Nanocrystalline copper sulphide (Cu2-xS) powders were synthesized by chemical precipitation from their aqueous solutions composed of different molar ratio of copper sulfate dehydrate (CuSO4.5H2O) and thiorea (NH2)2CS as source of Cu+2, S-2 ions respectively, and sodium ethylene diamine tetra acetic acid dehydrate (EDTA) as a complex agent. The compositions, morphological and structural properties of the nanopowders were characterized by energy dispersive spectroscopy (EDS), scanning electron microscope (SEM), and X-ray diffraction (XRD), respectively. The compositional results showed that the copper content was high and the Sulfur content was low for both CuS and Cu2S nanopowders. SEM images shows that all products consist of aggregate o

Non thermal argon plasma needle at atmospheric pressure was constructed. The experimental set up was based on simple and low cost electric components that generate electrical field sufficiently high at the electrodes to ionize various gases which flow at atmospheric pressure. A high AC power supply was used with 9.6kV peak to peak and 33kHz frequency. The plasma was generated using two electrodes. The voltage and current discharge waveform were measured. The temperature of Ar gas plasma jet at different gas flow rate and distances from the plasma electrode was also recorded. It was found that the temperature increased with increasing frequency to reach the maximum value at 15 kHz, and that the current leading the voltage, which demonstra

Complexes of Cr(III)andNi(II) ions with phthalate sulphanilate snthranillate hippurte and glycinate ions have been preparcd then the Nephelauxetic

Abstract

     In this research, the morphology and mechanical properties of (Epoxy/PVC) blend were investigated.  (EP/PVC) blend was prepared by manual mixing of epoxy resin with different weight ratios of (Poly vinyl chloride (PVC) after dissolving it in cyclohexanon). Five sheets of polymer blends in wt% included (0%, 5%, 10%, 15% and 20%) of PVC were prepared at room temperature. Tests were carried out to study some mechanical properties for these blends and compared with the properties of pure epoxy. The morphology of the prepared materials was examined to study the compatibility nature between the two polymers under work. It was found that the best ratio of addition is (20%) of PVC.

A research include of synthesized five member ring, which has been synthesized by condensation of 2-(1-(4- hydroxyphenyl) ethylidene)hydrazine-1-carbothioamide[I] with α-chloro ethylacetate in sodium acetate (fused) to form ethyl 2-(4-(1-((4-oxo-2-thioxopyrrolidin-3-ylidene)hydrazono) ethyl)phenoxy)acetate [II]. After that reacted [II]with hydrazine hydrate to resulting compound [III]. Compound [III] was refluxed with 4-aminobenzoicacid in excess of phosphorus oxy chloride give compound [IV],the later compound [IV] interact with acetyl acetone or ethylacetoacetate give to pyrazole and pyrazoline derivatives[V],[VI]. While when reacted with different aromatic aldehydes and one ketone consistence Schiff base derivatives [VII]a-e . The FTIR a

In this paper a new series of morpholine derivatives was prepared by reacting the morpholine with ethyl chloro acetate in the presence triethylamine as a catalyst in benzene gave morpholin-N-ethyl acetate(1) which reacted with hydrazine hydrate in ethanol, and gave morpholin-N-ethyl acetohydrazide (2) . Morpholin-N-aceto semithiocarbazide (3) were prepared by reacting compound(2) with ammonium thiocyanate , concentrated hydrochloric acid and ethanol as a solvent .Compound (3) reacted with sodium hydroxide and hydrochloric acid to give 5-(morpholin-N-methylene)-1H-1,2,4-triazole-3-thiol (4) .The new series of 1,2,4-triazol derivatives (5-8) was synthesized by reaction of compound(4) with formaldehyde , DMF as a solvent and different