Abstract

    Corrosion-fatigue occurs by the combined actions of cyclic loading and corrosive environment. The effect of shot peening on cumulative corrosion-fatigue life of 1100-H12 Al alloy was investigated. Before fatigue testing, specimens were submerged in 3.5%NaCl solution for 71 days. Constant fatigue tests were performed with and without corrosive environment. Cumulative corrosion-fatigue tests were also carried out in order to determine the fatigue life before and after shot peening. The constant fatigue life was significantly reduced due to corrosive environment and the endurance fatigue limit was reduced by 13% compared with dry fatigue. In case of shot peening the cumul

M. domestica is the most important insect that transmit pathogens for diseases in the world. The use of nanotechnology is eco-friendly method in control pests. The study aims to investigate the feasibility of bio-manufacturing nanocapsules of fungal secondary metabolites in order to improve the efficiency of metabolite and assess their inhibitory effect on the acetylcholine esterase enzyme in housefly larvae. An equal mixture of organic solvents, ethyl acetate and dichloromethane, was used to extract the metabolic products of the fungus M. anisopliae, (PEG4000) and chitosan was used in the preparation of nanocapsules. The results of the DLS granular size assay showed that the size of the extract particles and the size of the chitosan and

The pandemic SARS-CoV-2 is highly transmittable with its proliferation among nations. This study aims to design and exploring the efficacy of novel nirmatrelvir derivatives as SARS entry inhibitors by adapting a molecular modeling approach combined with theoretical design. The study focuses on the preparation of these derivatives and understanding their effectiveness, with a special focus on their binding affinity to the S protein, which is pivotal for the virus’s access to the host cell. Considering molecular docking aspects in the scope of a study on nirmatrelvir derivatives and S protein, dynamics simulations with 25 nanoseconds of their binding are explored. The study shows that these derivatives might work as effective antivi

This research focuses on improvement of the corrosion behaviour of commercial pure titanium (Ti) grade II when exposed to Hank’s solution through different surface treatments. The disc shape of titanium samples were constructed to be divided according to their surface treatment. The first experimental group the Ti sample was exposed to computer numerical control (CNC) fiber laser machine. Whereas, the other experimental group the Ti sample was only coated with Polyetherketon keton (PEKK) by using carbon dioxide (CO2) laser technique while the last experimental group the Ti sample was treated with CNC fiber laser followed by PEKK coating by using CO2 laser technique. All were compared with the untreated control group. The electrochemical a

In this search, Ep/SiO2 at (3, 6, 9, 12 %) composites is prepared by hand Lay-up method, to measure the change in the thermal conductivity and Impact Strength of epoxy resin before and after immersion in H2SO4 Solution with a 0.3N for 10 days. The results before immersion decreases with the increase of the weight ratios of the reinforcement material (SiO2), It changed from (82.6×10-2 to 38.7×10-2 W/m.°C) with change weight ratios from (3 to 12) % respectively, but after immersion time in the chemical solution where it was (65.6×10-2 W/m.°C) at the weight ratios (6 %) and became (46.6 × 10-2 W/m.°C) after immersion in sulfuric acid. The results of the Impact strength decreased by increasing the percentage weight ratio, it changed f

This research explored the performance of steel fiber concrete-filled stainless-steel tube columns stiffened with embedded carbon steel T-sections with various steel fiber ratios under biaxial bending conditions. A numerical parametric analysis was adopted, using finite element modeling with Abaqus CAE/2021 to evaluate the effects of the fiber ratio (ranging from 0% to 1.5%) on the load-bearing capacity and deflection behavior of columns. In addition, the compressive strength of concrete ranged between 45 and 65 MPa. An increase in the fiber ratio led to a substantial improvement in the ultimate load-bearing capacity (up to 24%), a reduction in deflection (of approximately 49%), and an improvement in column ductility, which were obt