Assessment of Modified - Asphalt Cement Properties
...Show More Authors

The Asphalt cement is produced as a by-product from the oil industry; the asphalt must practice further processing to control the percentage of its different ingredients so that it will be suitable for paving process. The objective of this work is to prepare different types of modified Asphalt cement using locally available additives, and subjecting the prepared modified Asphalt cement to testing procedures usually adopted for Asphalt cement, and compare the test results with the specification requirements for the modified Asphalt cement to fulfill the paving process requirements. An attempt was made to prepare the modified Asphalt cement for pavement construction in the laboratory by digesting each of the two penetration grade Asphalt cement (40-50 and 60-70) with sulfur, fly ash, silica fumes. Three different percentages of each of the above mentioned additives have been tried using continuous stirring and heating at 150 ºC for 30 minutes.

The prepared modified Asphalt specimens were subjected to physical properties determination; the penetration, softening point, ductility before and after laboratory aging. It was concluded that all percentage of additives has reduced the penetration value of asphalt cement, an exception to that could be noticed when using asphalt cement (40-50) and when adding sulfur. Softening point was increased with the addition of all percentage of additives except that with 7% sulfur by wt. of asphalt cement (40-50) it decreased by 8%.

After aging in general, the penetration decreased by about 37% for control specimens and the softening point increased by about 8% for control specimens.

For asphalt cement 40-50 after aging, Sulfur has the least impact on ductility since it reduces it by 20%. Silica fumes have moderate effect on ductility when it reduces it by 35%, while fly ash shows the highest impact of 36%.

For asphalt cement 60-70 after aging, sulfur was able to almost retain its ductility, while fly ash shows moderate reduction in ductility within a range of 20-36% and silica fumes shows high impact on ductility in the range of 30-50%.

Crossref
View Publication Preview PDF
Quick Preview PDF
Publication Date
Wed Mar 10 2021
Journal Name
Baghdad Science Journal
Using Different Types of Projectiles to Make Avalanches to Avoid Human Being Disasters and Properties Destruction
...Show More Authors

Some geological phenomena as landslides and the mobilization of the accumulated rocks or soil are discussed in this research by using projectiles that cause mobility and falling of these land masses which are present at the top of mountains and edges of roads and streets to avoid accidents and human disasters which will occur if they are left falling by effect of climate or vibrating factors that are produced by performing dams, bridges and reservoirs. According to the different divisions of land masses groups, primary and secondary, which depend on type of movement and material arrangement that form the mobile masses, this research had shown the effect of projectiles for every type of cannons on the mobility of every groups of these rocks

... Show More
View Publication Preview PDF
Crossref
Publication Date
Mon Mar 08 2021
Journal Name
Baghdad Science Journal
A study the electrical properties of a Se:2.5%as thin films prepared by thermal cvaporation
...Show More Authors

thin films of se:2.5% as were deposited on a glass substates by thermal coevaporation techniqi=ue under high vacuum at different thikness

View Publication Preview PDF
Crossref
Publication Date
Fri Jun 12 2020
Journal Name
Test Engineering & Management
Studying the Optical Properties of CdSe Quantum Dots Prepared by Colloidal Method with Different pH Values
...Show More Authors

Preview PDF
Publication Date
Sun Dec 02 2018
Journal Name
Journal Of The College Of Education For Women
Nutritional and Evaluation properties of natural orange juice enriched by coconut milk as kids' nutritional drink
...Show More Authors

Coconut milk is considered as a natural drink that enhances the immunity and it is enriched by calcium, iron, magnesium and vitamin (C) and it is also safe drink for kids and bacterial anti-oxdant, and it may be used in the natural juices instead of the whole milk (cow milk) which is added to some juices. This study aimed to determine the nutritrnal value and the sensory evaluation properties of the natural orange juice enriched by canned coconut milk                                                 &nb

... Show More
View Publication Preview PDF
Publication Date
Mon May 01 2017
Journal Name
Journal Of The Mechanical Behavior Of Biomedical Materials
Bioactivity, cytocompatibility and thermal properties of experimental Bioglass-reinforced composites as potential root-canal filling materials
...Show More Authors

To evaluate the bioactivity and the cytocompatibility of experimental Bioglass-reinforced polyethylene-based root-canal filling materials. The thermal properties of the experimental materials were also evaluated using differential scanning calorimetry, while their radiopacity was assessed using a grey-scale value (GSV) aluminium step wedge and a phosphor plate digital system. Bioglass 45S5 (BAG), polyethylene and Strontium oxide (SrO) were used to create tailored composite fibres. The filler distribution within the composites was assessed using SEM, while their bioactivity was evaluated through infrared spectroscopy (FTIR) after storage in simulated body fluid (SBF). The radiopacity of the composite fibres and their thermal properties were

