This research presents the results of the tests of the physical, chemical and biological treatments performed on the industrial effluent of Al-Rashid Factory for vegetable oils during January to July, 2010.      Some environmental parameters such as temperature, electrical conductivity(ec), Biological oxygen demand(bod), chemical oxygen demand(cod), total suspended solids(tss), dissolved oxygen(o2) and total dissolved solids(tdc) have been investigated. The study shows that the industrial effluent contains a percent of organic pollution and in different values, and that it is responsible for the (bod), which records (5.15-67)ppm, while the (cod) ranges between (25-170.5)ppm, the (ec) values range between (

This study was conducted to know the effect of some phenotype characteristics of corn plant on infection by (CSB), using 13 genotypes of corn plant, planting during autumn season 1997 and 1998. The result revealed that the mean of plant height (with male flowering) was (183-219) cm, the mean of leaf No./ plant in all genotypes was (16-18) leaf but the leaf area of plant was (4350-6249) cm2, there were significant differences of phenotype characteristics between genotypes ,the percentage of infection by (CSB) was (5.9-35.9),% the result showed that the phenotype characteristics had non effect on the infection percentage by (CSB) and the correlation coefficient was not significant.

The ceramic compound Mg1-xSixAl2O4 (x= 0, 0.1, 0.2, 0.3, 0.4) was prepared from nano powder of Al2O3 and MgO doped with Nano powder of SiO2 at different molar ratios. The specimens were prepared by standard chemical solid reaction technique and sintered at 1450 oC. Structure of the specimens was analyzed by using X-ray diffraction (XRD). The X-ray patterns of the specimens showed the formation of pure simple cubic spinel structure MgAl2O4 phase with space group of ̅ . The average grain size and surface topology were studied by atomic force microscopy. The results showed that the average grain size was about 73-90 nm. The DC electrical properties of the specimen were measured. The apparent density was found to increase and the porosity a

The influence of the reaction gas composition during the DC magnetron sputtering process on the structural, chemical and optical properties of Ce-oxide thin films was investigated. X-ray diffraction (XRD) studies confirmed that all thin films exhibited a polycrystalline character with cubic fluorite structure for cerium dioxide. X-ray photoelectron spectroscopy (XPS) analyses revealed that cerium is present in two oxidation states, namely as CeO2 and Ce2O3, at the surface of the films prepared at oxygen/argon flow ratios between 0% and 7%, whereas the films are completely oxidized into CeO2 as the aforementioned ratio increases beyond 14%. Various optical parameters for the thin films (including an optical band gap in the range of 2.25–3.

The current research reports the preparation and fabrication of the silver paste conductor which is employed as a soldering material for electro – optical components ohmic interconnections. The prepared paste possesses electrical characteristics identical to the ohmic connectors as its observable from resistance – temperature variation. Moreover, the I – V characteristics obeys Ohm’s law and this dependency was further confirmed by the nearly constant capacitance measurements with voltage and frequency. A noticeable improvement in electrical conductivity, compared to the pure silver paste sample, was noted for samples prepared by mixing predetermined weight ratios of brass and copper. Furthermore, stability of electrical resistan