In this research, Mn-doped TiO2 thin films were grown on glass, Si and OIT/glass substrates by R.F magnetron sputtering technique with thicknesses (250 nm) using TiO2:Mn target under Ar gas pressure and power of 100 Watt. Through the results of X-ray diffraction, the prepared thin films are of the polycrystallization type after the process of annealing at 600°C for two hour The average crystalline size were 145.32, 280.97 and 261.23 nm for (TiO2:Mn) thin film on glass, Si and OIT/glass substrates respectively, while the measured surface roughness is between 0.981nm and 1.14 nm. The fabricated (TiO2:Mn) thin film on glass sensors have high sensitivity for hydrogen( H2 reducing gas) compared to the sensitivity for hydrogen gas on Si and OIT/

The investment however "was its description and meaning, it remains a resident" in the composition of capital assets located in the forefront of the creation of productive assets, and this means that the investment in the productive sectors is a priority in achieving capital accumulation, on any other investment that takes place with the stages of advanced development of formation , not forgetting "to humans and investment humans as head of real money product, the source of the economic surplus and accumulation, and the source of producing values, and if human labor was the source of value, and the human was the source of work, therefore humanitarian work on different levels and skills presents capital", so the investment in huma

     In this work, the detection of zinc (Zn) ions that cause water pollution is studied using the CSNPs- Linker-alkaloids compound that was prepared by linking extracted alkaloids from Iraqi Catharanthus roseus plant with Chitosan nanoparticles (CSNPs) using maleic anhydride. This compound is characterized by an X-ray diffractometer (XRD) which shows that it has an orthorhombic structure with crystallite size in the nano dimension. Zeta Potential results show that the CSNPs-Linker-alkaloids carried a positive charge of 54.4 mV, which means it possesses high stability.  The Fourier transform infrared spectroscopy (FTIR) shows a new distinct band at 1708.93 cm-1 due to C=O esterification. Scanning electron microscope (SEM) image

The aim of this paper was to investigate the removal efficiencies of Zn⁺² ions from wastewater by adsorption (using tobacco leaves) and forward osmosis (using cellulose triacetate (CTA) membrane). Various experimental parameters were investigated in adsorption experiment such as: effect of pH (3 - 7), contact time (0  - 220) min, solute concentration (10 - 100) mg/l, and adsorbent dose (0.2 - 5)g. Whereas for forward osmosis the operating parameters studied were: draw solution concentration (10 - 150) g/l, pH of feed solution (4 - 7), feed solution concentration (10 - 100) mg/l. The result showed that the removal efficiency by using adsorption was 70% and the removal efficiency by using forward osmosis was 96.2 %. 

A rapid and sensitive method for analysis of amino acid hydrolysates of nigella sativa L seed has been developed using O-phthaldialehyde(OPA ) as a pre-column derivatizing agent. OPA reagents in the presence of mercaptoethanol react rapidly with primary amino acids ( less than 60 sec.) to form isindole derivatives which easily separated with good selectivity on ODS column. Resolution of amino acid derivatives is carried out with a methanol gradient in 0.01 maqueous sodium acetate. pH 7.1 . The quantitation of amino acid derivatives is reproducible within an average relative deviation of + 1.4% the linearity for most amino acids were more than 0.9993 with detection limit of 0.2 ppm. 15 amino acid were detected in the analysis of

The paper discusses the structural and optical properties of In 2 O 3 and In 2 O 3-SnO 2 gas sensor thin films were deposited on glass and silicon substrates and grown by irradiation of assistant microwave on seeded layer nucleated using spin coating technique. The X-ray diffraction revealed a polycrystalline nature of the cubic structure. Atomic Force Microscopy (AFM) used for morphology analysis that shown the grain size of the prepared thin film is less than 100 nm, surface roughness and root mean square for In 2 O 3 where increased after loading SnO 2 , this addition is a challenge in gas sensing application. Sensitivity of In 2 O 3 thin film against NO 2 toxic gas is 35% at 300 o C. Sensing properties were improved after adding Tin Oxi

The success of endodontic therapy is relied on radicular system cleaning, shaping, elimination of micro-organisms, and three dimensional filling of the radicular complex.This study was conducted to develop and assess new root canal sealer incorporating nano-sized bioactive glass into Gutta Flow II. The following concentration was used depend on a pilot study included adding (3%) of 45S5 bioactive glass into the Gutta Flow II. These materials were tested through assessment bioactivity. bioactivity test was undertaken after immersion of the tested samples into PBS for three days, seven days, fourteen days, and twenty eight days using FTIR too. study was found that it’s peaks was appear at level 800-1000 cm-1. The results showed that GFII gr