The addition of new reactive sites on the surface area of the inert sand, which are represented by layered double hydroxide nanoparticles, is the primary goal of this work, which aims to transform the sand into a reactive material. Cetyltrimethylammonium bromide (CTAB) surfactant is used in the reaction of calcium extracted from solid waste-chicken eggshells with aluminum prepared from the cheapest coagulant-alum. By separating amoxicillin from wastewater, the performance of coated sand named as "sand coated with (Ca/Al-CTAB)-LDH" was evaluated. Measurements demonstrated that pH of 12 from 8, 9, 10, 11, and 12, CTAB dosage of 0.05 g from 0, 0.03, 0.05, and 0.1 g, ratio of Ca/Al of 2 from 1, 2, 3, and 4, and mass of sand of 1 g/50 mL from

Thirty nine (12.8%) isolates of Staphylococcus aureus were isolated from 304 healthy human (Nasal swabs). It was found that percentage of males that have S. aureus is more than female's percentage. These isolates (39) were tested with different tests. Twenty seven isolates (69.23 %) were positive for Staphylococcus protein —A (SPA) ,thirty seven ( 94.8 %) were positive for tube coagulase , thirty five ( 89.7 % ) were positive with clumping factor and thirty two ( 82.05 %) had 13 — hemolytic on blood agar. It was found that 100% of the isolates (39 isolates) were positive with one, two or three tests (tube coagulase, clumping factor and SPA).

Background: This study report the corrosion behavior of commercially pure titanium and Ti-6Al-4V alloy samples without coating and with hydroxyapatite, partial stabilized zirconia and mixture of partial stabilized zirconia and hydroxyapatite coating and comparison between them through electrochemical polarization tests in 37 0 C Hank's solution. Materials and methods: Electrophoretic deposition technique (EPD) was used to achieve the coating from each one of three types of the coating materials (HAP, PSZ and mixture of 50% HAP and 50%PSZ) on Cp Ti and Ti-6Al-4V alloy samples. The electrochemical corrosion test was performed when samples were exposed to Hank's solution prepared in the laboratory and the polarization potential, corrosion rate

The experiment was conducted to evaluate and performance comparison for moldboard and disk plows in central of Iraq in 2011. Three factor were used in this study included Two types of plows included moldboard and disk plows which represented main plot , three forward speeds of the tillage was second factor included 1.85, 3.75 and 5.62 km / h which represented sup plot , and three levels of soil moisture was third factor included 21 , 18 and 14 % to determined data actual plow depth , Practical productivity, Volume of disturbed soil, Field efficiency , Slippage percentage in silt clay loam soil with depth 22 cm were studied in the experiment Split – split plot design under randomized complete block design with three replications using

Background: Polymeric composites have been widely used as dental restorative materials. A fundamental knowledge and understanding of the behavior of these materials in the oral cavity is essential to improve their properties and performance. The goal of this study was to measure water sorption of four composite resins containing different filler and resin matrix contents. Materials and method: Resin composite specimens giomer (Beautifil II) Filtek™ P90, Filtek™ Z350 XT, and Tetric N Ceram were prepared in a cylindrical mould of 3mm thickness and 6mm diameter (n=10) and light cured . All specimens placed in silica-gel desiccators at 37˚C for seven days, a constant weight was obtained. All samples were immersed in deionized distill