Assessment of Modified - Asphalt Cement Properties
...Show More Authors

The Asphalt cement is produced as a by-product from the oil industry; the asphalt must practice further processing to control the percentage of its different ingredients so that it will be suitable for paving process. The objective of this work is to prepare different types of modified Asphalt cement using locally available additives, and subjecting the prepared modified Asphalt cement to testing procedures usually adopted for Asphalt cement, and compare the test results with the specification requirements for the modified Asphalt cement to fulfill the paving process requirements. An attempt was made to prepare the modified Asphalt cement for pavement construction in the laboratory by digesting each of the two penetration grade Asphalt cement (40-50 and 60-70) with sulfur, fly ash, silica fumes. Three different percentages of each of the above mentioned additives have been tried using continuous stirring and heating at 150 ºC for 30 minutes.

The prepared modified Asphalt specimens were subjected to physical properties determination; the penetration, softening point, ductility before and after laboratory aging. It was concluded that all percentage of additives has reduced the penetration value of asphalt cement, an exception to that could be noticed when using asphalt cement (40-50) and when adding sulfur. Softening point was increased with the addition of all percentage of additives except that with 7% sulfur by wt. of asphalt cement (40-50) it decreased by 8%.

After aging in general, the penetration decreased by about 37% for control specimens and the softening point increased by about 8% for control specimens.

For asphalt cement 40-50 after aging, Sulfur has the least impact on ductility since it reduces it by 20%. Silica fumes have moderate effect on ductility when it reduces it by 35%, while fly ash shows the highest impact of 36%.

For asphalt cement 60-70 after aging, sulfur was able to almost retain its ductility, while fly ash shows moderate reduction in ductility within a range of 20-36% and silica fumes shows high impact on ductility in the range of 30-50%.

Crossref
View Publication Preview PDF
Quick Preview PDF
Publication Date
Tue Sep 01 2020
Journal Name
Baghdad Science Journal
Preparation of Polymeric Composites from Polypropylene and Palm Fronds and the Study of Some of Their Physical Properties
...Show More Authors

Abstract:
              In this study a type of polymeric composites from melting poly propylene as a basic substance with Palm fronds powder were prepared. Evaluation of polymeric composites was done by studying some of it is mechanical properties, which included:Yong modulus (E), Impact Strength (I.S), Brinell hardness (B.H) and Compression Strength (C.S). The polymeric composites were studied before and after reinforcment by comparing between them. There was an increase in resistance of Yong modulus (E), Impact Strength (I.S), Brinell hardness (B.H) and compression Strength (C.S). Also, the effect of some acids were studied such as (HCl, H2

... Show More
View Publication Preview PDF
Scopus Clarivate Crossref
Publication Date
Sun Dec 04 2011
Journal Name
Baghdad Science Journal
Effect of Laser Irradiation on the Optical Properties of SnO2 films Deposited by Post Oxidation of metal Films
...Show More Authors

Tin oxide films (SnO2) of thickness (1 ?m) are prepared on glass substrate by post oxidation of metal films technique. Films were irradiated with Nd:YAG double frequency laser of wavelength (532 nm) pulses of three energies (100, 500, 1000) mJ. The optical absorption, transmission, reflectance, refractive index and optical conductivity of these films are investigated in the UV-Vis region (200-900) nm. It was found that the average transmittance of the films is around (80%) at wavelength (550 nm) and showed high transmission (? 90 %) in the visible and near infrared region. The absorption edge shifts towards higher energies, which is due to the Moss-Burstien effect and it lies at (4 eV). The optical band gap increased with increasing of ene

... Show More
View Publication Preview PDF
Crossref
Publication Date
Sat Jan 19 2019
Journal Name
Iraqi Journal Of Agricultural Sciences
EFFECT OF TWO HARROWING SYSTEMS ON DECOMPOSITION OF ORGANIC MATTER, SOME SOIL PROPERTIES, GROWTH AND PRODUCTIVITY OF MAIZE
...Show More Authors

A field experiment was conducted at Abu-Ghrib during 2013- 2014 season to study the effect of harrowing systems on the decomposition and fermentation on organic matter(OM) when added and mixed with the soil under special technology, as well as its effect on the growth parameters and productivity of (Zea mays L. 5018). The experiment was laid out using factorial randomized complete block design (RCBD) in split-split design with three replications in SCL bare soil with a percent of moisture ranged from 16 – 18 %. The main plots were designated to the two systems of harrowing (Rotary Harrowand Disc Harrow ). The sub main plots were specified for two organic matters ( Sheep manure ,cow manure ) . Data were statistically analyzed, and

... Show More
View Publication
Crossref
Publication Date
Sun Jan 01 2017
Journal Name
International Journal Of Latest Trends In Engineering And Technology
Study the effect of number of nozzle on optical and structural properties of sno2 films grown by (apcvd)
...Show More Authors

View Publication Preview PDF
Crossref
Publication Date
Mon May 11 2020
Journal Name
Baghdad Science Journal
Acoustic and Thermal Insulation of Nanocomposites for Building Material: Improvement Of Sound And Thermal Insulation Properties Of Nanocomposite
...Show More Authors

