Zinc oxide (ZnO) transparent thin films with different oxygen flow rates (0.5, 1.0, and 1.5)Litter/min. were prepared by thermal evaporation technique on glass substrate at a temperature of 200℃ with rate (10±2)nm sec-1,  The crystallinity and structure of these films were analyzed  by X-ray diffraction (XRD). It exhibits a polycrystalline hexagonal wurtzite structure and the preferred orientation along (002) plane. The Optical properties of ZnO were determined through the optical transmission method using ulta violet–Visible spectrophotometer with in wave length (300-1100)nm. The optical transmittance of the ZnO films increases from 75% to 85% with increase flow rate of O2, and the optical band gap of ZnO

A precise evaluation of caries excavation endpoint is essential in clinical and laboratory investigations. Caries invasion differentiates dentin into structurally altered layers. This study assessed these changes using Raman spectroscopy and Vickers microhardness. Ten permanent molars with occlusal and proximal carious lesions were assessed and compared at 130 points utilizing four Raman spectroscopic peaks: phosphate v1 at 960 cm−1, amide I (1650 cm−1), amide III (1235 cm−1) and the C-H bond of the pyrrolidine ring (1450 cm−1). The phosphate-to-amide I peak ratio and collagen integrity peak ratio (amide III: C-H bond) of carious zones were calculated and compared in both lesions. The former ratio was correlated to 130 Vicke

   For extraction chloro anion complexes of Cd2+ and Hg2+ used many organic agents as extractant according to liquid ion exchange method such as α-Naphthyl amine (α-NA), 4-Amino benzoic acid (4-ABA), 2-[(4-Carboxy methyl phenyl) azo]-4,5-diphenyl imidazole (4CMePADPI) and Cryptand (C222). This study includes definition hydrochloric acid concentration in aqueous phase and shaking with organic phase necessary for extraction as well as shaking time, organic solvent effect, interferences and alkaline salt effect. Thermodynamic showed the ion exchange reaction was exothermic for α-NA, C222 and endothermic for 4-ABA, 4-CMePADPI for extraction CdCl4=, but for extraction HgCl4= was exothermic with 4-ABA, 4CMePADPI and C222 but

Two simple, rapid, and useful spectrophotometric methods were suggest or the determination of sulphadimidine sodium (SDMS) with and without using cloud point extraction technique in pure form and pharmaceutical preparation. The first  method was based on  diazotization of the Sulphdimidine Sodium drug by sodium nitrite at 5 ºC, followed by coupling with α –Naphthol in basic medium to form an orange colored product . The product was stabilized and its absorption was measured at 473 nm. Beer’s law was obeyed in the concentration range of (1-12) μg∙ml^-1. Sandell’s sensitivity was 0.03012 μg∙cm^-1, the detection limit was 0.0277 μg∙ml^-1, and the limit of Quantitation was 0.03605μg

NiO nanoparticle synthesis by chemical method and characterized by XRD with crystal size 11.72
nm and grain size 13 nm from FESEM image also NiO micro used ,two NiO as an additive to evaluate the
possibility of producing photodegradable polymers, the practical application of solid-phase photocatalytic
degradation of polyvinyl chloride (PVC- NiO composite films) was investigated. PVC has a negative impact
on the environment since its polymer degrades slowly, yet it has a wide range of industrial applications and
the amount used shows no evidence of diminishing use. Thus, a synthesis of modified PVC- NiO micro and
nano has been studied with 0, 50, 100, 150, 200, 250, and 300 (hours) as irradiation time a

The physicochemical behaviour of dodecyltrimethylammonium bromide (DTAB) in water and ethanol-water mixture in the presence and absence of ZnSO₄ were studied by measuring the conductivity at 298.15 K. The pre-micellar (S₁) and post-micellar slopes (S₂) were obtained and calculated the degree of dissociation (α) and the critical micelle concentration (cmc). With an increase in ethanol content, the cmc and α of DTAB increased whereas, in the presence of ZnSO₄, the cmc and α decreased. By using cmc and α, thermodynamic properties as the standard free energy of micellization ( ) were evaluated. With an increase in ethanol content, the negative values of  are decreased indicating less spont

The current work is concerned with preparing cobalt manganese ferrite (Co1-xMnxFe2O4) with different concentrations of cobalt and manganese (x=0.2, 0.4, and 0.6) and decorating it with polyaniline (PAni) for use in supercapacitive applications. The results of the X-ray diffraction (XRD) manifested a broad peak of PAni and a cubic structure of cobalt manganese ferrite having crystal size between 60 nm and 138 nm, which decreases with increasing concentration of Mn. The field emission scanning electron microscopy (FESEM) images evidenced that the PAni has nanofiber (NF) structures, according to the method of preparation, where the hydrothermal method was used. The magnetic properties of the prepared ferrite, as well as the prepared PAni/Co1-x