In this research, we studied the structural properties of SnO2 films nanostructure which prepared by chemical spray pyrolysis method at room temperature on the rules of glass heated (400oC) with rate of spraying (2.5 ml/ min). The effect of annealing temperaturs (450,500,550,600 and 650oC) for two hours on those properties has been indicated. The results of x-ray diffraction showed that all of the prepared films were polycrystalline with tetragonal type and orientation was (110) for all models before and after annealing, and the annealing led to an increase in the grain size. The full width at half maximum (FWHM) values of the (110) peaks of the films decreased from 1.492o to 1.064o with increasing annealing temperature .The surface morp

The aim of this research is to identify the impact of the effectiveness of digital transformation technology in improving the efficiency of the insurance service in the public insurance companies in Iraq through digital transformation technology in the insurance process "promotion of the insurance product, submission of insurance application, underwriting, settlement of losses" and to achieve this goal a questionnaire was designed A survey distributed in the surveyed community Which represents the decision makers in the researched companies under study, and one of the most important results of the research was the existence of a relationship between digital transformation and improving the efficiency of the insurance process, whether thr

Hollow core photonic bandgap fibers provide a new geometry for the realization and enhancement of many nonlinear optical effects. Such fibers offer novel guidance and dispersion properties that provide an advantage over conventional fibers for various applications. Dispersion, which expresses the variation with wavelength of the guided-mode group velocity, is one of the most important properties of optical fibers. Photonic crystal fibers (PCFs) offer much larger flexibility than conventional fibers with respect to tailoring of the dispersion curve. This is partly due to the large refractive-index contrast available in the silica/air microstructures, and partly due to the possibility of making complex refractive-index structure over the fibe

Polyaniline organic Semiconductor polymer thin films have been prepared by oxidative polymerization at room temperature, this polymer was deposited on glass substrate with thickness 900nm, FTIR spectra was tested , the structural,optical and electrical properties were studied through XRD ,UV-Vis ,IR measurements ,the results was appeared that polymer thin film sensing to NH3 gas.

The rate of gas induction was measured in gas-inducing type mechanically agitated contactors provided with two impellers. A reactor of 0.5 m i.d. was used with a working capacity of 60 liters of liquid. Tap water was used as the liquid phase, and air was used as the gas phase. The bioreactor mixing system consists of two equal diameter stirrers; the top impeller is shrouded-disk/curved-blade turbine with six evacuated bending blades, while the bottom impeller was disk turbine. The impeller speed was varied in the range of 50 to 800 rpm. The ratio of impeller diameter to tank diameter (D/T) and the submergence (S) of upper impeller from the top were varied. The effects of clearance of lower impeller from the tank bottom (C₂) an

In this work, polyvinylpyrrolidone (PVP), multi-walled carbon nanotubes (MWCNTs) nanocomposite was prepared and hybridized with Graphene (Gr) by the solution casting method.  The morphological and electrical properties were investigated by field effect scanning electron microscopy (FESEM) images, portraying a uniform dispersion of graphene within the PVP-MWCNT nanocomposite. The AC conductivity increased from (1.45552) to (2.34812) (Ω cm)^-1 with the use of nanocomposite. The increasing continues for the AC conductivity after hybridized with graphene up to (7.20641) (Ω cm)^-1. In addition, the performances of the prepared samples for gas sensor application have been investigated.