This work aims to enhance acoustic and thermal insulation properties for polymeric composite by adding nanoclay and rock wool as reinforcement materials with different rations. A polymer blend of (epoxy+ polyester) as matrix materials was used. The Hand lay-up technique was used to manufacture the castings. Epoxy and polyester were mixed at different weight ratios involving (50:50, 60:40, 70:30, 80:20, and 90:10) wt. % of (epoxy: polyester) wt. % respectively. Impact tests for optimum sample (OMR), caustic and thermal insulation tests were performed. Nano clay (Kaolinite) with ratios ( 5 and 7.5% ) wt.% , also hybrid reinforcement materials involving (Kaolite 5 & 7.5 % wt.% + 10% volume fraction of rockwool ) were added as reinforcem

... Show More
View Publication Preview PDF
Scopus (5)
Crossref (4)
Scopus Clarivate Crossref
Publication Date
Wed Aug 29 2018
Journal Name
Biomedical And Pharmacology Journal
Comparison of Some Mechanical and Physical Properties of three Types of Impression Materials with Different Dental Implant Angulations
...Show More Authors

Choosing an appropriate impression material is a challenge for many dentists, yet an essential component to provide an excellent clinical outcome and improve productivity and profit. The purpose of present study was to compare wettability, tear strength and dimensional accuracy of three elastomeric impression materials, with the same consistencies (light-body). Three commercially available light body consistency and regular set 3M ESPE Express polyvinylsiloxane (PVS), 3M ESPE Permadyne polyether (PE), and Identium (ID), impression materials were comparedTear strength test, contact angle test and linear dimensional accuracy were evaluated for three elastic impression material. Among the three experimental groups PE impression materia

... Show More
View Publication
Crossref (2)
Crossref
Publication Date
Mon Oct 01 2018
Journal Name
The Saudi Dental Journal
Evaluation of some mechanical properties of a new silicone elastomer for maxillofacial prostheses after addition of intrinsic pigments
...Show More Authors

Objective: The approximate life span of a silicone maxillofacial prosthesis is as short as1.5–2 years of clinical service, then a new prosthesis should be fabricated. The most common reasonfor re-making the prosthesis is silicone mechanical properties degradation. The aim of this studywas to assess some mechanical properties of VST-30 silicone for maxillofacial prostheses after addi-tion of intrinsic pigments.Methods: Two types of intrinsic pigments (rayon flocking and burnt sienna); each of them wasincorporated into silicone. One hundred and twenty samples were prepared and split into 4 groupsaccording to the conducted tests (tear strength, hardness, surface roughness, and tensile strengthand elongation percentage) with 30 samples for ea

... Show More
View Publication
Scopus (19)
Crossref (18)
Scopus Clarivate Crossref
Publication Date
Mon Sep 25 2017
Journal Name
Biomedical And Pharmacology Journal
Comparative Study of the Effect of Incorporating SiO2 Nano-Particles on Properties of Poly methyl Methacrylate Denture Bases
...Show More Authors

View Publication
Crossref (22)
Crossref
Publication Date
Wed May 22 2024
Journal Name
Scientific Reports
The use of image analysis to study the effect of moisture content on the physical properties of grains
...Show More Authors
Abstract<p>Designing machines and equipment for post-harvest operations of agricultural products requires information about their physical properties. The aim of the work was to evaluate the possibility of introducing a new approach to predict the moisture content in bean and corn seeds based on measuring their dimensions using image analysis using artificial neural networks (ANN). Experimental tests were carried out at three levels of wet basis moisture content of seeds: 9, 13 and 17%. The analysis of the results showed a direct relationship between the wet basis moisture content and the main dimensions of the seeds. Based on the statistical analysis of the seed material, it was shown that the characteristics </p> ... Show More
View Publication
Scopus (6)
Crossref (6)
Scopus Clarivate Crossref
Publication Date
Mon Aug 01 2022
Journal Name
Baghdad Science Journal
Lymphocytes Prediction of Homeostasis Model Assessment of Beta-cells Function (HOMA-B) and C-peptide Level during Pregnancy: New Insight into Beta-cells Proliferation and Insulin Sensitivity
...Show More Authors

This work aims to detect the associations of C-peptide and the homeostasis model assessment of beta-cells function (HOMA2-B%) with inflammatory biomarkers in pregnant-women in comparison with non-pregnant women. Sera of 28 normal pregnant women at late pregnancy versus 27 matched age non-pregnant women (control), were used to estimate C-peptide, triiodothyronine (T3), and thyroxin (T4) by Enzyme-linked-immunosorbent assay (ELISA), fasting blood sugar (FBS) by automatic analyzer Biolis 24i, hematology-tests by hematology analyzer and the calculation of HOMA2-B% and homeostasis model assessment of insulin sensitivity (HOMA2-S%) by using C-peptide values instead of insulin. The comparisons, correlations, regression analysis tests were perfo

... Show More
View Publication Preview PDF
Scopus (2)
Crossref (1)
Scopus Clarivate Crossref