Background: Poly (methyl methacrylate) has several disadvantages (poor mechanical properties) like impact and transverse strength. In order to overcome these disadvantages, several methods were used to strengthen the acrylic resin by using different fibers or fillers. This study was conducted to evaluate the effect of Plasma treatment of the fiber on mechanical properties Poly (methyl methacrylate) denture base material. Materials and methods: Specimens were prepared from poly methyl metha acrylic (PMMA) divided according to present of fiber into 4 groups (first group without fiber as control group, second group with Plasma treated polyester fibers, third group with Plasma treated polyamide fibers and fourth group Plasma treated combination

Burnishing improves fatigue strength, surface hardness and decrease surface roughness of metal because this process transforms tensile residual stresses into compressive residual stresses. Roller burnishing tool is used in the present work on low carbon steel (AISI 1008) specimens. In this work, different experiments were used to study the influence of feed parameter and speed parameter in burnishing process on fatigue strength, surface roughness and surface hardness of low carbon steel (AISI 1008) specimens. The first parameter used is feed values which were (0.6, 0.8, and 1) mm at constant speed (370) rpm, while the second parameter used is speed at values (540, 800 and 1200) rpm and at constant feed (1) mm. The results of the fatigue

A series of experiments have been taken out to test the validity of the effect of Aluminum hydrate on its interaction with Aluminum during sintering of aluminum metal matrix. The approach has been shown to be valid and several compositions have been fabricated. The alumina hydrate particle size and the amount of alumina hydrate in the composites are also shown to have an influence on the extent of densification.

The densities for all sintered specimens were measured. It was found that density increases as compaction pressure increases, the density decreases as particles size increases. At 400 MPa there is an optimum particles size which is (90-125) µm to reach maximum density and the density decreases as volume fraction increase

􀀤􀁅􀁖􀁗􀁕􀁄􀁆􀁗􀀑􀀃􀀬􀁑􀀃􀁗􀁋􀁌􀁖􀀃􀁕􀁈􀁖􀁈􀁄􀁕􀁆􀁋􀀏􀀃􀀤􀁊􀀤􀁏􀀔􀀐􀁛􀀬􀁑􀁛􀀶􀁈􀀕􀀃􀀋􀀤􀀤􀀬􀀶􀀌􀀃􀁆􀁒􀁐􀁓􀁒􀁘􀁑􀁇􀀃􀁄􀁏􀁏􀁒􀁜􀁖􀀃􀁓􀁕􀁈􀁓􀁄􀁕􀁈􀁇􀀃􀁉􀁒􀁕􀀃􀁇􀁌􀁉􀁉􀁈􀁕􀁈􀁑􀁗􀀃􀁛􀀃􀀋􀀓􀀑􀀖􀀏􀀃􀀓􀀑􀀙􀀃􀁄􀁑􀁇􀀃􀀓􀀑􀀜􀀌􀀃􀁅􀁜􀀃􀁐􀁈􀁏􀁗􀁌􀁑􀁊􀀃 􀁗􀁋􀁈􀁐􀀃 􀁌􀁑􀀃 􀁄􀁑􀀃 􀁈􀁙􀁄􀁆􀁘􀁄􀁗􀁈􀁇􀀃 􀁔􀁘􀁄􀁕􀁗􀁝􀀃 􀁗􀁘􀁅􀁈􀀃 􀀋􀀕􀀑􀀘􀀍􀀔􀀓􀀐􀀖􀀃 􀁗􀁒􀁕􀁕􀀌􀀑􀀃 􀀤􀀤􀀬􀀶􀀃 􀁚􀁌􀁗􀁋􀀃 􀁇􀁌􀁉􀁉

Iron-Epoxy composite samples were prepared by added
different weight percentages (0, 5, 10, 15, and 20 wt %) from Iron
particles in the range of (30-40μm) as a particle size. The contents
were mixed carefully, and placed a circular dies with a diameter of
2.5 cm. Different mechanical tests (Shore D Hardness, Tensile
strength, and Impact strength ) were carried out for all samples. The
samples were immersed in water for ten weeks, and after two weeks
the samples were take-out and drying to conducting all mechanical
tests were repeated for all samples. The hardness values increased
when the Iron particle concentration increased while the Impact
strength is not affected by the increasing of Iron particles
c

Background: Poly propylene fibers with and without silane treatment have been used to reinforce heat cure denture base acrylic but, some mechanical properties like transverse strength, impact strength, tensile strength, hardness, wear resistance and wettability. Which are related to the clinical use of the prosthesis are not evaluated yet. The aim of the study is to identify the influence of incorporation of treated and untreated fibers on these properties Materials and methods: Eighty four heat cure acrylic specimens were constructed by conventional flasking technique. They were divided into six groups according to the tests and each group was subdivided into two subgroups control and experimental groups (seven samples for each subgroup

A novel encapsulated deep eutectic solvent (DES) was introduced for biodiesel production via a two-step process. The DES was encapsulated in medical capsules and were used to reduce the free fatty acid (FFA) content of acidic crude palm oil (ACPO) to the minimum acceptable level (< 1%). The DES was synthesized from methyltriphenylphosphonium bromide (MTPB) and p-toluenesulfonic acid (PTSA). The effects pertaining to different operating conditions such as capsule dosage, reaction time, molar ratio, and reaction temperature were optimized. The FFA content of ACPO was reduced from existing 9.61% to less than 1% under optimum operating conditions. This indicated that encapsulated MTPB-DES performed high catalytic activity in FFA esterificatio