A new Turbidimetric method characterized by simplicity, accuracy and speed for determination of Hydronium ion by continuous flow injection analysis. The method was based on the formation of complex Zn3[Fe(CN)6] for Zinc(II) that was eluted by Hydronium ion from cation exchanger column with Potassium hexacyanoferrate(III) for the formation of a pale yellow precipitate and this precipitate was determined using homemade Linear Array Ayah-5SX1-T-1D continuous flow injection analyser. The optimum parameters were 2.7 mL.min-1 flow rate using H2O as a carrier stream, 1.7 mL.min-1 reagent stream, 110 L sample volume and open valve for the purge of the sample segment. Data treatment shows that linear range 0.01-0.1 mol.L-1 for each acids (HClO

Material Requirements Planning System (MRP) is considered as one of the planning and controlling of production and inventory systems which is used to prepare plan of the final production requirements and its parts of subcomponents raw materials and the time at which it was needed for the purpose of preparing orders of production and purchase.

The problem of the present work is represented in the general company of electrical industrialization adoption of traditional methods and personal experience of the process of the products and\or purchase quantity and inventory quantities and limiting the required time for acquiring the required quantities of the materials and parts used in the finish product of the

The 2-D Resistivity imaging survey conducted within the desert area to meet the region's need of groundwater, due to the absence of any surface water, in addition, there are no any geophysical studies carried out previously. Ten point survey was performed to study the ground water aquifers in the southwest of Samawah city, Iraq. The length of the survey line in each point survey is 1200 meters by using 120 electrodes with 10 meters electrode spacing by applying Wenner-Schlumberger array. There are three main resistivity zones in the study area. The first resistivity zone ranging between 2.00-10.1 ohm.m, locate at shallow depth, represented Quaternary deposits. The second resistivity zone ranging between 22.8-51.3 ohm.m, it represents bea

The azo dye brilliant reactive red K-2BP (λmax = 534 nm) is widely used for coloring textiles because of its low-cost and tolerance fastness properties. Wastewaters treatment that contains the dye by conventional ways is usually inadequate due to its resistance to biological and chemical degradation. During this study, the continuous reactor of an advanced oxidation method supported the use of H₂O₂/sunlight, H₂O₂/UV, H₂O₂/TiO₂/sunlight, and H₂O₂/TiO₂/UV for decolorization of brilliant reactive red dye from the effluent. The existence of an optimum pH, H₂O₂ concentration, TiO₂ concentration, and d

Epoxy (EP) – Silica (SiO2) composites are well known composites used in microelectronic industry . So it is important to study their dielectric behavior under different conditions such as
the presence carbon black (UV absorber) and immersion in the water for 30 days .
Dielectric properties were calculated over the frequency range 102 – 106 Hz for epoxy composites with different weight % of micrometer 1.5μm SiO2 particles (60%, 65% and 70wt%) modified with 0.5wt% silane coupling agent to improve adhesion between EP and SiO2 phases .

In the present work, pulsed laser deposition (PLD) technique was applied to a pellet of Chromium Oxide (99.999% pure) with 2.5 cm diameter and 3 mm thickness at a pressure of 5 Tons using a Hydraulic piston. The films were deposited using Nd: YAG laser λ= (4664) nm at 600 mJ and 400 number of shot on a glass substrate, The thickness of the film was (107 nm). Structural and morphological analysis showed that the films started to crystallize at annealing temperature greater than 400 oC. Absorbance and transmittance spectra were recorded in the wavelength range (300-
4400) nm before and after annealing. The effects of annealing temperature on absorption coefficient, refractive index, extinction coefficient, real and imaginary parts of d

Thin films of pure polycarbonate (PC) with anthracene doping PC films for different doping ratios (10, 20, 30, 40, 50 and 60 ml) were prepared by using a casting method. The influence of anthracene doping ratio on photo-fries rearrangement of polycarbonate was systematic investigated. Furthermore, pure PC and anthracene doping PC films were irradiated via UV light at a wavelength (254 nm) for different periods (5, 240, 288, and 360 hrs). The photo-fries rearrangement occurring in pure PC and anthracene doping PC films were monitored using UV and FTIR spectroscopies. The photo-fries rearrangement leads to scission the carbonate linkage and formation phenylsalicylate and dihydroxybenzophenes. The result of the UV spectrum confirms disappea

In this paper a thin films of selenium was prepare on substrates of n-Si by evaporation in a vacuum technique with thickness about 0.5μm. And then an annealing process was done on samples at two temperature (100 and 200) C ° in a vacuum furnace (10^-3 torr).
Some structural, optical and mechanical properties of prepared thin films were measured. Results showed that the prepared film was the crystallization, optical transmittance and micro hardness of the prepared thin films increased significantly after annealing.