Background: 37% phosphoric acid (PA) is the traditional enamel etching technique prior to bracket ‎adhesion, yet it has been implicated in numerous enamel injuries. The purpose of the current study was to create a calcium phosphate (CaP) etching paste in a ‎‎simplified capsule ‎formula that can underpin clinically ‎adequate bracket bond strength ‎without jeopardizing the ‎integrity of enamel upon ‎the debracketing procedure. Materials and Methods: micro-sized hydroxyapatite (HA) powder was mixed with 40% PA solution to prepare ‎experimental acidic CaP paste. Sixty human premolars were ‎assigned into two groups of 30 each. ‎Enamel conditioning was accomplished using 37% PA-gel‎ for control group and CaP paste for e

  In the last decade, the web has rapidly become an attractive platform, and an indispensable part of our lives. Unfortunately, as our dependency on the web increases so programmers focus more on functionality and appearance than security, has resulted in the interest of attackers in exploiting serious security problems that target web applications and web-based information systems e.g. through an SQL injection attack.     SQL injection in simple terms, is the process of passing SQL code into interactive web applications that employ database services such applications accept user input  such as form  and then include this input in database requests, typically SQL statements in a way that was not intende

  The reaction of LAs-Cl8 : [ (2,2- (1-(3,4-bis(carboxylicdichloromethoxy)-5-oxo-2,5dihydrofuran-2-yl)ethane – 1,2-diyl)bis(2,2-dichloroacetic acid)]with sodium azide in ethanol with drops of distilled water has been investigated . The new product L-AZ :(3Z ,5Z,8Z)-2azido-8-[azido(3Z,5Z)-2-azido-2,6-bis(azidocarbonyl)-8,9-dihydro-2H-1,7-dioxa-3,4,5triazonine-9-yl]methyl]-9-[(1-azido-1-hydroxy)methyl]-2H-1,7-dioxa-3,4,5-triazonine – 2,6 – dicarbonylazide was isolated and characterized by elemental analysis (C.H.N) , 1H-NMR , Mass spectrum and Fourier transform infrared spectrophotometer (FT-IR) . The reaction of the L-AZ withM+n: [ ( VO(II) , Cr(III)  ,Mn(II) , Co(II) , Ni(II) , Cu(II) , Zn(II) , Cd(II) and

The Results of Theoretical Studies and Experiment of Advanced Economies , Have Been Proven That Investment Expenditure Is Not The Only Factor And The Main Source of Production Growth, But Efficient Using Of The Fixed Assets Is More Important In This Process, All That Depends On Groups of Factors Called The Non-Investment Economic Growth,  That Are Un-bodied Technical Progress With Organizational Nature.

It's Distinguished Features That it has An Influence on The Production Growth Without Any Large Additional Investment Expenditure Or Any Additional Increment in Inputs And That Can Not Be Reached Without Activating The Factors of Non-Investment Economic Growth, Which is Still Affecting Negatively In T

An acidic environment causes surface changes of resin composites. Filler particlesize and filler distribution also have a direct effect on these surface changes. This invitro study evaluated the influence of Pepsi Cola drink on the surface roughness ofComposan LCM and Composan Ceram over time. Sixteen disc shaped specimens(10mm diameter, 2mm thickness) of each resin composite were fabricated, therebyforming two groups (n= 8). Surface roughness (Ra) was analyzed after 24 hrs beforeexposure to beverage. The specimens were submitted to a five minutes immersion inPepsi Cola three times daily interrupted by immersion in deionized distilled water (37C˚). Surface roughness measurements were done at 10, 30, and 60 days intervals. Datawere

    In this  work , impact strength and the water absorption  ratio of powders of white and brown local chicken eggshell reinforced epoxy with different volume fractions ( 1 , 2 , 3 , 4 and  5 % ) were studied .       The experimental results show that composite filled by ( 1 % Vol . )of white eggshell powder exhibited  maximum  impact  strength and high resistance to tape water , so we choose this volume fraction to use the epoxy composite in coating . Optical microscopic observations are taken to develop a better  understanding of the phenomena taking place in the material system at microscopic level .

Bearing capacity of a concrete pile in fine grained cohesive soils is affected by the degree of saturation of the surrounding soil through the contribution of the matric suction. In addition, the embedded depth and the roughness of the concrete pile surface (expressed as British Pendulum Number BPN) also have their contribution to the shear strength of the concrete pile, consequently its bearing capacity. Herein, relationships among degree of saturation, pile depth, and surface roughness, were proposed as a mathematical model expressed as an equation where the shear strength of a pile can be predicted in terms of degree of saturation, depth, and BPN. Rel

Porcelain is one of the most important ceramic materials with a wide range of traditional and technical applications. Since most mixtures of porcelain have a high sintering temperature, bentonite has been added in this research to improve the characteristics of sintering and burning. The porcelain mixture consisted of the following Iraqi raw materials: 30% wt kaolin, 30 wt% non-plastic clay (grog), 10% wt sodium feldspar, 10 wt% potassium feldspar and 20 wt% flint. After the mechanical mixing process and transfer the powder mixture to the slurry by adding distilled water, then different weight percentage of the sodium bentonite(0, 2.5, 5, 7.5 and 10) wt% was added. The specimens were prepared by using the solid casting m

Carbon fiber reinforced polymers (CFRP) were widely used in strengthening reinforced concrete members
in the last few years, these fibers consist mainly of high strength fibers which increase the member capacity in addition to changing the mode of failure of the reinforced concrete beams. Experimental and theoretical investigations were carried to find the behavior of reinforced concrete beams strengthened by CFRP in shear and bending. The experimental work included testing of 12 beams divided into 4 groups; each group contains 3 beams. The following parameters were taken into consideration: - Concrete crushing strength. - CFRP strengthening location (shear strengthening and both shear and flexure strengthening). Reinforced beams were