal gap of IPS. emax CAD crowns which fabricated with two different CAD/CAM systems .Materials and Methods: Twenty IPS e.max CAD crowns were fabricated. We had two major groups (A, B) (10 crowns for each group) according to the CAD/CAM system being used: Group A: fabricated with Imes - Icore CAD/CAM system; Group B: fabricated with In Lab Sirona CAD/CAM system. Each group was subdivided into two s

ABSTRACT: Polypyrrole and polypyrrole / silver nanocomposites were fabricated by in-situ polymerization employing Ammonium Persulphate as an oxidizing agent. Nanocomposites were synthesized by combining polypyrrole and silver nanoparticles in various weight percentages (0.1%, 0.5%, 3%, 5% and 7% wt.). Crystallographic data were collected using X-ray diffraction.  PPy particles were found to have an orthorhombic symmetry. In contrast, PPy/Ag nanocomposites were reported to have monoclinic structure. The crystallite size was determined by XRD using Scherrer equation and considered to be within 49 nm range. DC conductivity of pelletized samples was evaluated in the temperature range of 323.15k to 453.15k. The conductiv

This research presents the kinetics of the saponification reaction using mixed fats of olein and stearin [in the ratio (3:1)] with NaOH solution. In this reaction, excess solution of NaOH was used to ensure the reaction being irreversible. Three parameters were varied to show their effects on the reaction rate .They are: percentage excess of NaOH solution (10 % - 100 %) , temperature (100-150)oC , and stirring speed (400-1100) rpm. It was noticed that increasing the percentage excess of NaOH solution enhances the rate of reaction while increasing temperature decreases the reaction rate since it is exothermic reaction.    Increasing stirring speed also improves the reaction rate because it is mass transfer controlled .Calcu

The study involves removing of [Alizarin Red S (ARS) and Alizarin yellow R (AYR)] by using Iraqi Siliceous Rocks Powder (SRP). Adsorption isotherms were studied and the factors which influence it, such as temperature and salt effect. Adsorption isotherms of (ARS) were found to be comparable to Temkin equation. Adsorption isotherms of (AYR) were found to be comparable to Freundlich equation. The adsorption process on this surface was studied at different temperatures. The results showed that the adsorption of (ARS,AYR) on surface increased with increasing temperature (Endothermic process). According to the above results the thermodynamic functions (ΔH, ΔG, ΔS) were calculated. The adsorption quantity increasing for (ARS, AYR) with increas

The thermal properties (thermal transfer and thermal expansion coefficient) of the enhanced epoxy resin (MWCNT / x-TiO₂) were studied by weight ratios with the values (0%, 3%, 5%, 7% and 10%) and a constant ratio of 3% of MWCNT. The ultrasonic technology was used to prepare the neat and composites which were then poured into Teflon molds according to standard conditions. Thermo-analyzer sensor technology was used to measure thermal transfer (thermal conductivity, thermal flow, thermal diffusion, thermal energy and heat resistance). The thermal conductivity, flow, and thermal conductivity values were increased sequentially by increasing the weight ratio of the filler while the results of stored energy values an

Several schottky diodes were fabricated from polyaniline/ Carbon nanotube (single and multiwalled) composites. These composites were synthesized with different concentration and two carbon nanotubes types, Single and Multi-Walled Carbon Nanotubes (SWCNT & MWCNT). Aluminum and silver paste were chosen as schottky and ohmic contact respectively. physical and electrical were used to studied these composite by using Atomic Force Microscopy (AFM) and electrical measurements. The Root Mean Square RMS surface roughness of the composite samples was found to be around 4nm. The currentvoltage characteristic were measurements for all samples in the bias range ±15V at room temperature. The results shows the increasing in carbon nanotubes concentration