... Show More
View Publication Preview PDF
Crossref (27)
Crossref
Publication Date
Sat Dec 01 2018
Journal Name
Al-khwarizmi Engineering Journal
Effect Ti/AlTiN Multilayer Coating on the Crater Wear Process of Cutting Tool and Tribological Properties
...Show More Authors

Tool wear is a major problem in machining operations because the resulting material loss gradually changes of the machine tool. There many factors may leads to material loss like; friction, corrosion, and also it’s happened by rubbing during machining processes between the work piece and the tool. Dimensional accuracy of the work piece, and also the surface finish will be reducing by tool wear. It can also increase cutting force. In this study, we focused on the effect of the coating process on crater wear problems. Crater wear is caused by the flow between the chip and the rake face of the tool, whereas flank wear is caused by the contact between the tool and the work piece. In reducing crater wear, aluminum titanium nitride (AlTiN) u

... Show More
View Publication Preview PDF
Crossref
Publication Date
Tue Oct 30 2018
Journal Name
Iraqi Journal Of Physics
Annealing effects on optical and structural properties of chromium oxide thin film deposited by PLD technique
...Show More Authors

Optical properties of chromium oxide (Cr2O3) thin films which were prepared by pulse laser deposition method, onto glass substrates. Different laser energy (500-900) mJ were used to obtain Cr2O3 thin films with thickness ranging from 177.3 to 372.4 nm were measured using Tolansky method. Then films were annealed at temperature equal to 300 °C. Absorption spectra were used to determine the absorption coefficient of the films, and the effects of the annealing temperature on the absorption coefficient were investigated. The absorption edge shifted to red range of wavelength, and the optical constants of Cr2O3 films increases as the annealing temperature increased to 300 °C. X-ray diffraction (XRD) study reveals that Cr2O3 thin films are a

... Show More
View Publication Preview PDF
Crossref
Publication Date
Sun Apr 08 2018
Journal Name
Al-khwarizmi Engineering Journal
Microstructural Characterization and Mechanical Properties of Similar and Dissimilar Al Alloys Joined using Friction Stir Welding
...Show More Authors

The influence of pre- shot peening and welding parameters on mechanical and metallurgical properties of dissimilar and similar aluminum alloys AA2024-T3 and AA6061-T6 joints using friction stir welding have been studied. In this work, numbers of plates were equipped from sheet alloys in dimensions (150*50*6) mm then some of them were exposed to shot peening process before friction stir welding using steel ball having diameter 1.25 mm for period of 15 minutes. FSW joints were manufactured from plates at three welding speeds (28, 40, 56 mm/min) and welding speed 40mm/min was chosen at a rotating speed of 1400 rpm for welding the dissimilar pre- shot plates. Tow joints were made at rotational speed of 1000 rpm and welding speed of 40m/min f

... Show More
View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Sun Dec 09 2018
Journal Name
Baghdad Science Journal
Enhancement of the Tensile and the Compression Properties for Heat- Cured Acrylic Resin Denture Base Materials
...Show More Authors

This work aims to investigate the tensile and compression strengths of heat- cured acrylic resin denture base material by adding styrene-butadiene (S- B) to polymethyl methacrylate (PMMA). The most well- known issue in prosthodontic practice is fracture of a denture base. All samples were a blend of (90%, 80%) PMMA and (10%, 20%) S- B powder melted in Oxolane (Tetra hydro furan). These samples were chopped down into specimens of dimensions 100x10x2.5mm to carry out the requirements of tensile tests. The compression strength test specimens were shaped into a cylinder with dimensions of 12.7mm in diameter and 20mm in length. The experimental results show a significant increase in both tensile and compression strengths when compared to cont

... Show More
View Publication Preview PDF
Scopus (8)
Crossref (2)
Scopus Clarivate Crossref
Publication Date
Sun Jun 12 2011
Journal Name
Baghdad Science Journal
The optical properties of Poly methyl methacrylate (PMMA) polymers doped by Potassium Iodide with different thickness
...Show More Authors

Films of pure Poly (methyl methacrylate) (PMMA) doped by potassium iodide (KI) salt with percentages (1%) at different thickness prepared by casting method at room temperature. In order to study the effect of increasing thickness on optical properties, transmission and absorption spectra have been record for five different thicknesses(80,140,210,250,320)µm. The study has been extended to include the changes in the band gap energies, refractive index, extinction coefficient and absorption coefficient with thickness.

View Publication Preview PDF
Crossref